Hussein MA, Kumar AM, Azeem MA, Sorour AA, Saravanan S. Ti-30Nb-3Ag alloy with improved corrosion resistance and antibacterial properties for orthopedic and dental applications produced by mechanical alloying. J Mech Behav Biomed Mater 2023; 142:105851. [PMID: 37068434 DOI: 10.1016/j.jmbbm.2023.105851] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/14/2023] [Revised: 04/10/2023] [Accepted: 04/12/2023] [Indexed: 04/19/2023]
Abstract
Titanium alloys have gained popularity as a bioimplant material due to their biocompatibility, low modulus of elasticity, and increased strength. However, other issues, such as corrosion resistance, and infections can reduce the implant's lifespan. This paper aims to fabricate a new Ti-30Nb-3Ag at% alloy with enhanced in vitro corrosion and antibacterial properties by mechanical alloying (MA) followed by powder consolidation. XRD, SEM/EDX, and Vickers microhardness analyses were used to examine the phases compositions, microstructure, and microhardness, respectively. The in vitro corrosion performance of Ti-30Nb-3Ag alloy was inspected in a simulated body medium and artificial saliva. The alloy's antibacterial properties were evaluated in the gram-positive and negative bacterial medium. The results showed that after MA for 60 h, nanocrystalline β-Ti (BCC) and α-Ti (HCP) solid solutions were formed with crystallite sizes of 7.44 and 3.47 nm, respectively. The sintered sample exhibited densifications of 97%, with a microstructure composed of β-Ti, α-Ti, and a minor quantity of ultrafine Ti2Ag phase. The microhardness result showed that Ti-30Nb-3Ag alloy possesses HV 491.5. Ti-30Nb-3Ag alloy has a potent antibacterial capability of 85.75% and 88.81% relative to Ti-6Al-4V alloy and CP-Ti, respectively. In vitro corrosion results revealed that the Ti-30Nb-3Ag alloy exhibited the widespread passive area in the investigated anodic regions and presented the highest impedance values in comparison with the commercial alloys, confirming its improved corrosion resistance performance in both studied mediums. Ti-30Nb-3Ag alloy possibly be a competitive bioimplant material for orthopedic and dental uses owing to its enhanced biocorrosion and antibacterial properties compared to commercial Ti-6Al-4V alloy and CP-Ti.
Collapse
Affiliation(s)
- M A Hussein
- Interdisciplinary Research Center for Advanced Materials, King Fahd University of Petroleum & Minerals (KFUPM), Dhahran, 31261, Saudi Arabia.
| | - A Madhan Kumar
- Interdisciplinary Research Center for Advanced Materials, King Fahd University of Petroleum & Minerals (KFUPM), Dhahran, 31261, Saudi Arabia
| | - M A Azeem
- Department of Mechanical Engineering, King Fahd University of Petroleum & Minerals(KFUPM), Dhahran, 31261, Saudi Arabia
| | - A A Sorour
- Interdisciplinary Research Center for Advanced Materials, King Fahd University of Petroleum & Minerals (KFUPM), Dhahran, 31261, Saudi Arabia; Department of Mechanical Engineering, King Fahd University of Petroleum & Minerals(KFUPM), Dhahran, 31261, Saudi Arabia
| | - S Saravanan
- Department of Bioengineering, King Fahd University of Petroleum and Minerals, Dhahran, 31261, Saudi Arabia
| |
Collapse
|
2
|
Development of Antibacterial Ti-Cu x Alloys for Dental Applications: Effects of Ageing for Alloys with Up to 10 wt% Cu. MATERIALS 2019; 12:ma12234017. [PMID: 31816905 PMCID: PMC6926654 DOI: 10.3390/ma12234017] [Citation(s) in RCA: 19] [Impact Index Per Article: 3.8] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 10/29/2019] [Revised: 11/27/2019] [Accepted: 11/28/2019] [Indexed: 11/17/2022]
Abstract
Peri-implantitis, a disease caused by bacteria, affects dental implants in patients. It is widely treated with antibiotics, however, with growing antibiotic resistance new strategies are required. Titanium-copper alloys are prospective antibacterial biomaterials, with the potential to be a remedy against peri-implantitis and antibiotic resistance. The aim of this study was to investigate Ti-Cux alloys, exploring how Cu content (up to 10 wt%) and ageing affect the material properties. Electron microscopy, X-ray diffraction, hardness testing, bacteriological culture, and electrochemical testing were employed to characterize the materials. It was found that alloys with above 3 wt% Cu had two phases and ageing increased the volume fraction of Ti2Cu. An un-aged alloy of 5 wt% Cu showed what could be Ti3Cu, in addition to the α-Ti phase. The hardness gradually increased with increased Cu additions, while ageing only affected the alloy with 10 wt% Cu (due to changes in microstructure). Ageing resulted in faster passivation of the alloys. After two hours the aged 10 wt% Cu alloy was the only material with an antibacterial effect, while after six hours, bacteria killing occurred in all alloys with above 5 wt% Cu. In conclusion, it was possible to tune the material and antibacterial properties of Ti-Cux alloys by changing the Cu concentration and ageing, which makes further optimization towards an antibacterial material promising.
