Antimicrobial effect of bioceramic cements on multispecies microcosm biofilm: a confocal laser microscopy study

Sol-gel-derived calcium silicate cement incorporating collagen and mesoporous bioglass nanoparticles for dental pulp therapy

OBJECTIVE

Calcium silicate cements (CSCs) are often used in endodontics despite some limitations related to their physical properties and antibacterial efficacy. This study aimed to develop and demonstrate the viability of a series of CSCs that were produced by sol-gel method and further modified with mesoporous bioactive glass nanoparticles (MBGNs) and collagen, for endodontic therapy.

METHODS

Calcium silicate (CS) particles and MBGNs were synthesized by the sol-gel method, and their elemental, molecular, and physical microstructure was characterized. Three CSCs were developed by mixing the CS with distilled water (CS+H2O), 10 mg/mL collagen solution (CS+colH2O), and MBGNs (10 %) (CSmbgn+colH2O). The mixing (MT) and setting (ST) times of the CSCs were determined, while the setting reaction was monitored in real-time. Antibacterial efficacy against Enterococcus faecalis (E. faecalis) and regenerative potential on dental pulp stem cells (DPSCs) were also analyzed.

RESULTS

The CS+H2O displayed a ST comparable to commercial products, while CSmbgn+colH2O achieved the longest MT of 68 s and the shortest ST of 8 min. All the experimental CSCs inhibited the growth of E. faecalis. Additionally, compared to the control group, CSCs supported cell proliferation and spreading and mineralized matrix production, regardless of their composition.

SIGNIFICANCE

Tested CSCs presented potential as candidates for pulp therapy procedures. Future research should investigate the pulp regeneration mechanisms alongside rigorous antibacterial evaluations, preferably with multi-organism biofilms, executed over extended periods.

Antibacterial, biocompatible, and mineralization-inducing properties of calcium silicate-based cements

BACKGROUND

Different pulp capping materials have different origins and compositions, require different preparations, and may vary in their bioactive properties.

AIM

The purpose of this study was to evaluate the antibacterial activity, biocompatibility, and mineralization-inducing potential of calcium silicate-based pulp capping materials.

DESIGN

Six contemporary calcium silicate-based cements, ProRoot MTA, MTA Angelus, Biodentine, EndoSequence, NeoMTA 2, and NeoPutty, were evaluated. The antibacterial effects of these materials against Streptococcus mutans UA159 and Enterococcus faecalis ATCC 29212 were determined by the agar diffusion assay and the direct culture test. The biocompatibility and mineralization-inducing potential of these materials in preodontoblastic 17IIA11 cells were evaluated by the MTT assay and by Alizarin Red S staining, respectively.

RESULTS AND CONCLUSION

In agar diffusion test, only Biodentine showed distinct antibacterial effects against S. mutans. All the tested materials, however, showed antibacterial effects against S. mutans and E. faecalis in the direct culture test, with Biodentine showing the strongest growth inhibition against both S. mutans and E. faecalis. All the tested materials showed acceptable biocompatibility and mineralization-supporting potential in our experimental conditions. In summary, ProRoot MTA, MTA Angelus, Biodentine, EndoSequence, NeoMTA 2, and NeoPutty demonstrated acceptable in vitro antimicrobial, biocompatible, and mineralization-supporting properties.

The Effect of Chitosan Incorporation on Physico-Mechanical and Biological Characteristics of a Calcium Silicate Filling Material

OBJECTIVES

A tricalcium silicate-based cement, Biodentine™, has displayed antibiofilm activity when mixed with chitosan powder. This study aimed to assess the effect of chitosan incorporation on the physico-mechanical and biological properties of Biodentine™.

METHODS

In this study, medium molecular weight chitosan powder was incorporated into Biodentine™ in varying proportions (2.5 wt%, 5 wt%, 10 wt%, and 20 wt%). The setting time was determined using a Vicat apparatus, solubility was assessed by calculating weight variation after water immersion, radiopacity was evaluated and expressed in millimeters of aluminum, the compressive strength was evaluated using an Instron testing machine, and the microhardness was measured with a Vickers microhardness tester. In addition, surface topography of specimens was analyzed using scanning electron microscopy, and the effect of chitosan on the viability of human embryonic kidney (HEK 293) cells was measured by a colorimetric MTT assay.

