Effect of Temperature of Sodium Hypochlorite on Cyclic Fatigue Resistance of Heat-treated Reciprocating Files

Cutting efficiency and corrosion resistance of heat-treated endodontic files after various disinfection protocols

The aim of this study is to evaluate the effect of various disinfection protocols on the cutting efficiency and chemical composition of ProTaper, Twisted File, Twisted File Adaptive, and Hedström files. Four experimental groups (n = 10) were presoaked in either enzymatic solution or 1% sodium hypochlorite for 30 min, followed by either 5 or 15 min of ultrasonic cleaning and then autoclaved. Resin-simulated canals with a single curvature of 38-40° were prepared by each instrument system. Cutting efficiency of each instrument was analyzed by subtracting the final weight from the initial weight of the resin blocks. Chemical compositions were studied by field emission scanning electron microscopy and X-ray energy-dispersive spectrometry. The cutting efficiency of Hedström, ProTaper, and Twisted File instruments decreased compared to their control groups (p < 0.05) whereas it did not change for Twisted File Adaptive. More corrosion was detected with longer ultrasonication time. No difference was observed regarding the pre-soaking media. Disinfection protocols exerted a significant overall effect on the performance of Hedström, ProTaper, and Twisted File instruments. Corrosion, microcracks, and crevices were evident on all tested instruments after disinfection protocols applied. All disinfection protocols, regardless of the pre-soaking media used or the ultrasonic cleaning time applied, have some effect on the cutting efficiency and the surface characteristics of the files.

Influence of sodium hypochlorite on cyclic fatigue resistance of nickel-titanium instruments: A systematic review and meta-analysis of in vitro studies

OBJECTIVE

This systematic review/meta-analysis investigated the influence of NaOCl on cyclic fatigue resistance of endodontic NiTi instruments.

MATERIALS AND METHODS

A systematic search until July 2022 in PubMed/MEDLINE, Embase, Scopus, Web of Science, SciELO, Cochrane Library, and grey literature was conducted. According to the PECOS strategy, only in vitro studies evaluating the effects of NaOCl on the cyclic fatigue resistance of NiTi instruments were eligible. Cyclic fatigue resistance was the primary outcome. A modified Joanna Briggs Institute's Checklist was used for risk of bias assessment.

RESULTS

Of the 2,445 records screened, 37 studies were included. Most studies used simulated canals made of stainless-steel block with severe to moderate curvatures. NaOCl concentration varied from 1-6%, mainly at 37 °C. Regarding fatigue resistance, 23 studies using 1.2% to 6% NaOCl showed a reduction in the resistance compared to the control groups, especially when pre-heated. Four meta-analyses were performed according to the tested NiTi systems. The meta-analyses indicated that the PTU F2 files had higher reduction of fatigue resistance after exposure to 5.25% NaOCl; no differences between NaOCl and no immersion were observed for Reciproc R25, WaveOne 25.08, and WaveOne Gold Primary files. Included studies had low risk of bias.

CONCLUSION

NaOCl appears to reduce cyclic fatigue resistance of certain NiTi files, especially when they are pre-heated, particularly in conventional NiTi files compared to some heat-treated instruments. It is possible that the temperature of the solution may have a greater influence on resistance than NaOCl itself. Important to note that an overall tendency toward no significant influence was observed among various systems.

CLINICAL RELEVANCE

Precautions are necessary when a pre-heated high-concentration NaOCl is used to enhance its properties during root canal preparation, mainly using conventional wire.

Impacts of NaOCl and Irritrol irrigation solutions with/without autoclave sterilisation on the cyclic fatigue resistance of different nickel-titanium files

This research aimed to examine the impact of NaOCl and Irritrol solutions with/without autoclave sterilisation on the cyclic fatigue resistance of ProTaper, WaveOne Gold and Reciproc NiTi files. Seventy files in every group were separated into seven subgroups (n = 10) according to irrigation solutions and sterilisation procedures. The mean and standard deviations of the time to fracture was calculated for each group, and the data statistical analysis was performed (P ≤ 0.05). Significantly higher cyclic fatigue resistance was found in Reciproc files than the other types of files. The differences between the control and other subgroups were found to be statistically insignificant (P > 0.05), except for subgroups 5 and 7 (P ≤ 0.05). Immersing NiTi files in NaOCl or Irritrol with sterilisation for three times considerably reduced the cyclic fatigue resistance of these files. Reciproc files exhibited the highest cyclic fatigue resistance in comparison with ProTaper and WaveOne Gold files.