Collapse
|
3
|
Effect of Copper Ion Concentration on Bacteria and Cells. MATERIALS 2019; 12:ma12223798. [PMID: 31752323 PMCID: PMC6888263 DOI: 10.3390/ma12223798] [Citation(s) in RCA: 32] [Impact Index Per Article: 6.4] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 08/09/2019] [Revised: 10/10/2019] [Accepted: 11/12/2019] [Indexed: 12/27/2022]
Abstract
In the oral cavity, dental implants—most often made of commercially pure titanium—come in contact with bacteria, and antibacterial management has been researched extensively to improve patient care. With antibiotic resistance becoming increasingly prevalent, this has resulted in copper being investigated as an antibacterial element in alloys. In this study, the objective was to investigate the copper ion concentrations at which cyto-toxicity is avoided while bacterial inhibition is ensured, by comparing Cu ion effects on selected eukaryotes and prokaryotes. To determine relevant copper ion concentrations, ion release rates from copper and a 10 wt. % Cu Ti-alloy were investigated. Survival studies were performed on MC3T3 cells and Staphylococcus epidermidis bacteria, after exposure to Cu ions concentrations ranging from 9 × 10−3 to 9 × 10−12 g/mL. Cell survival increased from <10% to >90% after 24 h of exposure, by reducing Cu concentrations from 9 × 10−5 to 9 × 10−6 g/mL. Survival of bacteria also increased in the same range of Cu concentrations. The maximum bacteria growth was found at 9 × 10−7 g/mL, probably due to stress response. In conclusion, the minimum inhibitory concentrations of Cu ions for these prokaryotes and eukaryotes were found in the range from 9 × 10−5 to 9 × 10−6 g/mL. Interestingly, the Cu ion concentration correlating to the release rate of the 10 wt. % Cu alloy (9 × 10−8 g/mL) did not kill the bacteria, although this alloy has previously been found to be antibacterial. Further studies should investigate in depth the bacteria-killing mechanism of copper.
Collapse
|
4
|
Zhang Z, Zheng G, Li H, Yang L, Wang X, Qin G, Zhang E. Anti-bacterium influenced corrosion effect of antibacterial Ti-3Cu alloy in Staphylococcus aureus suspension for biomedical application. MATERIALS SCIENCE & ENGINEERING. C, MATERIALS FOR BIOLOGICAL APPLICATIONS 2018; 94:376-384. [PMID: 30423720 DOI: 10.1016/j.msec.2018.09.057] [Citation(s) in RCA: 25] [Impact Index Per Article: 4.2] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 11/16/2017] [Revised: 08/12/2018] [Accepted: 09/20/2018] [Indexed: 11/25/2022]
Abstract
Titanium and titanium alloys have been widely used as dental and orthopedic materials. The infection and the bacterium influenced corrosion both are concerned problems. Ti-3Cu alloy exhibits strong antibacterial properties against E. coli and S. aureus. The strong antibacterial properties of Ti-3Cu provides with a potential new method to reduce the bacterium influenced corrosion. S. aureus suspension was selected to simulate a serious bacterial condition. The corrosion behavior of Ti-3Cu alloy in S. aureus suspension was investigated by an electrochemical testing and an immersion test in comparison with pure titanium. Electrochemical results showed that Ti-3Cu exhibited a much better anti-corrosion property than cp-Ti in S. aureus suspension. Surface observation demonstrated that no corrosion pit was observed on Ti-3Cu alloy after 30 days immersion in the suspension while lots of corrosion pits were found on cp-Ti. The biofilm formation on the surface was observed by scanning electronic microscopy (SEM) in different periods. It has been revealed that S. aureus could grow and gather on the surface of cp-Ti to form biofilm after 18 h immersion, but only several bacteria were found on Ti-3Cu alloy even after 24 h immersion, displaying that Ti-3Cu alloy exhibits very strong anti-adhesion properties against S. aureus. It was concluded that Ti-3Cu performs a super anti-corrosion property due to the strong anti-adhesion property, in which Ti2Cu precipitate plays a critical role.