RESULTS

Incorporation of 2.5 wt% and 5 wt% chitosan powder delivered an advantage by speeding up the setting time of Biodentine material. However, the incorporation of chitosan compromised all other material properties and the crystalline structure in a dose-dependent manner. The chitosan-modified material also showed significant decreases in the proliferation of the HEK 293 cells, signifying decreased biocompatibility.

SIGNIFICANCE

Chitosan incorporation into calcium silicate materials adversely affects the physical and biological properties of the material. Despite the increased antimicrobial activity of the modified material, the diminution in these properties is likely to reduce its clinical value.

An In Vitro Study: Does Adding Iodine Potassium Iodide and Cetrimide to Calcium Hydroxide Paste Enhance Its Antimicrobial Effect Against Oral Biofilms?

Objectives This study aimed to evaluate the antibiofilm effect of calcium hydroxide (CH), 0.5% iodine potassium iodide (IKI), and 0.5% cetrimide (CTR), alone and in combinations on one-week and three-week-old biofilms. Materials and methods Gingival plaque was collected, and biofilms were grown in vitro anaerobically. Biofilms were exposed to each of the three medicaments and their combinations for one day, one week, and two weeks. Proportions of dead and live bacteria in the biofilms were evaluated. Results The killing of bacteria by different medicaments in the three-week-old biofilm was lower than in the one-week-old biofilm (p<0.05). The efficacy of IKI and CTR in killing bacteria was weaker than that of CH, but the highest efficacy in killing was achieved when all three were combined (p<0.05). There was no significant difference in the antibiofilm effect between a day's exposure to the mixture of the three medicaments and one or two weeks of treatment with CH alone (p>0.05). Conclusions Three-week-old biofilms are more resistant to medicaments than one-week-old biofilms. Combining IKI and CTR with CH resulted in a stronger antibiofilm effect than using CH alone. Mixing the three medicaments may enable obtaining the desired clinical effect in a shorter exposure time.

Antibacterial Activity of Root Repair Cements in Contact with Dentin-An Ex Vivo Study

This study assessed the antibacterial characteristics of the dentin/material interface and dentin surfaces exposed to experimental hydraulic calcium silicate cement (HCSC) with or without bioactive glass (BG) replacement (20% or 40%) or mixed with a silver nanoparticle (SNP) solution (1 or 2 mg/mL), and Biodentine, TotalFill BC RRM putty and Intermediate Restorative Material (IRM). Human root dentin segments with test materials were assessed at 1 or 28 days. In one series, the specimens were split to expose the dentin and material surfaces. A 24 h direct contact test was conducted against three-day established Enterococcus faecalis and Pseudomonas aeruginosa monospecies biofilms. In another series, the dentin/material interface of intact specimens was exposed to biofilm membranes for 3 days and the antibacterial activity was assessed via confocal microscopy. The interface was additionally characterised. All one-day material and dentin surfaces were antibacterial. Dentin surfaces exposed to HCSC with 40% BG-replacement, Biodentine and IRM had decreased antibacterial properties compared to those of the other cements. The HCSC mixed with a 2 mg/mL SNP solution had the highest antimicrobial effect in the confocal assay. The interfacial characteristics of HCSCs were similar. The test materials conferred antibacterial activity onto the adjacent dentin. The BG reduced the antibacterial effect of dentin exposed to HCSC; a 2 mg/mL SNP solution increased the antibacterial potential for longer interaction periods (three-day exposure).

Sol-gel synthesis of lithium doped mesoporous bioactive glass nanoparticles and tricalcium silicate for restorative dentistry: Comparative investigation of physico-chemical structure, antibacterial susceptibility and biocompatibility

Introduction: The sol-gel method for production of mesoporous bioactive glass nanoparticles (MBGNs) has been adapted to synthesize tricalcium silicate (TCS) particles which, when formulated with other additives, form the gold standard for dentine-pulp complex regeneration. Comparison of TCS and MBGNs obtained by sol-gel method is critical considering the results of the first ever clinical trials of sol-gel BAG as pulpotomy materials in children. Moreover, although lithium (Li) based glass ceramics have been long used as dental prostheses materials, doping of Li ion into MBGNs for targeted dental applications is yet to be investigated. The fact that lithium chloride benefits pulp regeneration in vitro also makes this a worthwhile undertaking. Therefore, this study aimed to synthesize TCS and MBGNs doped with Li by sol-gel method, and perform comparative characterizations of the obtained particles.