Influence of Sodium Hypochlorite and Chlorhexidine on the Dynamic Cyclic Fatigue Resistance of XP Endo Shaper Instruments

Objective  This study evaluated the dynamic cyclic fatigue resistance of the XP-Endo Shaper (XPS), associated with chlorhexidine digluconate (CHX) or sodium hypochlorite (NaOCl) in two different formulations: gel (G) or liquid (L).

Materials and Methods  Sixty XPS were used in an artificial stainless-steel canal, and the files were fully immersed in the irrigating solution throughout the experiment until the fracture. The files were divided into six groups ( n  = 10) based on the irrigation solution used: NaOCl(L), NaOCl(G), CHX(L), CHX(G), natrosol gel (NAT) (control), and lubricating oil (LO) (control). The artificial canal was manufactured 1.5 mm wide, 20 mm long, and, 3.5 mm deep with a straight cervical segment measuring 14.29 mm; an apical segment of 4.71 mm with 3 mm radius; and 90 degrees of curvature apical 1 mm long straight segment. Resistance to cyclic fatigue was determined by recording the number of cycles to fracture (NCF).

Results  The CHX(G), CHX(L), and OIL (LO) groups showed no significant difference between them and presented longer time to fracture ( p  > 0.05). NaOCl(L) shows the lowest NCF without significant differences between NaOCl(G) and NAT. The NCF of the NaOCl(G) was statistically similar to the CHX(L) and statistically lower than the CHX(G) and OIL groups. NAT did not present a statistical difference of the NaOCl(L), NaOCl(G), and presented a significantly lower NCF than the CHX(G) ( p  < 0.01).

Conclusion  The use of CHX(G) resulted in increased cyclic fatigue resistance of the XPS instruments compared to NaOCl or LO.

A critical analysis of research methods and experimental models to study the physical properties of NiTi instruments and their fracture characteristics

The aim of this review is to provide a critical overview of the physical properties (surface hardness, cutting efficiency, bending properties, flexibility and cyclic fatigue resistance) of NiTi instruments. Frequently used experimental models regarding these aspects will be presented and discussed with regard to their strengths and weaknesses. For all these aspects, a plethora of experimental models have been described. Based on a critical appraisal and especially taking the appropriate translation of experimental findings to clinical endodontics into account, suggestions for future research based on clearly defined and valid experimental methodologies will be provided. Up to now, very few attempts have been made to assess which particular physical properties of NiTi instruments exert an impact on the clinical outcome of root canal treatment. Departure from merely focusing on physical properties and fracture characteristics towards more biological aspects in terms of treatment outcome is essential.

Comparison of Cyclic Fatigue Resistance of Heat-Treated Nickel-Titanium Reciprocating Instruments at the Intracanal Temperature

Background/Aim: The aim of the present study was to compare the cyclic fatigue resistance of NiTi files running with reciprocal motion and having different characteristics (RPC Blue, WOG, EndoArt Wise Reciproc Gold, EndoArt Wise Reciproc Blue) at the intracanal temperature (35°C) by using NaOCl irrigation solution.

Material and Methods: Totally 60 WaveOne GOLD (Dentsply-Sirona, Ballaigues, Switzerland), Reciproc Blue (VDW, Munich, Germany), EndoArt Wise Reciproc Gold, and EndoArt Wise Blue (Inci Dental Productions Co, Istanbul, Turkey) (n= 15) files were used. Each of the rotary files were tested at the intracanal temperature (35°C) using a dynamic model in a stainless-steel artificial canal with an inner diameter of 1.5 mm, 60° angle of curvature, and 2mm radius of curvature until fracture occurred. The device automatically stopped at the moment of fracture and the number of cycles to the fracture was calculated as per second. The lengths of fractured parts were measured using a digital microcaliper. The One-Way Analysis of Variance (ANOVA) and Tukey’s post-hoc tests were used for intergroup comparisons.

Results: In 2 mm Radius of curvature, the EndoArt Wise Reciproc Blue group had a significantly higher time to fracture followed by the EndoArt Wise Reciproc Gold, Resiproc Blue, WaveOne Gold. No significant difference was found between EndoArt Wise Reciproc Gold and Resiproc Blue groups (P>0.05). Among the groups, there was no statistically significant difference in the lengths of fractured parts of the instruments (P> 0.05).