Collapse
Affiliation(s)
- Ziming Zhang
- Key Laboratory for Anisotropy and Texture of Materials, Education Ministry of China, School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China
| | - Guitian Zheng
- Key Laboratory for Anisotropy and Texture of Materials, Education Ministry of China, School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China
| | - Haixia Li
- Key Laboratory for Anisotropy and Texture of Materials, Education Ministry of China, School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China
| | - Lei Yang
- Key Laboratory for Anisotropy and Texture of Materials, Education Ministry of China, School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China
| | - Xiaoyan Wang
- School of Metallurgy, Northeastern University, Shenyang 110819, China
| | - Gaowu Qin
- Key Laboratory for Anisotropy and Texture of Materials, Education Ministry of China, School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China
| | - Erlin Zhang
- Key Laboratory for Anisotropy and Texture of Materials, Education Ministry of China, School of Materials Science and Engineering, Northeastern University, Shenyang 110819, China.
| |
Collapse
|
5
|
Lu Y, Ren L, Xu X, Yang Y, Wu S, Luo J, Yang M, Liu L, Zhuang D, Yang K, Lin J. Effect of Cu on microstructure, mechanical properties, corrosion resistance and cytotoxicity of CoCrW alloy fabricated by selective laser melting. J Mech Behav Biomed Mater 2018; 81:130-141. [PMID: 29510340 DOI: 10.1016/j.jmbbm.2018.02.026] [Citation(s) in RCA: 6] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 05/14/2017] [Revised: 02/17/2018] [Accepted: 02/19/2018] [Indexed: 11/17/2022]
Abstract
In the study, CoCrWCu alloys with differing Cu content (2, 3, 4 wt%) were prepared by selective laser melting using mixture powders consisting of CoCrW and Cu, aiming at investigating the effect of Cu on the microstructures, mechanical properties, corrosion behavior and cytotoxicity. The SEM observations indicated that the Cu content up to 3 wt% caused the Si-rich precipitates to segregate along grain boundaries and in the grains, and EBSD analysis suggested that the Cu addition decreased the recrystallization degree and increased the grain diameter and fraction of big grains. The tensile tests found that the increasing Cu content led to a decrease of mechanical properties compared with Cu-free CoCrW alloy. The electrochemical tests revealed that the addition of Cu shifted the corrosion potential toward nobler positive, but increased the corrosion current density. Also, a more protective passive film was formed when 2 wt% Cu content was added, but the higher Cu content up to 3 wt% was detrimental to the corrosion resistance. It was noted that there was no cytotoxicity for Cu-bearing CoCrW alloys to MG-63 cell and the cells could spread well on the surfaces of studied alloys. Meanwhile, the Cu-bearing CoCrW alloy exhibited an excellent antibacterial performance against E.coli when Cu content was up to 3 wt%. It is suggested that the feasible fabrication of Cu-bearing CoCrW alloy by SLM using mixed CoCrW and Cu powders is a promising candidate for use in antibacterial oral repair products. This current study also can aid in the further design of antibacterial Cu-containing CoCrW alloying powders.