Methods: TCS particles and MBGNs containing 0%, 5%, 10% and 20% Li were synthesized and particle morphology and chemical structure determined. Powder concentrations of 15mg/10 mL were incubated in artificial saliva (AS), Hank’s balanced saline solution (HBSS) and simulated body fluid (SBF), at 37°C for 28 days and pH evolution and apatite formation, monitored. Bactericidal effects against S. aureus and E. coli, as well as possible cytotoxicity against MG63 cells were also evaluated through turbidity measurements.

Results: MBGNs were confirmed to be mesoporous spheres ranging in size from 123 nm to 194 nm, while TCS formed irregular nano-structured agglomerates whose size was generally larger and variable. From ICP-OES data, extremely low Li ion incorporation into MBGNs was detected. All particles had an alkalinizing effect on all immersion media, but TCS elevated pH the most. SBF resulted in apatite formation for all particle types as early as 3 days, but TCS appears to be the only particle to form apatite in AS at a similar period. Although all particles had an effect on both bacteria, this was pronounced for undoped MBGNs. Whereas all particles are biocompatible, MBGNs showed better antimicrobial properties while TCS particles were associated with greater bioactivity.

Conclusion: Synergizing these effects in dental biomaterials may be a worthwhile undertaking and realistic data on bioactive compounds targeting dental application may be obtained by varying the immersion media.

Comparative Evaluation of Physicomechanical Properties and Antimicrobial Activity of White Portland Micro- and Nanoparticulate Peruvian Cement, Mineral Trioxide Aggregate, and Neomineral Trioxide Aggregate

AIM

To compare the surface microhardness, compressive strength, and antimicrobial activity of white Portland nanoparticle and microparticle Peruvian cement, mineral trioxide aggregate (MTA), and neomineral trioxide aggregate (NeoMTA) at 24 hours and 28 days.

MATERIALS AND METHODS

Twenty specimens were prepared for each group of cement microparticulated powder (PCm), nanoparticulated cement (PCn), MTA, and NeoMTA to be evaluated at two different times, 24 hours and 28 days for the surface microhardness test and compressive strength. For the antimicrobial activity tests, another 20 specimens were prepared for each group of cement where they were subdivided into two subgroups according to the different periods at 24 hours and 48 hours. For the surface microhardness and compressive strength, the specimens, and the cement groups were mixed according to the manufacturer's instructions and transferred to a cylindrical polyethylene mold of 6-mm diameter and 4-mm height. The compressive strength test was conducted using a universal testing machine. Moreover, the agar diffusion technique was to evaluate the antibacterial and antifungal activity of the American Type Culture Collection (ATCC) Enterococcus faecalis and Candida albicans. Finally, the data were statistically analyzed.

RESULTS

The highest microhardness values for the 24-hour subgroup were recorded for NeoMTA cement (16.99 ± 2.02), followed by MTA, PCn, and PCm, respectively. As for the 28-day subgroup, PCn cement (41.64 ± 3.20) presented the highest microhardness, followed by NeoMTA, PCm, and MTA, respectively, with statistically significant differences among them. The compressive strength of both subgroups 24 hours and 28 days exhibited the highest mean for PCn (41.3 ± 4.29, 65.74 ± 3.06), followed by PCm, NeoMTA, and the lowest value for MTA cement. Finally, for the antimicrobial activity, the highest mean for the 24-hours and 48-hours subgroup was recorded for NeoMTA cement (17.6 ± 1.26, 17.8 ± 1.44), followed by PCn, PCm, and the lowest value for MTA, with significant differences between them.

CLINICAL SIGNIFICANCE

It is highly recommended, Portland cement (PC) as a viable substitute since it has very similar components and properties, but at a lower cost.

CONCLUSION

Regardless of the evaluation time, PCn produced higher surface microhardness and compressive strength; however, NeoMTA showed higher antimicrobial activity.

