Regeneration of Na-ETS-10 using microwave and conductive heating

Graphene oxide enhances thermal stability and microwave absorption/regeneration of a porous polymer

Microwave regeneration of adsorbents offers several advantages over conventional regeneration methods; however, its application for microwave transparent adsorbents such as polymers is challenging. In this study, hypercrosslinked polymer/graphene oxide (GO) nanocomposites with large surface area and enhanced microwave absorption ability were synthesized. Polymers of 4, 4´-bis ((chloromethyl)-1, 1´-biphenyl- benzyl chloride) were hypercrosslinked through the Friedel-Crafts reactions. GO sheets were synthesized through the Hummer's method. Nanocomposites with different GO contents (1-8 wt%) were synthesized by solution mixing method. Thermogravimetry analysis revealed a large enhancement in the thermal stability of GO-filled nanocomposites compared to pristine polymer. N₂ adsorption isotherm analysis showed 7% and 10% reduction in BET surface area and total pore volume of the nanocomposite with 8 wt% GO. Compared to the pristine polymer, the dielectric constant and dielectric loss factor increased from 5 to 17 and 0.05-1.6, respectively, for the nanocomposites with 8 wt% GO. Microwave-assisted desorption of toluene from samples revealed more than 160 ºC and 4 times improvement in the desorption temperature and desorption efficiency, respectively, by addition of 4 wt% GO to the polymer. This study showed the important role of GO addition for efficient microwave-assisted regeneration of polymer adsorbents.

Porous carbon black-polymer composites for volatile organic compound adsorption and efficient microwave-assisted desorption

Adsorbents with high surface area, thermal stability and microwave absorption ability are highly desired for cyclic adsorption and microwave regeneration processes. However, most polymeric adsorbents are transparent to microwaves. Herein, porous hyper-crosslinked polymers (HCP) of (4,4'-bis((chloromethyl)-1,1'-biphenyl-benzyl chloride)) with different carbon black (CB) contents were synthesized via the Friedel-Crafts reaction. CB was selected as the filler due to its low cost and high dielectric loss and was embedded inside the polymer structure during polymerization. CB-containing composites showed enhanced thermal stability at elevated temperatures, and more than a 90-times increase in the dielectric loss factor, which is favorable for microwave regeneration. Nitrogen physisorption analysis by the Bruner-Emmett-Teller isotherms demonstrated that CB presence in the polymer structure nonlinearly decreases the surface area and total pore volume (by 38% and 26%, respectively at the highest CB load). Based on the characterization testing, 4 wt% of CB was found to be an optimum filler content, having the highest MW absorption and minimal effect on the adsorbent porosity. HCP with 4 wt% CB allowed a substantial increase in the desorption temperature and yielded more than a 450% enhancement in the desorption efficiency compared to HCP without CB.

Using microwave heating to improve the desorption efficiency of high molecular weight VOC from beaded activated carbon

Incomplete regeneration of activated carbon loaded with organic compounds results in heel build-up that reduces the useful life of the adsorbent. In this study, microwave heating was tested as a regeneration method for beaded activated carbon (BAC) loaded with n-dodecane, a high molecular weight volatile organic compound. Energy consumption and desorption efficiency for microwave-heating regeneration were compared with conductive-heating regeneration. The minimum energy needed to completely regenerate the adsorbent (100% desorption efficiency) using microwave regeneration was 6% of that needed with conductive heating regeneration, owing to more rapid heating rates and lower heat loss. Analyses of adsorbent pore size distribution and surface chemistry confirmed that neither heating method altered the physical/chemical properties of the BAC. Additionally, gas chromatography (with flame ionization detector) confirmed that neither regeneration method detectably altered the adsorbate composition during desorption. By demonstrating improvements in energy consumption and desorption efficiency and showing stable adsorbate and adsorbent properties, this paper suggests that microwave heating is an attractive method for activated carbon regeneration particularly when high-affinity VOC adsorbates are present.