Collapse
Affiliation(s)
- Yanjin Lu
- Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155 Yangqiao Rd West, Fuzhou, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Ling Ren
- Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Rd, Shenyang, China.
| | - Xiongcheng Xu
- Key Laboratory of Stomatology, Fujian Medical University, 88 Jiaotong Road, Fuzhou, China
| | - Yang Yang
- Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155 Yangqiao Rd West, Fuzhou, China
| | - Songquan Wu
- Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155 Yangqiao Rd West, Fuzhou, China
| | - Jiasi Luo
- Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155 Yangqiao Rd West, Fuzhou, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Mingyu Yang
- Southwest Hospital, Army Medical University, Chongqing, China
| | - Lingling Liu
- Key Laboratory of Stomatology, Fujian Medical University, 88 Jiaotong Road, Fuzhou, China
| | - Danhong Zhuang
- Key Laboratory of Stomatology, Fujian Medical University, 88 Jiaotong Road, Fuzhou, China
| | - Ke Yang
- Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Rd, Shenyang, China
| | - Jinxin Lin
- Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155 Yangqiao Rd West, Fuzhou, China; University of Chinese Academy of Sciences, Beijing 100049, China.
| |
Collapse
|
6
|
Optimization of mechanical properties, biocorrosion properties and antibacterial properties of wrought Ti-3Cu alloy by heat treatment. Bioact Mater 2018; 3:28-38. [PMID: 29744440 PMCID: PMC5935767 DOI: 10.1016/j.bioactmat.2018.01.004] [Citation(s) in RCA: 39] [Impact Index Per Article: 6.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/02/2017] [Revised: 01/25/2018] [Accepted: 01/26/2018] [Indexed: 12/16/2022] Open
Abstract
Previous study has shown that Ti-3Cu alloy shows good antibacterial properties (>90% antibacterial rate), but the mechanical properties still need to be improved. In this paper, a series of heat-treatment processes were selected to adjust the microstructure in order to optimize the properties of Ti-3Cu alloy. Microstructure, mechanical properties, biocorrosion properties and antibacterial properties of wrought Ti-3Cu alloy at different conditions was systematically investigated by X-ray diffraction, optical microscope, scanning electron microscope, transmission electron microscopy, electrochemical measurements, tensile test, fatigue test and antibacterial test. Heat treatment could significantly improve the mechanical properties, corrosion resistance and antibacterial rate due to the redistribution of copper elements and precipitation of Ti2Cu phase. Solid solution treatment increased the yield strength from 400 to 740 MPa and improved the antibacterial rate from 33% to 65.2% while aging treatment enhanced the yield strength to 800–850 MPa and antibacterial rate (>91.32%). It was demonstrated that homogeneous distribution and fine Ti2Cu phase plays a very important role in mechanical properties, corrosion resistance and antibacterial properties. Heat treatment increased the tensile strength but reduced the ductility of Ti-Cu alloy. Heat treatment improved the corrosion resistance of Ti-Cu alloy slightly. Heat treatment enhanced the antibacterial properties of Ti-Cu alloy.
Collapse
|
7
|
Bai B, Zhang E, Liu J, Zhu J. The anti-bacterial activity of titanium-copper sintered alloy against Porphyromonas gingivalis in vitro. Dent Mater J 2017; 35:659-67. [PMID: 27477233 DOI: 10.4012/dmj.2016-001] [Citation(s) in RCA: 24] [Impact Index Per Article: 3.4] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/23/2022]
Abstract
This study investigates the anti-bacterial property of Ti-Cu sintered alloys against Porphyromonas gingivalis. The anti-anaerobic property of Ti-Cu sintered alloys against P. gingivalis was investigated by antibacterial activity test, DNA measurement, DAPI staining and morphology observation. The antibacterial rates of the Ti-5Cu against P. gingivalis after 18 and 24 h incubation were 36.04 and 54.39%, and those of Ti-10Cu were 68.69 and 75.39%, which were lower than their anti-aerobic abilities. The concentration of P. gingivalis DNA gradually decreased with the increasing Cu content, which was nearly 50% after 24 h incubation on Ti-10Cu. SEM results showed that the shape of P. gingivalis changed and the bacteria broke apart with the addition of Cu and the extension of the culture time. Ti-Cu sintered alloys could not only kill anaerobic bacteria but also reduce the activity of the survived bacteria. The anti-anaerobic mechanism was thought to be in associated with the Cu ion released from Ti-Cu alloy.
