Effect of iodixanol particle size on the mechanical properties of a PMMA based bone cement

A Three-Parameter Weibull Distribution Method to Determine the Fracture Property of PMMA Bone Cement

Poly (methyl methacrylate) (PMMA) bone cement is an excellent biological material for anchoring joint replacements. Tensile strength ft and fracture toughness KIC have a considerable impact on its application and service life. Considering the variability of PMMA bone cement, a three-parameter Weibull distribution method is suggested in the current study to evaluate its tensile strength and fracture toughness distribution. The coefficients of variation for tensile strength and fracture toughness were the minimum when the characteristic crack of PMMA bone cement was αch∗=8dav. Using the simple equation αch∗=8dav and fictitious crack length Δαfic=1.0dav, the mean value μ (= 43.23 MPa), minimum value ftmin (= 26.29 MPa), standard deviation σ (= 6.42 MPa) of tensile strength, and these values of fracture toughness (μ = 1.77 MPa⋅m1/2, KICmin = 1.02 MPa⋅m1/2, σ = 0.2644 MPa⋅m1/2) were determined simultaneously through experimental data from a wedge splitting test. Based on the statistical analysis, the prediction line between peak load Pmax and equivalent area Ae1Ae2 was obtained with 95% reliability. Nearly all experimental data are located within the scope of a 95% confidence interval. Furthermore, relationships were established between tensile strength, fracture toughness, and peak load Pmax. Consequently, it was revealed that peak load might be used to easily obtain PMMA bone cement fracture characteristics. Finally, the critical geometric dimension value of the PMMA bone cement sample with a linear elastic fracture was estimated.

The influence of low concentrations of a water soluble poragen on the material properties, antibiotic release, and biofilm inhibition of an acrylic bone cement

Soluble particulate fillers can be incorporated into antibiotic-loaded acrylic bone cement in an effort to enhance antibiotic elution. Xylitol is a material that shows potential for use as a filler due to its high solubility and potential to inhibit biofilm formation. The objective of this work, therefore, was to investigate the usage of low concentrations of xylitol in a gentamicin-loaded cement. Five different cements were prepared with various xylitol loadings (0, 1, 2.5, 5 or 10 g) per cement unit, and the resulting impact on the mechanical properties, cumulative antibiotic release, biofilm inhibition, and thermal characteristics were quantified. Xylitol significantly increased cement porosity and a sustained increase in gentamicin elution was observed in all samples containing xylitol with a maximum cumulative release of 41.3%. Xylitol had no significant inhibitory effect on biofilm formation. All measured mechanical properties tended to decrease with increasing xylitol concentration; however, these effects were not always significant. Polymerization characteristics were consistent among all groups with no significant differences found. The results from this study indicate that xylitol-modified bone cement may not be appropriate for implant fixation but could be used in instances where sustained, increased antibiotic elution is warranted, such as in cement spacers or beads.

Mechanical effects, antimicrobial efficacy and cytotoxicity of usnic acid as a biofilm prophylaxis in PMMA

Experiments were performed to test the null hypothesis that the addition of a natural occurring antibiotic would not alter mechanical properties of polymethylmethacrylate (PMMA). Compression and four-point bending tests were used to assess mechanical properties of zirconium dioxide bearing bone cement (Type Zr) and barium sulfate bearing bone cement (Type Ba), mixed with the antibiotic usnic acid ("usnic"), used to create a surface resistant to biofilm formation. Addition of usnic had a statistically significant effect on the material properties. Compressive and bending strengths decreased as usnic was added and Type Zr was stronger than Type Ba although material properties remained above recommended minima. With implications of liver toxicity with large doses of usnic taken as a dietary supplement, cytotoxicity tests using bone cement coupons were performed and showed very little or no toxicity in primary cultures of rabbit skin derived fibroblasts. A simple test of usnic's efficacy as a biofilm prophylaxis in PMMA was also conducted. Bone cement coupons with usnic were tested for their effectiveness against methicillin resistant Staphylococcus aureus. Diminished biofilm formation on usnic-containing coupons indicated that usnic can be an effective anti-microbial agent.