Conclusions: EndoArt Wise Reciproc Blue files exhibited significantly higher cyclic fatigue resistance compared with other files tested in a 2-mm radius of curvature and a 60° angle in an artificial canal at the intracanal temperature.

Body temperature fatigue behaviour of reciprocating and rotary glide path instruments in sodium hypochlorite solutions alone or combined with etidronate

The aim of the study was to compare cyclic fatigue (CF) resistance of reciprocating and rotary glide path instruments in the presence of irrigation solutions at body temperature. CF resistance of 100 instruments (50 ProGlider and 50 WaveOne Gold Glider) was tested in sodium hypochlorite solutions alone (NaOCl) or in combination with etidronate (NaOCl/HEBP). The CF platform with a simulated canal (curvature = 60°/radius = 3 mm) was submerged in a temperature-controlled bath with the solutions kept at 37 ± 1°C controlled by a precision mercury glass thermometer. Instruments were actioned following manufacturer guidelines, and time to failure was recorded and compared among groups with Weibull analysis. Reciprocating glide path preparation instruments were more resistant to CF than rotary instruments in both irrigation solutions. The irrigation solution did not affect the mean life of ProGlider, but reciprocating instruments lasted significantly longer used in presence of NaOCl compared to NaOCl/HEBP.

The Effect of Taper and Apical Diameter on the Cyclic Fatigue Resistance of Rotary Endodontic Files Using an Experimental Electronic Device

The aim of this study was to analyze the effect of the taper and apical diameter of nickel–titanium (NiTi) endodontic rotary files on the dynamic cyclic fatigue resistance. A total of 50 unused conventional NiTi wire alloy endodontic rotary instruments were used in this study. All NiTi endodontic rotary files were submitted to a custom-made dynamic cyclic fatigue device until fracture occurred. The time to failure, the number of cycles to failure, the number of pecking movements, and the length of the fractured file tip were analyzed using the analysis of variance (ANOVA) test. In addition, the Weibull characteristic strength and Weibull modulus were also calculated. The paired t-test revealed statistically significant differences between the time to failure, number of cycles to failure, and number of cycles of in-and-out movement of both the apical diameter (p ˂ 0.001) and the taper (p ˂ 0.001) of NiTi endodontic rotary files; however, the results did not show statistically significant differences between the mean length of the fractured files regarding the apical diameter (p = 0.344) and taper study groups (p = 0.344). Increased apical diameter and taper of NiTi endodontic rotary files decreased their dynamic resistance to cyclic fatigue.

Effect of canal curvature location on the cyclic fatigue resistance of reciprocating files

OBJECTIVES

To determine the effect of the location of the canal curvature on the fatigue resistance of WaveOne (WO), WaveOne Gold (WOG), Reciproc (Rec), and Reciproc Blue (RecB) files, and to examine the phase transformation behaviors of the reciprocating file systems.

MATERIAL AND METHODS

The instruments were subjected to fatigue testing in five artificial canals with a curvature of 60° angle and a 3-mm radius. The location of the curvature was unique for each canal. Each file was inserted 16 mm into the canal and operated until fracture occurred. The time to fracture was recorded and the length of the fragment was measured. Differential scanning calorimetry was used to characterize the thermal behavior of the files. The number of cycles to failure was analyzed using two-way analysis of variance and the post hoc Tukey test. The Kruskal-Wallis test was used to compare the mean fragment lengths between groups.

RESULTS

The instruments had significantly lower fatigue resistance in canals with curvatures in the middle and coronal canals compared with those with apical curvatures (p < 0.05). At all tested curvature locations, RecB had superior fatigue resistance compared with WO and Rec (p < 0.05). There were no significant differences between WOG and Rec in canals with curvatures in the middle and coronal canals. The DSC thermograms for RecB exhibit a single exothermic peak during cooling but double endothermic peaks during heating indicating that a two-step phase transformation from martensite to R-phase to austenite takes place.

CONCLUSIONS

The reciprocating instruments experience decreased cyclic fatigue resistance when operated in canals with coronal- and middle-third curvatures when compared with curvatures in the apical-third. Instrumenting coronally positioned curvatures with reciprocating files needs to be performed with caution.

CLINICAL RELEVANCE

The location of the root canal's curvature influences the fracture resistance of rotary files that are used with reciprocating movements. Therefore, caution needs to be exercised when using reciprocating instruments in canals with coronal or middle curvatures.