Collapse
Affiliation(s)
- Bing Bai
- Department of Prosthodontics, School of Stomatology, China Medical University
| | | | | | | |
Collapse
|
8
|
Fretting Corrosion Behavior of Experimental Ti-20Cr Compared to Titanium. MATERIALS 2017; 10:ma10020194. [PMID: 28772554 PMCID: PMC5459177 DOI: 10.3390/ma10020194] [Citation(s) in RCA: 11] [Impact Index Per Article: 1.6] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 01/19/2017] [Revised: 02/13/2017] [Accepted: 02/14/2017] [Indexed: 11/17/2022]
Abstract
Experimental cast titanium alloys containing 20 mass% chromium (Ti-20Cr) show preferable mechanical properties and a good corrosion resistance. This study evaluated the fretting corrosion behavior of Ti-20Cr. Ti-20Cr (n = 4) and commercially pure titanium (CP-Ti, n = 6) disk specimens were used. The fretting corrosion test was performed by electrochemical corrosion at 0.3 V in 0.9% saline solution and mechanical damage using 10 scratching cycles with three different scratching speeds (10–40 mm/s) at 10 N. After testing, the activation peak, repassivation time and surface morphology of each specimen were analyzed. The differences between the results were tested by parametric tests (α = 0.05). The average activation peaks were significantly higher in CP-Ti than in Ti-20Cr (p < 0.01), except at 20 mm/s. In the series of scratching speeds, faster scratching speeds showed higher activation peaks. The maximum activation peaks were also higher in CP-Ti. Slight differences in the repassivation time were observed between the materials at every scratching speed; faster scratching speeds showed shorter repassivation times in both materials (p < 0.05). CP-Ti showed severe damage and significantly higher wear depth than Ti-20Cr (p < 0.05). In conclusion, adding chromium to titanium reduced surface damage and improved the fretting corrosion resistance.
Collapse
|
9
|
Effect of extrusion processing on the microstructure, mechanical properties, biocorrosion properties and antibacterial properties of Ti-Cu sintered alloys. MATERIALS SCIENCE & ENGINEERING. C, MATERIALS FOR BIOLOGICAL APPLICATIONS 2016; 69:760-8. [PMID: 27612770 DOI: 10.1016/j.msec.2016.07.051] [Citation(s) in RCA: 43] [Impact Index Per Article: 5.4] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 06/16/2016] [Revised: 07/12/2016] [Accepted: 07/19/2016] [Indexed: 11/23/2022]
Abstract
Ti-Cu sintered alloys, Ti-Cu(S) alloy, have exhibited good anticorrosion resistance and strong antibacterial properties, but low ductility in previous study. In this paper, Ti-Cu(S) alloys were subjected to extrusion processing in order to improve the comprehensive property. The phase constitute, microstructure, mechanical property, biocorrosion property and antibacterial activity of the extruded alloys, Ti-Cu(E), were investigated in comparison with Ti-Cu(S) by X-ray diffraction (XRD), optical microscopy (OM), scanning electronic microscopy (SEM) with energy disperse spectroscopy (EDS), mechanical testing, electrochemical testing and plate-count method in order to reveal the effect of the extrusion process. XRD, OM and SEM results showed that the extrusion process did not change the phase constitute but refined the grain size and Ti2Cu particle significantly. Ti-Cu(E) alloys exhibited higher hardness and compressive yield strength than Ti-Cu(S) alloys due to the fine grain and Ti2Cu particles. With the consideration of the total compressive strain, it was suggested that the extrusion process could improve the ductility of Ti-Cu alloy(S) alloys. Electrochemical results have indicated that the extrusion process improved the corrosion resistance of Ti-Cu(S) alloys. Plate-count method displayed that both Ti-Cu(S) and Ti-Cu(E) exhibited strong antibacterial activity (>99%) against S. aureus. All these results demonstrated that hot forming processing, such as the extrusion in this study, refined the microstructure and densified the alloy, in turn improved the ductility and strength as well as anticorrosion properties without reduction in antibacterial properties.
Collapse
|