Biological and chemical properties of five mineral oxides and of mineral trioxide aggregate repair high plasticity: an in vitro study

Calcium silicate-based cements have diverse applications in endodontics. This study aimed to evaluate the antibiofilm action, biocompatibility, morphological structure, chemical composition and radiopacity of Five Mineral Oxides (5MO), Mineral Trioxide Aggregate Repair High Plasticity (MTA Repair HP), and Mineral Trioxide Aggregate (MTA) cements. MTT analysis was used to test the antibiofilm action of these cements against five anaerobic microorganisms, and test their biocompatibility with mouse macrophage (RAW 264.7) and osteoblasts (MG-63) cultures. Their morphological structure and chemical composition were evaluated by scanning electron microscopy (SEM) coupled to energy dispersion X-ray spectroscopy (EDX), and the phase analysis was performed by X-ray diffraction (XRD). Conventional radiography was used to assess the radiopacity of the cements. 5MO, MTA Repair HP and MTA were effective against Porphyromonas gingivalis, Parvimonas micra, Fusobacterium nucleatum and Prevotella intermedia, they were biocompatible with macrophages and osteoblasts after 5 min of contact, and they had adequate radiopacity to be used clinically. Bismuth oxide (Bi2O3) is used as a radiopacifier in MTA and 5MO, and calcium tungstate, in MTA Repair HP. Titanium dioxide (TiO₂) (ANATASE) is responsible for the antimicrobial action and biocompatibility of 5MO.

Current status on antimicrobial activity of a tricalcium silicate cement

Biodentine (BD) is a bioactive material with many indications in endodontic therapy. The purpose of this study was to compile and review the outcomes of in vitro and in vivo studies of BD in terms of antimicrobial effectiveness. An electronic search was carried out in PubMed, from January 2009-April 2021 using the keywords: (Biodentine or dentine substitute or "Ca₃SiO₅" or tricalcium silicate cement or bioceramic cement) and (antimicrobial activity or antimicrobial effect or antimicrobial effectiveness or antibacterial activity or antibacterial effect or antibacterial effectiveness or antibiofilm activity or antibiofilm effectiveness). Two independent reviewers evaluated the studies for eligibility. All studies that did not include BD or its antimicrobial properties, as well as abstracts not written in English, were excluded. This review identified the need to develop standardized methods to evaluate antimicrobial activity in vitro. Most of the studies were against planktonic bacteria and gave conflicting results. Studies ex vivo and in vivo against biofilm are required to elucidate the antimicrobial activity of BD.

Antimicrobial and Antibiofilm Properties of Bioceramic Materials in Endodontics

Microbes are prevalent in the root canals of necrotic teeth, and they are the cause of primary and post-treatment apical periodontitis. Bacteria can dwell within the infected root canal system as surface-adherent biofilm structures, which exhibit high resistance to antimicrobial agents. Bioceramic materials, with their biocompatible nature and excellent physico-chemical properties, have been widely used in dental applications, including endodontics. This review focuses on the application of bioceramic technology in endodontic disinfection and the antibiofilm effects of endodontic bioceramic materials. Different bioceramic materials have shown different levels of antibiofilm effects. New supplements have emerged to potentially enhance the antibiofilm properties of bioceramics aiming to achieve the goal of microbial elimination in the root canal system.

Marginal gaps and internal voids after root-end filling using three calcium silicate-based materials: A Micro-CT analysis

This study evaluated the 3D quality of root-end filling, assessing the presence (volume and percentage) of marginal gaps and internal voids formed after retro-filling with three calcium silicate-based materials: MTA Angelus (Angelus Soluçoes Odontologicas, Londrina, PR, Brazil), Biodentine (Septodont Ltd., Saint Maur-des-Faussés, France) and Neo MTA Plus (Avalon Biomed Inc., Bradenton, Florida, US). Thirty human, extracted, single rooted teeth were used. Orthograde root canal treatment, root resection (3mm shorter than the apex) and retrograde cavity preparation with ultrasonic tips were performed. Teeth were divided into 3 groups (n =10 each) following a stratified randomization according to the initial volume of the root-end cavity. After retrofilling, samples were stored for 7 days. Then, two rounds of micro-CT scans were performed: soon after root-end preparation (with the cavity still empty) and 7 days after root-end filling. Marginal gaps, internal voids volume (mm3 and %), as well as, the overall defects (sum of gaps and voids) were evaluated. Statistics compared the three groups in relation to those defects. There was not statistical difference between groups regarding the marginal gaps (P≥ 0.05), the internal voids (P≥ 0.05), and the overall defects (P≥ 0.05). Median (mm3) and % of overall air-entrapment defects (gaps and/or voids) was: 0.004mm3 and 1.749% for MTA Angelus, 0.018mm3 and 6.660% for Biodentine, and 0.012mm3 and 4.079% for Neo MTA Plus. All materials had gaps and/or voids. No differences were found between MTA Angelus, Biodentine and Neo MTA Plus.

