Dissolution rate studies of compression-molded units made from hydroxypropyl cellulose films

Enhanced fixation of implants by bone ingrowth to titanium fiber mesh: Effect of incorporation of hydroxyapatite powder

Tight fixation between bone and implant materials is of great importance for a successful outcome of procedures such as total knee arthroplasty (TKA) and total hip arthroplasty (THA). Titanium fiber mesh is an attractive structure for the establishment of tight fixation between bone and implant by bone ingrowth into the spaces among the fibers. Enhancement of bone ingrowth is desired not only for tight fixation but also for a fast recovery. Our hypothesis is that just the presence of hydroxyapatite (HA) particles ensures improved bone ingrowth, and that long-term stability can be obtained by mechanical anchoring of bone in the spaces among titanium fibers. In this study, we examine our hypothesis by in vivo experiment using dog femur. HA particles were incorporated in titanium fiber mesh coated on titanium alloy rod by dipping in a slurry of HA with hydroxy-propyl-cellulose in an ethanol solution. Specimens were implanted for 3, 5, and 8 weeks, and were then compared with the results from specimens without the use of HA. Bonding strength was evaluated by push-out test, and histomorphometric measurements were made with analysis software to calculate the average value of bone ingrowth. A significantly higher bonding strength was observed for the specimens with HA-incorporated implant at 3 and 5 weeks, and larger bone ingrowth deep inside the titanium fiber mesh was measured at 3 weeks. Our proposed method has the additional advantage of not requiring a high temperature that may result in changes in characters of HA powder such as phase transition, grain growth, and decomposition. Moreover, this technique of HA powder incorporation without high-temperature treatment allows the use of several types of metallic fiber mesh, as well as the application to fiber mesh made of organic polymers. We conclude that this simple modification of titanium fiber mesh with HA powder can improve the fixation of implant to bone in the initial stage after operation.

Development of polymer film dosage forms of lidocaine for buccal administration: II. Comparison of preparation methods

In previous studies, we prepared film dosage forms of lidocaine (LC) with hydroxypropylcellulose (HPC) as a film base using the solvent evaporation (SE) method. However, from the viewpoint of environmental issues, a reduction in organic solvent use in pharmaceutical and other industries is required. In this study, we prepared the LC films by direct compression of the physical mixture (DCPM method) and direct compression of the spray dried powder (DCSD method). Magnesium stearate, which was required as a lubricant for direct compression, showed no effect on the LC release rate. The LC release rate (%/h) was independent of the compression pressure, but a higher pressure was preferable to easily remove the film from the punches. An increase in the film weight decreased the LC release rate expressed in %/h, whereas no significant effect of film weight was observed on the LC release rate from unit surface area expressed in mg/h/cm(2). The LC release rate (%/h) was independent of the LC content, suggesting that the LC release rate (mg/h) can be quantitatively controlled by changing the LC content in the formulation. The LC release rate and penetration rate were affected by the preparation method; that is, DCPM method < DCSD method < SE method. The LC penetration rates through excised hamster oral mucosa were linearly correlated to the release rate of un-ionized LC, which was estimated by the LC release rate multiplied by the un-ionized fraction of LC for the HPC film dosage form.