Preparation of energetic polyurethane binders with enhanced properties by nonmigratory reactive monocyclic plasticizers

Simultaneous Enhancement of the Mechanical Properties, Performance and Insensitivity of an Energetic Elastomeric Polyurethane Binder by Kinetically Grafting Reactive Spiranes

A series of robust energetic polyurethane binders was developed by in situ grafting reactive spiranes to achieve the migration-resistant processing aid and compensate for the energy output. The reactive grafting spiranes (RGSs), bearing two highly ring-strained spiranes, were synthesized sequentially to provide a promising ring strain energy up to a maximum value of 290 kJ mol-1. The thermodynamic compatibility of the RGS with uncured glycidyl azido polymer (GAP) was studied quantitatively by analyzing the glass transition temperature of their blendings. The reactivity study of the catalyst-free click reaction with respect to spacer-dependent species was amplified by tracing the extent of the reaction and measuring the activation energy. The faster reactivity of propargyl species was evident from two experimental approaches, which were verified further by theoretical predictions. Interestingly, the energy gap difference in the frontier molecular orbitals agreed well with the difference in activation energy between the two types of spacer-dependent species. The mechanical and thermochemical enhancements of GAP-based polyurethane with RGS were basically gained from those highly ring-strained moieties.

Influence of Fluorinated Polyurethane Binder on the Agglomeration Behaviors of Aluminized Propellants

In this study, fluorinated polyurethane (FPU) was prepared from dialcohol-terminated perfluoropolyether as a soft segment; isophorone diisocyanate (IPDI) as a curing agent; 1,2,4-butanetriol (BT) as a crosslinker; and 1,4-butanediol (BDO) as a chain extender. Fourier transform infrared spectroscopy (FTIR) and ¹H NMR were used to characterize the structure of the FPU. The mechanical properties of the FPUs with different BDO and BT contents were also measured. The tensile strength and breaking elongation of the optimized FPU formula were 3.7 MPa and 412%, respectively. To find out the action mechanism of FPU on Al, FPU/Al was prepared by adding Al directly to FPU. The thermal decomposition of the FPU and FPU/Al was studied and compared by simultaneous differential scanning calorimetry-thermogravimetry-mass spectrometry (DSC-TG-MS). It was found that FPU can enhance the oxidation of Al by altering the oxide-shell properties. The combustion performance of the FPU propellant, compared with the corresponding hydroxyl-terminated polyether (HTPE)-based polyurethane (HPU) propellant, was recorded by a high-speed video camera. The FPU propellants were found to produce smaller agglomerates due to the generation of AlF₃ in the combustion process. These findings show that FPU may be a useful binder for tuning the agglomeration and reducing two-phase flow losses of aluminized propellants.