Chitosan Enhances the Anti-Biofilm Activity of Biodentine against an Interkingdom Biofilm Model

Endodontic infection is a biofilm disease that is difficult to irradicate with current treatment protocols, and as such, persistent micro-organisms may lead to ongoing or recurrent disease. The potential for the use of enhanced filling materials to modify biofilm regrowth is a promising strategy. This current study aimed to evaluate the anti-biofilm efficacy of calcium silicate cements modified with chitosan. The development of mono-species and multi-species biofilms on ProRoot MTA, Biodentine and bovine dentine discs were explored using quantitative microbiology analysis. The effect on regrowth of biofilms was assessed following the addition of chitosan to each cement. In comparison to a dentine substrate, both materials did not show the ability to inhibit biofilm regrowth. Biodentine incorporated with chitosan displayed a dose-dependent reduction in multi-species biofilm regrowth, unlike MTA. Notably, interkingdom biofilms were shown to enhance bacterial tolerance in the presence of chitosan. This study demonstrates the potential to enhance the antimicrobial properties of Biodentine. The findings highlight the need for appropriate model systems when exploring antimicrobial properties of materials in vitro so that interspecies and interkingdom interactions that modify tolerance are not overlooked while still supporting the development of innovative materials.

Antibiofilm potential over time of a tricalcium silicate material and its association with sodium diclofenac

OBJECTIVES

The objectives of this study are to investigate, over time, the antimicrobial activity against polymicrobial biofilms and ability to inhibit biofilm formation, of Biodentine (BD) alone and with 5% and 10% sodium diclofenac (DC).

MATERIAL AND METHODS

The antimicrobial activity of BD alone and modified with 5% and 10% DC against polymicrobial biofilm growth in dentin was determined by a modified direct contact test. The study groups were (1) BD; (2) BD + 5% DC; and (3) BD + 10% DC. The viability of microorganisms after 1 and 4 weeks was quantified by means of an ATP assay and flow cytometry. The antibiofilm efficacy of the materials, preventing polymicrobial biofilm formation over time, was assessed by confocal laser scanning microscopy (CLSM).

RESULTS

The results obtained with both the ATP test and flow cytometry showed that BD alone and with 5% and 10% DC exerted antibiofilm activity with respect to the control, in the two evaluated times (p < 0.001). Comparison between groups showed a tendency of increased antimicrobial effect, both over time and depending on the DC concentration. These results coincide with those obtained in CLSM analysis, where efficacy increased with time and DC concentration.

CONCLUSIONS AND CLINICAL RELEVANCE

Biodentine, over time, showed antimicrobial and antibiofilm efficacy on polymicrobial biofilms. The addition of 5% and 10% DC to BD enhanced this effect, in a concentration- and time-dependent manner.

Concentrated MTA Repair HP reduced biofilm and can cause reparative action at a distance

AIM

To evaluate in vitro whether MTA Repair HP can induce repair processes at a distance, including its effects on biofilm, cell viability, migration, production of TGF-β, phosphate and ALP, evaluated through MTA diluted extracts.

METHODOLOGY

Initially, antibacterial tests were performed with the bacterium Streptococcus mutans (ATCC 25175) in the presence of MTA extracts (dilutions of 1:1, 1:2 and 1:4). Growth inhibition assay by microdilution in broth, antibiofilm plate assay of young biofilm and antibiofilm assay in confocal microscopy of mature biofilm were carried out. Then, pulp cells were stimulated in the presence of several MTA dilutions, and cell viability (MTT assay), proliferation and migration capacity (scratch assay) were evaluated. To evaluate the capacity of 1:1, 1:2 and 1:4 dilutions of MTA Repair HP to promote the production of important agents of odontogenic differentiation and mineralization, ALP activity, TGF-β secretion and phosphate quantification were measured. Statistical differences were verified using one-way and two-way anova and Tukey's post-tests.

