Passivation Behavior of Type-316L Stainless Steel in the Presence of Hydrogen Sulfide Ions Generated from a Local Anion Generating System

Effect of Sulfide and Chloride Ions on Pitting Corrosion of Type 316 Austenitic Stainless Steel in Groundwater Conditions Using Response Surface Methodology

This study investigates the corrosion resistance of Type 316 stainless steel as a candidate material for radioactive waste disposal canisters. The viability of stainless steel is examined under groundwater conditions with variations in pH, bisulfide ions (HS-), and chloride ions (Cl-) concentrations. Utilizing response surface methodology, correlations between corrosion factors and two crucial response variables, passive film breakdown potential and protection potential, are established. Cyclic potentiodynamic polarization tests and advanced analytical techniques provide detailed insights into the material's behavior. This research goes beyond, deriving an equation through response surface methodology that elucidates the relationship between the factors and breakdown potential. HS- weakens the passive film and reduces the pitting corrosion resistance of the stainless steel. However, this study highlights the inhibitory effect of HS- on pitting corrosion when Cl- concentrations are below 0.001 M and at equivalent concentrations of HS-. Under these conditions, immediate re-passivation occurs from the destroyed passive film to metal sulfides such as FeS2, MoS2, and MoS3. As a result, no hysteresis loop occurs in the cyclic polarization curve in these conditions. This research contributes to the understanding of Type 316 stainless-steel corrosion behavior, offering implications for the disposal of radioactive waste in geological repositories.

Passivation Effect of the Chlorinated Paraffin Added in the Cutting Fluid on the Surface Corrosion Resistance of the Stainless Steel

Cutting fluids are the most effective method to lower the cutting temperature and decrease the cutting tool wear. At the same time, the cutting fluids influence the corrosion resistance property of the machined surface. In this study, chlorinated paraffin (CP), which is a common additive in the cutting fluid, was selected as the research objective to study its corrosion resistance property. The passivation effect of CP with different concentrations on the machined surface of stainless steel was studied. Electrochemical measurements and surface morphology investigation were used to characterize the passivation effect of CP with different concentrations. The test results showed that the corrosion resistance of stainless steel in the cutting fluid was enhanced with the increase in CP additive. This reason is that the charge transfer resistance increases and the corrosion current density decreases with the increase in CP additive. The X-ray photoelectron spectroscopy (XPS) results show that the proportion of metal oxides on the processed surface of the stainless steel sample was increased from 20.4% to 22.0%, 32.9%, 26.6%, and 31.1% after adding 1 mL, 2 mL, 4 mL and 6 mL CP in the cutting fluid with a total volume of 500 mL, respectively. The oxidation reaction between CP and the stainless steel sample resulted in an increase in metal oxides proportion, which prevented the stainless steel sample from corrosion in cutting fluid.