Influence of COM-peptides/proteins on the properties of flocs formed at different shear rates

Instantaneous and reversible flocculation of Scenedesmus via Chitosan and Xanthan Gum complexation

An instantaneous and reversible flocculation method for Scenedesmus harvesting was developed, based on the complexation of Chitosan (CTS) and Xanthan Gum (XG). Under rapid stirring, Scenedesmus cells formed centimeter-sized flocs within 20 s using binary flocculants of 4 mg/L CTS and 16 mg/L XG. These flocs exhibited a remarkable harvest efficiency exceeding 95 % when filtered through 500-μm-pore-sized sieves. Furthermore, the flocs could be completely disintegrated by using alkaline or NaCl solutions (pH > 11 or NaCl concentration > 1.5 mol/L). Adjusting pH allowed recovery of 50 % CTS and 75 % XG, resulting in microalgae biomass with lower flocculant content and reducing reagent costs. Electrostatic interaction of -COO- of XG and -NH3+ of CTS deduced the formation of polyelectrolyte complexes (PECs), which shrink and wrap the coexisting algal cells to form the flocs under stirring. CTS and XG complexation was instantaneous and reversible, explaining quick flocculation and disintegration.

Preparation of a biobased polyelectrolyte complex from chitosan and sodium carboxymethyl cellulose and its antibacterial characteristics

Using chitosan (CTS) and sodium carboxymethyl cellulose (CMCNa) as raw biobased materials, polyelectrolyte complex (PEC), which is the product of strong electrostatic interaction between two bio-based polyelectrolytes with opposite charges, was attempted to prepare. To enlarge the reactive contact area between CTS and CMCNa, the crosslinked vacuolar structure of PEC was prepared without addition of cross-linked agent. The preparation conditions had a significant impact on the yield of PEC and the bibulous rate of PEC. When pH, mass ratio of CMC-Na-to-CTS, stirring speed and reaction system temperature were 5, 1:2 [(1 wt% CMCNa, 2 wt% CTS), CMC-Na:CTS = 1:1 (v/v)], 800 rpm, 2 min and 25 °C, the yield of PEC reached 71.2 %. The prepared PEC was characterized by XRD and FT-IR. Afterwards, the antibacterial performance of PEC was examined. The prepared PEC had certain bacteriostatic effect on gram-positive and gram-negative bacteria. The bacteriostasis ratios of PEC against Escherichia coli and Staphylococcus aureus were 18.7 % and 31.3 %, respectively. By controlling the combination parameters of the preparation system, an effective strategy was successfully developed for preparation of biobased PEC with bacteriostatic and crosslinked vacuolar structure through simple physical blending without the application of additional crosslinker.

Phenomenological Changes in Lignin Following Polymerization and Its Effects on Flocculating Clay Particles

Cationic kraft lignin (CKL) macromolecules were produced via polymerizing kraft lignin (KL) with [2-(acryloyloxy)ethyl]trimethylammonium chloride (ATAC) or [2-(methacryloyloxy)ethyl]trimethylammonium methyl sulfate (METAM). Despite slightly different charge densities (2.3-2.5 mmol/g) of CKL, lignin-METAM (KL-METAM) had a significantly larger molecular weight and radius of gyration. A correlation was observed between the structure of CKLs and their impacts on the surface hydrophilicity of kaolin particles. In interacting with kaolin particles, KL-METAM generated larger and stronger flocs with looser structures than did KL-ATAC. Compared to ATAC, METAM had one additional methyl substituent on its structure, which provided fundamental evidence on how a small group (i.e., a methyl group) on the structure of a cationic monomer can have a substantial influence on its polymerization with lignin and subsequently on the efficiency of the induced macromolecule as a flocculant in a kaolin suspension system.