RESULTS

The test dilutions of MTA Repair HP did not inhibit planktonic S. mutans growth but were able to reduce young and mature S. mutans biofilm (p < 0.001). In addition, none of the MTA Repair HP dilutions was cytotoxic for pulp cells. The 1:2 and 1:4 dilutions of MTA Repair HP induced migration and proliferation of pulp cells (p < 0.05). ALP activity and TGF-β secretion were independent of the tested dilution (p < 0.001). Diluted 1:4 MTA Repair HP produced less phosphate than the more concentrated 1:1 and 1:2 MTA dilutions (p < 0.001).

CONCLUSIONS

Undiluted MTA Repair HP reduced S. mutans biofilm, when compared to 1:2 and 1:4 MTA dilutions. Furthermore, none of the tested dilutions was cytotoxic to pulp cells. MTA Repair HP promoted cell migration and proliferation at a distance, assessed through the dilution of the MTA. Even from a distance, MTA Repair HP has the ability to participate in some events related to repair, such as migration, proliferation and TGF production.

Antimicrobial Activity of Calcium Silicate-Based Dental Materials: A Literature Review

Endodontic biomaterials have significantly improved dental treatment techniques in several aspects now that they can be used for vital pulp treatments, as temporary intracanal medication, in definitive fillings, in apical surgeries, and for regenerative procedures. Calcium silicate-based cement is a class of dental material that is used in endodontics in direct contact with the dental structures, connective tissue, and bone. Because the material interacts with biological tissues and stimulates biomineralization processes, its properties are of major importance. The main challenge in endodontic treatments is the elimination of biofilms that are present in the root canal system anatomical complexities, as it remains even after chemical-mechanical preparation and disinfection procedures. Thus, an additional challenge for these biomaterials is to exert antimicrobial activity while maintaining their biological properties in parallel. This article reviews the literature for studies considering the antimicrobial properties of calcium silicate-based dental biomaterials used in endodontic practice. Considering the reviewed studies, it can be affirmed that the reduced antimicrobial effect exhibited by calcium silicate-based endodontic materials clearly emphasizes that all clinical procedures prior to their use must be carefully performed. Future studies for the evaluation of these materials, and especially newly proposed materials, under poly-microbial biofilms associated with endodontic diseases will be necessary.

Apicoectomy of Perforated Root Canal Using Bioceramic Cement and Photodynamic Therapy

Root perforation is a common endodontic accident. Its management depends mainly on root canal disinfection and sealing the perforation area by preventing any communication with the periodontium to prevent recontamination. A patient was referred to treat root perforation due to a previous treatment of tooth #22. The diagnosis was symptomatic periapical periodontitis, and the treatment plan was to retreat the root canal of #22 and make a surgical intervention (apicoectomy) associated with antimicrobial photodynamic therapy as a complementary technique. Five mineral oxides (5MO) cement was used as a root-end filling material. The procedures were performed in two sessions and controlled in two visits (after 30 days and 12 months). A bone neoformation was observed at the periapical area of tooth #22. 5MO bioceramic cement was effective in inducing the repair of the periapical lesion and had the ability to seal the exposed periapical area of the tooth. Its success depended mainly on root canal and surgical site disinfection.

Antimicrobial action of NeoMTA Plus on mono- and dual-species biofilms of Enterococcus faecalis and Candida albicans: An in vitro study

OBJECTIVE

To evaluate the antimicrobial action of NeoMTA Plus on mono- and dual-species biofilms of Enterococcus faecalis and Candida albicans.

