Isothermal crystallization and melting behavior of 2-methyl-1,3-propanediol substituted sulfonated poly(ethylene terephthalate) copolyesters

Synthesis and Structural Characterization of Sequential Structure and Crystallization Properties for Hydrophilic Modified Polyester

The hydrophilic copolyester polyethylene terephthalate (PET) (ENCDP-X) was successfully synthesized by chemical modification consisting of copolymerization and blending and the comonomers, including sodium isophthalate-5-sulfonate (SIPE), polyethylene glycol (PEG), 2,2-dimethyl-1,3-propanediol (NPG) and matting agent TiO₂ with different content. Moreover, the structural characterization of sequential structure, crystallization and thermal properties were studied. The results showed that the comonomers were successfully embedded in the copolyester, the actual molar ratio in the copolyester was consistent with the relative feed ratio and the degree of randomness was calculated to be 0.99, showing that the random copolymers synthesized during the melt polycondensation process and the chemical structure was roughly consistent with the expected molecular chain sequence structure. The thermal parameters of the modified copolyester, containing the glass transition temperature (T_g), melting point (T_m), crystallinity (X_c) and thermal degradation temperature, were decreased, and the cold crystallization temperature (T_c) was increased. In addition, with the increasing of the TiO₂ content, it improves the thermal performance of the copolyester and it is beneficial to processing and application. The above conclusion is further verified by non-isothermal kinetic analysis. In addition, the copolyester exhibited the better hydrophilicity than pure PET.

The effect of crystallization properties influenced by 2-methyl-1,3–propanediol units on the optical properties of modified poly(ethylene terephthalate)

In this study, the preparation and properties of poly(ethylene terephthalate-co-2-methyl-1,3-propanediol) copolyester (PEMT) were reported. The PEMT crystallization properties, optical properties, thermal properties, rheological properties, and other properties were characterized by nuclear magnetic resonance (1H NMR), differential scanning calorimetry, thermo gravimetric analysis, ultraviolet visible near-infrared (UV-VIS-NIR) spectroscopy, polarizing microscope crystal culture, X-ray diffraction (XRD), and rheometer. It was proved that the crystallization abilities and crystallization rate of PEMT copolyesters were significantly affected by the content of 2-methyl-1,3-propanediol (MPO) units; the copolyester becomes amorphous when the content of MPO units exceeded 20 mol%. According to the XRD data, the diffraction peaks of PEMT remained unchanged compared with those of poly(ethylene terephthalate). The transmittance of copolyesters displayed a tendency of increasing at first and then declining with the increase in MPO. In addition to the crystallization properties, the transmittance of copolyesters was also affected by the extent of yellowing. When the MPO addition was less than 20 mol%, PEMT can maintain good thermal decomposition performance and processability.

Synthesis and structure analysis of polyesteramides modified with bio-based diaminopentane hexanedioic salt

Two series of bio-based diaminopentane hexanedioic salt (DHS) modified polyesteramides were successfully synthesized by two different synthesis processes in which DHS reacted with bis-hydroxyethyl terephthalate (BHET) and low molecular weight polyester (LPET), respectively. The intrinsic viscosities of the polyesteramides ranged from 0.62 dl/g to 0.78 dl/g, which correlated greatly with the requirements of subsequent processing such as spinning. The results of the heteronuclear multiple bond correlation (HMBC) indicated that the diaminopentane segment was directly connected with the purified terephthalic acid (PTA) segment. The presence of ester and amide group characteristic peaks in the Fourier transform-infrared (FT-IR) spectroscopy confirmed that the final resultant products were polyesteramides. The results of elemental analysis showed that the ratio of actual nitrogen content to theoretical nitrogen content of two series of polyesteramides was 76%~90%, and the actual nitrogen content in both series was proportional to the addition of DHS.