In vitro study of bioactivity of homemade tissue-engineered periosteum

Enhanced Silk Fibroin/Sericin Composite Film: Preparation, Mechanical Properties and Mineralization Activity

The periosteum plays an important role in bone formation and reconstruction. One of the reasons for the high failure rate of bone transplantation is the absence of the periosteum. Silk fibroin (SF) and silk sericin (SS) have excellent biocompatibility and physicochemical properties, which have amazing application prospects in bone tissue engineering, but lacked mechanical properties. We developed a series of SF/SS composite films with improved mechanical properties using boiling water degumming, which caused little damage to SF molecular chains to retain larger molecules. The Fourier transform infrared spectroscopy and X-ray diffraction results showed that there were more β-sheets in SF/SS films than in Na₂CO₃ degummed SF film, resulting in significantly improved breaking strength and toughness of the composite films, which were increased by approximately 1.3 and 1.7 times, respectively. The mineralization results showed that the hydroxyapatite (HAp) deposition rate on SF/SS composite films was faster than that on SF film. The SF/SS composite films effectively regulated the nucleation, growth and aggregation of HAp-like minerals, and the presence of SS accelerated the early mineralization of SF-based materials. These composite films may be promising biomaterials in the repair and regeneration of periosteum.

Repair of long bone defects of large size using a tissue-engineered periosteum in a rabbit model

Tissue engineering is a promising approach for bone regeneration. In this study, we aimed to investigate whether tissue engineered periosteum (TEP), which was fabricated by combining osteogenically-induced mesenchymal stem cells (MSCs) with porcine small intestinal submucosa (SIS), could restore long bone defects of large size in rabbits. Twenty-four adult New Zealand white rabbits (NZWRs) were used in the experiments. Long bone defects of large size (30 mm-50 mm; average, 40 mm) were established on both sides of NZWRs' radii. The defects were treated with TEP (Group A), allogeneic deproteinized bone (DPB, Group B), TEP combined with DPB (Group C), and pure SIS (Group D). The healing outcome was evaluated by radiography and histological examination at 4, 8, and 12 weeks post-treatment. The radiographical findings showed that bone defects of large size were all repaired in Groups A, B and C within 12 weeks, whereas Group D (pure SIS group) failed to result in defect healing at 4, 8, and 12 weeks. Although there was some new bone regeneration connecting the allografts and bone ends, as observed under radiographical and histological observations, bone defects of large sizes were restored primarily by structurally allografted DPB within 12 weeks. The TEP groups (Groups A and C) showed partial or total bone regeneration upon histological inspection. Based on 12-week histological examinations, significantly more bone was formed in Group A than Group C (P < 0.05), and both groups formed significantly more bone than in Groups B and D. The results indicated that long bone defects of a large size could be restored by TEP or TEP combined with the DPB scaffold, and such materials provide an alternative approach to resolving pathological bone defects in clinical settings.

Periosteal Tissue Engineering: Current Developments and Perspectives

Periosteum, a highly vascularized bilayer connective tissue membrane plays an indispensable role in the repair and regeneration of bone defects. It is involved in blood supply and delivery of progenitor cells and bioactive molecules in the defect area. However, sources of natural periosteum are limited, therefore, there is a need to develop tissue-engineered periosteum (TEP) mimicking the composition, structure, and function of natural periosteum. This review explores TEP construction strategies from the following perspectives: i) different materials for constructing TEP scaffolds; ii) mechanical properties and surface topography in TEP; iii) cell-based strategies for TEP construction; and iv) TEP combined with growth factors. In addition, current challenges and future perspectives for development of TEP are discussed.

Irregular Bone Defect Repair Using Tissue-Engineered Periosteum in a Rabbit Model

Background:

In previous studies, we succeeded in repairing a long bone defect with tissue-engineered periosteum (TEP), fabricated by incorporating rabbit mesenchymal stem cells with small intestinal submucosa. In this study, we investigated the feasibility of allogeneic irregular bone defect repair using TEP.

Methods:

We performed a subtotal resection of the scapula in 36 rabbits to establish a large irregular bone defect model. The rabbits were then randomly divided into three groups (n = 12 per group) and the defects were treated with TEP (Group 1), allogeneic deproteinized bone (DPB) (Group 2) or a hybrid of TEP and DPB (Group 3). At 4, 8, and 12 weeks after surgery, the rabbits were sacrificed, and the implants were harvested. X-ray radiographic and histological examinations were performed to detect bone healing. Ink-formaldehyde perfusion was introduced to qualitatively analyze vascularization in TEP engineered new bone.

Results:

The repair of scapular defects was diverse in all groups, shown by radiographic and histological tests. The radiographic scores in Group 1 and Group 3 were significantly higher than Group 2 at 8 and 12 weeks (p < 0.05). Histological scores further proved that Group 1 had significantly greater new bone formation compared to Group 3 (p < 0.05), while Group 2 had the lowest osteogenesis at all time-points (p < 0.001). Ink-formaldehyde perfusion revealed aboundant microvessels in TEP engineered new bone.

Conclusion:

We conclude that TEP is promising for the repair of large irregular bone defects. As a 3D scaffold, DPB could provide mechanical support and a shaping guide when combined with TEP. TEP engineered new bone has aboundant microvessels.