MATERIAL AND METHODS

A total of 171 sterile dentin blocks, measuring 4 mm × 4 mm × 1 mm, were incubated in media containing E. faecalis (3.1 × 10⁸ cells/mL) and/or C. albicans (1 × 10⁷ cells/mL) for 2 d. These blocks were randomly divided into three groups: the control (no treatment with biomaterials), MTA (treated with an MTA sample with width and thickness same as those of the dentin block after the material was set), and NeoMTA Plus (treated with NeoMTA Plus in a fashion similar to the treatment of the MTA group) groups. The biomaterials remained in contact with the biofilms for 24 h. Quantitative analyses of the number of colony-forming units (CFUs) and metabolic activity (XTT), were performed. Furthermore, qualitative analysis of biofilm structure was performed by scanning electron microscopy. Data were statistically analyzed considering a significance level of 5%.

RESULTS

XTT and the number of CFUs were similar among the groups (p > 0.05). The type of biofilm (mono- or dual-species) or the biomaterial used (MTA or NeoMTA Plus) did not affect the results. Biofilm structure exhibited a robust architecture composed of yeast and bacterial cell multilayers and was homogeneous among the groups.

CONCLUSION

NeoMTA Plus was not effective against mono- and dual-species biofilms of E. faecalis and C. albicans. Further research investigating biofilm removal methods including those involving the use of biomaterials with antiseptics and other supporting therapies is warranted.

Physicochemical, antimicrobial, and biological properties of White-MTAFlow

OBJECTIVES

To evaluate a new material containing tantalum oxide as an alternative radiopacifier, and a water-based gel for hydration, in comparison with two calcium silicate-based cement: ProRoot MTA and Biodentine.

MATERIALS AND METHODS

ProRoot MTA (Dentsply), Biodentine (Septodont), and a new hydraulic calcium silicate cement White-MTAFlow (Ultradent) (in 'thin' consistency) were characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive spectroscopy (EDS). The interaction with dentin was also assessed using SEM and EDS. Physical and chemical properties radiopacity, setting time, linear flow, volumetric central filling, and lateral flow, pH, and volume change were investigated together with the color luminosity (L) and color change (ΔE). The agar diffusion and direct contact antimicrobial activity, and methylthiazolyldiphenyl-tetrazolium-bromide (MTT) cytotoxicity using human fibroblast cells were also evaluated. Data were statistically analyzed at a 5% significance level.

RESULTS

All materials were composed of tricalcium and dicalcium silicate but had different radiopacifiers, and calcium hydroxide (portlandite) deposition was detected in XRD analysis. White-MTAFlow exhibited radiopacity values in accordance with ISO standard, and the longest setting time. The water-based gel provided the highest linear flow, a comparable cavity central filling, and the highest groove-lateral flow in the volumetric flow analysis. White-MTAFlow exhibited an alkalinity reduction, and Biodentine, a progressive increase of pH values after 28 days. However, similar volume loss for White-MTAFlow was assessed in comparison to Biodentine after the 28-day immersion. White-MTAFlow showed the highest L value (91.5), and ProRoot MTA the lowest (78.1) due to dentin staining caused by bismuth migration. None of the materials exhibited inhibition halos against the tested bacteria, and similar turbidity values were obtained after 48 h in direct contact with E. faecalis, indicating an upregulation to bacterial growth. White-MTAFlow showed MTT cytocompatibility similarly to the control group.

CONCLUSIONS

White-MTAFlow in 'thin' consistency presents comparable physicochemical, biological, and antimicrobial properties to ProRoot MTA and Biodentine, and does not cause color alteration in dentin.

CLINICAL RELEVANCE

White-MTAFlow is a suitable material for use as reparative endodontic cement. Further studies considering its biocompatibility are necessary.

Dental discoloration caused by Grey-MTAFlow cement: analysis of its physicochemical, biological and antimicrobial properties

Tricalcium silicate-based cement are materials used in reparative and regenerative procedures in endodontics. A recently proposed formulation aimed to enhance handling during clinical use with a versatile material applicable by syringe. Although, the use of bismuth oxide as radiopacifier and grey raw powder are drawbacks considering aesthetics.

The Antibiofilm Activity and Mechanism of Nanosilver- and Nanozinc-Incorporated Mesoporous Calcium-Silicate Nanoparticles

Background

Mesoporous calcium-silicate nanoparticles (MCSNs) have good prospects in the medical field due to their great physicochemical characteristics, antibacterial activity and drug delivery capacity. This study was to analyze the antibiofilm activity and mechanisms of silver (Ag) and zinc (Zn) incorporated MCSNs (Ag/Zn-MCSNs) with different percentages of Ag and Zn.

