?-Irradiation of ultrahigh-molecular-weight polyethylene: Electron paramagnetic resonance and nuclear magnetic resonance spectroscopy and imaging studies of the mechanism of subsurface oxidation

Radical Composition and Radical Reaction Kinetics in the Probe-Irradiated XLPE Samples as a Potential Source of Information on Their Aging Degree

Polyethylene is a model polyolefin, and a widely used material for the manufacture of many products, including cable sheaths. Understanding degradation mechanisms at the atomic scale leading to oxidation during aging is crucial for many long-term applications. The concentrations of radicals derived from oxidation and chain scission during radio-oxidation, as well as their ratio, are important parameters controlling the predominance of chain scission or crosslinking of the polymer. In this work, we propose a cryogenic EPR technique for measuring oxidation- and fragmentation-derived radicals as a less-destructive method for the evaluation of cable insulation aging and performance capability. We investigate the effect of the low-dose and high-dose radiation aging on the formation of free radicals in the polymer matrix that are both unprotected and protected by antioxidants. The stability of radicals after aging is a determinant of macroscopic processes and structural changes during aging. Under the conditions of the higher dose rate, the peroxy radical buildup is lower per dose. Peroxy radical buildup is followed by decay during aging, in accordance with POOH content. Our results allow the prediction of the capability of the antioxidant to protect the XLPE material in the function of dose and time.

Short data-acquisition times improve projection images of lung tissue

MR images of laboratory rat lungs that resolve the thin membranes that separate lung lobes are presented. It appears that the capabilities of in vivo small-animal pulmonary MRI may rival those of in vivo small-animal X-ray CT. Free induction decay (FID)-projection imaging was employed with particular attention to the choice of acquisition time. For a given nominal resolution, one obtains optimal point discrimination when the acquisition time T(acq) normalized by the signal decay time constant T(2)(*) is approximately 0.8-0.9, although a better signal-to-noise ratio (SNR) is obtained when this quotient is 1.6. Currently available equipment should be able to even exceed the results presented herein.

The effect of alpha-tocopherol on the oxidation and free radical decay in irradiated UHMWPE

We developed a radiation cross-linked ultra-high molecular weight polyethylene (UHMWPE) stabilized with alpha-tocopherol (Vitamin E) as a bearing material in total joint replacements. The stabilizing effect of alpha-tocopherol on free radical reactions in UHMWPE is not well understood. We investigated the effect of alpha-tocopherol on the oxidation and transformation of residual free radicals during real-time aging of alpha-tocopherol-doped, irradiated UHMWPE (alphaTPE) and irradiated UHMWPE (control). Samples were aged at 22 degrees C (room temperature) in air, at 40 degrees C in air and at 40 degrees C in water for 7 months. During the first month, alphaTPE showed some oxidation at the surface, which stayed constant thereafter. Control exhibited substantial oxidation in the subsurface region, which increased with time. The alkyl/allyl free radicals transformed to oxygen centered ones in both materials; this transformation occurred faster in alpha-TPE. In summary, the real-time oxidation behavior of alpha-TPE was consistent with that observed using accelerated aging methods. This new UHMWPE is oxidation resistant and is expected to maintain its properties in the long term.