Control of Metal-Ion Composition in the Synthesis of Ternary II-II′-VI Nanoparticles by Using a Mixed-Metal Cluster Precursor Approach

The ternary molecular nanoclusters [Zn(x)Cd(10-x)Se4(SePh)12(PnPr3)4] (x = 1.8, 1 a; x = 2.6, 1 b) were employed as single-source precursors for the synthesis of high-quality hexagonal Zn(x)Cd(1-x)Se nanocrystals. The tellurium clusters [Zn(x)Cd(10-x)Te4(TePh)12(PnPr3)4] (x = 1.8, 2 a; x = 2.6, 2 b) are equally convenient precursors for the synthesis cubic Zn(x)Cd(1-x)E nanoparticles. The thermolysis of the cluster molecules in hexadecylamine provides an efficient system in which the inherent metal-ion stoichiometry of the clusters is retained in the nanocrystalline products, whilst also affording control of particle size within the 2-5 nm range. In all cases, the nanoparticles are monodisperse, and luminescence spectra exhibit emission energies close to the absorption edge. Analysis of the optical spectra and X-ray diffraction patterns of these materials indicates a metal-ion concentration gradient within the structures of the nanocrystals, with Zn(II) ions predominantly located near the surface of the particles.

Sequential synthesis of type II colloidal CdTe/CdSe core-shell nanocrystals

Colloidal type II CdTe/CdSe nanocrystals were synthesized by sequential addition of a tri-n-octylphosphine telluride (TOPTe)/TOP solution and several shell-precursor solutions to a CdO/TOP solution; the shell-precursor solutions consisted of CdO and TOPSe in TOP. For the growth of the CdTe core, the TOPTe/TOP solution was swiftly added to the CdO/TOP solution at a higher temperature (300 degrees C) than the growth temperature (250 degrees C). For the growth of the CdSe shell, in contrast, the CdO/TOPSe/TOP solution was slowly added to the CdTe/TOP solution at a lower temperature than the growth temperature (200-240 degrees C). The temporal evolution of the optical properties of the growing core-shell nanocrystals was monitored in detail. During the growth of the CdSe shell, the core-shell nanocrystals exhibited interesting changes in photoluminescence (PL) properties. The highest PL efficiency (approximately 38 %) was detected from core-shell nanocrystals with a CdSe shell thickness of 0.4-0.5 nm (indicated by TEM); the formation of the first monolayer is proposed. Our synthetic approach is well suited to a practical realization of engineering materials with bandgaps in the near-IR and IR spectral ranges.