Methods

Ag/Zn(1:9, molar ratio)-MCSNs and Ag/Zn(9:1, molar ratio)-MCSNs were prepared and characterized. Endocytosis of nanoparticles by Enterococcus faecalis (E. faecalis) treated with Ag/Zn-MCSNs was observed using TEM to explore the antibacterial mechanisms. The antibiofilm activity of Ag/Zn-MCSNs with different ratios of Ag and Zn was tested by E. faecalis biofilm model in human roots. The human roots pretreated by different Ag/Zn-MCSNs were cultured with E. faecalis. Then, SEM and CLSM were used to observe the survival of E. faecalis on the root canal wall. Cytotoxicity of the nanoparticles was tested by CCK8 kits.

Results

The Ag/Zn-MCSNs release Ag⁺ and destroy the cell membranes to kill bacteria. The MCSNs containing Ag showed antibacterial activity against E. faecalis biofilms in different degrees, and they can adhere to dentin surfaces to get a continuous antibacterial effect. However, MTA, MCSNs and Zn-MCSNs could not disrupt the bacterial biofilms obviously. MCSNs, Ag/Zn(1:1, molar ratio)-MCSNs and Ag/Zn(1:9)-MCSNs showed no obvious cytotoxicity, while Ag-MCSNs and Ag/Zn(9:1)-MCSNs showed cytotoxicity. Zn-MCSNs can slightly promote cell proliferation.

Conclusion

Ag/Zn-MCSNs have good antibiofilm activity. They might achieve an appropriate balance between the antibacterial activity and cytotoxicity by adjusting the ratio of Ag and Zn. Ag/Zn-MCSNs are expected to be a new type of root canal disinfectant or sealer for root canal treatment.

Detection, treatment and prevention of endodontic biofilm infections: what's new in 2020?

Endodontic disease, a biofilm infection of the root canal space, is a significant cause of dental morbidity worldwide. Endodontic treatment, or root canal treatment, as it is commonly known is founded on the ability to eradicate microbial biofilm infection and prevent re-infection of the highly complex root canal space. Despite many "advances" in clinical endodontics we have seen little improvement in outcomes. The aim of this critical review paper is to provide a contemporary view of endodontic microbiology and biofilm polymicrobiality, provide an understanding of the host response, and how together these impact upon clinical treatment. Ultimately, it is intended to provide insight into novel opportunities and strategies for the future diagnostics, treatment, and prevention of endodontic disease.

Effect of a bioactive cement on the microbial community in carious dentin after selective caries removal - An in-vivo study

OBJECTIVES

Selective caries removal in deep lesions means that soft carious affected dentin is left in the center of the cavity. Thus, using a tricalcium silicate cement Biodentine™ (Septodont, Paris) to seal the remaining soft dentin could have an antibacterial effect. This in-vivo study aimed to do quantitative and qualitative analyses on the bacterial composition within carious dentin before and after selective caries removal when applying Biodentine.

METHODS

Eleven patients with deep primary carious lesions at two posterior teeth without pulpal symptoms were included. Carious dentin was selectively removed and sampled with a sterile round bur (Komet No. 18) at baseline visit and eight weeks later. On the first visit, one lesion per patient, the remaining carious dentin was covered with Biodentine before adhesive restoration. Caries samples were investigated by microbial cultivation, molecular analysis and amplicon deep-sequencing of 16S rRNA genes. Bacterial DNA from intact cells was differentiated from cell-free DNA by DNase degradation prior to DNA isolation.

RESULTS

Reduction of cell-derived as well as cell-free bacterial DNA eight weeks after selective caries removal was significantly higher when Biodentine was applied. Lactobacillus was most abundant within the microbial community of deep carious dentin lesions at the first visit. After intervention with Biodentine application, Lactobacillus was diminished to a high degree. In general, the diversity in samples, as well as bacterial composition differed interindividually as well as intraindividually.

CONCLUSION AND CLINICAL SIGNIFICANCE

Despite the heterogenous and diversity of microbial composition in patients, Biodentine can have beneficial antibacterial effects when applied to residual carious dentin, offering an alternative and safe treatment option. The study is officially registered with German Clinical Trials Register (DRKS00011067).