Decellularized Periosteum-Covered Chitosan Globule Composite for Bone Regeneration in Rabbit Femur Condyle Bone Defects

Critical-sized bone defects are incapable of self-healing and are commonly seen in clinical practice. The authors explore a new treatment for this, decellularized periosteum is applied to chitosan globules (chitosan-DP globules) as a hybrid material. The efficacy of chitosan-DP globules on rabbit femoral condyle bone defects is assessed with biocompatibility, biomechanics, and osteogenic efficiency measurements, and compared with the results of chitosan globules and empty control. No difference in cytotoxicity is observed among chitosan-DP globules, chitosan globules, and the empty control. Chitosan-DP globules possesse a better surface for cell adhesion than did chitosan globules. Chitosan-DP globules demonstrate superior efficiency for osteogenesis in the defect area compared to chitosan globules as per microcomputed tomography examination and push-out testing, with relatively minor histological differences. Both chitosan globule groups show more satisfactory results than those for the empty control. The results implicate chitosan-DP globules as a promising solution for bone defects.

Engineering biomimetic periosteum with β-TCP scaffolds to promote bone formation in calvarial defects of rats

Background

There is a critical need for the management of large bone defects. The purpose of this study was to engineer a biomimetic periosteum and to combine this with a macroporous β-tricalcium phosphate (β-TCP) scaffold for bone tissue regeneration.

Methods

Rat bone marrow-derived mesenchymal stem cells (rBMSCs) were harvested and cultured in different culture media to form undifferentiated rBMSC sheets (undifferentiated medium (UM)) and osteogenic cell sheets (osteogenic medium (OM)). Simultaneously, rBMSCs were differentiated to induced endothelial-like cells (iECs), and the iECs were further cultured on a UM to form a vascularized cell sheet. At the same time, flow cytometry was used to detect the conversion rates of rBMSCs to iECs. The pre-vascularized cell sheet (iECs/UM) and the osteogenic cell sheet (OM) were stacked together to form a biomimetic periosteum with two distinct layers, which mimicked the fibrous layer and cambium layer of native periosteum. The biomimetic periostea were wrapped onto porous β-TCP scaffolds (BP/β-TCP) and implanted in the calvarial bone defects of rats. As controls, autologous periostea with β-TCP (AP/β-TCP) and β-TCP alone were implanted in the calvarial defects of rats, with a no implantation group as another control. At 2, 4, and 8 weeks post-surgery, implants were retrieved and X-ray, microcomputed tomography (micro-CT), histology, and immunohistochemistry staining analyses were performed.

Results

Flow cytometry results showed that rBMSCs were partially differentiated into iECs with a 35.1% conversion rate in terms of CD31. There were still 20.97% rBMSCs expressing CD90. Scanning electron microscopy (SEM) results indicated that cells from the wrapped cell sheet on the β-TCP scaffold apparently migrated into the pores of the β-TCP scaffold. The histology and immunohistochemistry staining results from in vivo implantation indicated that the BP/β-TCP and AP/β-TCP groups promoted the formation of blood vessels and new bone tissues in the bone defects more than the other two control groups. In addition, micro-CT showed that more new bone tissue formed in the BP/β-TCP and AP/β-TCP groups than the other groups.

Conclusions

Inducing rBMSCs to iECs could be a good strategy to obtain an endothelial cell source for prevascularization. Our findings indicate that the biomimetic periosteum with porous β-TCP scaffold has a similar ability to promote osteogenesis and angiogenesis in vivo compared to the autologous periosteum. This function could result from the double layers of biomimetic periosteum. The prevascularized cell sheet served a mimetic fibrous layer and the osteogenic cell sheet served a cambium layer of native periosteum. The biomimetic periosteum with a porous ceramic scaffold provides a new promising method for bone healing.

In vivo investigation of tissue-engineered periosteum for the repair of allogeneic critical size bone defects in rabbits

Aim: The aim of the study was to evaluate the efficacy of tissue-engineered periosteum (TEP) in repairing allogenic bone defects in the long term. Materials & methods: TEP was biofabricated with osteoinduced rabbit bone marrow mesenchymal stem cells and porcine small intestinal submucosa (SIS). A total of 24 critical sized defects were created bilaterally in radii of 12 New Zealand White rabbits. TEP/SIS was implanted into the defect site. Bone defect repair was evaluated with radiographic and histological examination at 4, 8 and 12 weeks. Results: Bone defects were structurally reconstructed in the TEP group with mature cortical bone and medullary canals, however this was not observed in the SIS group at 12 weeks. Conclusion: The TEP approach can effectively restore allogenic critical sized defects, and achieve maturity of long-bone structure in 12 weeks in rabbit models.

Combined delivery of FGF-2, TGF-β1, and adipose-derived stem cells from an engineered periosteum to a critical-sized mouse femur defect

Critical-sized long bone defects suffer from complications including impaired healing and non-union due to substandard healing and integration of devitalized bone allograft. Removal of the periosteum contributes to the limited healing of bone allografts. Restoring a periosteum on bone allografts may provide improved allograft healing and integration. This article reports a polysaccharide-based tissue engineered periosteum that delivers basic fibroblast growth factor (FGF-2), transforming growth factor-β1 (TGF-β1), and adipose-derived mesenchymal stem cells (ASCs) to a critical-sized mouse femur defect. The tissue engineered periosteum was evaluated for improving bone allograft healing and incorporation by locally delivering FGF-2, TGF-β1, and supporting ASCs transplantation. ASCs were successfully delivered and longitudinally tracked at the defect site for at least 7 days post operation with delivered FGF-2 and TGF-β1 showing a mitogenic effect on the ASCs. At 6 weeks post implantation, data showed a non-significant increase in normalized bone callus volume. However, union ratio analysis showed a significant inhibition in allograft incorporation, confirmed by histological analysis, due to loosening of the nanofiber coating from the allograft surface. Ultimately, this investigation shows our tissue engineered periosteum can deliver FGF-2, TGF-β1, and ASCs to a mouse critical-sized femur defect and further optimization may yield improved bone allograft healing. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 900-911, 2017.