Structure formation in polymer solutions

Exploring the Diverse Morphology of Porous Poly(Lactic Acid) Fibers for Developing Long-Term Controlled Antibiotic Delivery Systems

In this study, we aimed to explore the morphologies of porous poly(lactic acid) (PLA) fibers through liquid−liquid phase separation, and investigate the relationship among pore formation, physical properties, and antibacterial activities of the fibers for identifying their potential as drug delivery carriers. Antibacterial activities of gentamicin-, kanamycin-, and amikacin-loaded PLA fibers against E. coli and S. epidermidis were evaluated. The antibacterial activity of drugs against E. coli showed the following profile: gentamicin > amikacin > kanamycin; however, S. epidermidis growth was almost completely inhibited immediately after the administration of all three drugs. The efficiency of gentamicin can be attributed to the electrostatic interactions between the positively and negatively charged antibiotic and bacterial cell membrane, respectively. Furthermore, gentamicin-loaded porous PLA fibers were evaluated as drug delivery systems. The cumulative amount of gentamicin in porous PLA nanofibers was considerably higher than that in other PLA fibers for 168 h, followed by 7:3 PLA > 6:4 PLA > 5:5 PLA > non-porous PLA. The 7:3 PLA fibers were projected to be ideal drug carrier candidates for controlled antibiotic release in delivery systems owing to their interconnected internal structure and the largest surface area (55.61 m2 g−1), pore size (42.19 nm), and pore volume (12.78 cm3 g−1).

Preparation of Poly(l-lactic acid) Scaffolds by Thermally Induced Phase Separation: Role of Thermal History

Poly-L-Lactic Acid (PLLA) scaffolds for tissue engineering were prepared via thermally induced phase separation of a ternary system PLLA/dioxane/tetrahydrofurane. An extension to solution of a previously developed method for solidification from the melt was adopted, the technique being based on a Continuous Cooling Transformation (CCT) approach, consisting in recording the thermal history of rapidly cooled samples and analysing the resulting morphology. Different foams were produced by changing the thermal history, the dioxane to THF ratio (50/50, 70/30, 90/10 v/v) and the polymer concentration (2, 2.5, 4 ° wt) in the starting ternary solution. Pore size, porosity, melting and crystallization behavior were studied, together with a morphological and kinetic analysis of the foams produced. A large variety of morphologies was achieved, the largest pore size (20 μm) was achieved at the highest polymer concentration (4 ° wt) and the lowest dioxane concentration (50/50 dioxane/THF v/v), whereas the largest porosity (90 °) was attained at the highest dioxane concentration (90/10). The average pore size is related to cooling rate, with a 1/3 power law exponent at low polymer concentrations and low dioxane content for thermal histories driven by low undercoolings. At high undercoolings, the growth of the demixed domains significantly departs from the diffusive-like regime.

Surface morphology of electrospun PLA fibers: mechanisms of pore formation

Interaction of relative humidity with solvent(s) is relatively more important in obtaining surface pores than solvent volatility and phase separation.

Novel fabricated matrix via electrospinning for tissue engineering

Electric field-driven fiber formation (electrospinning) is developing into a practical means for preparing novel porous filament with unusual structures and affordable mechanical properties. Polycaprolactone (PCL) was dissolved in solvent mixtures of methylene chloride/N,N-dimethyl formamide with ratios of 100/0, 75/25, and 50/50 (v/v) for electrospinning. The filament was formed by coagulation of the spinning solution following the well-known principle of phase separation in polymer solutions valid in other wet shaping processes. A strand of electrospun porous filament consisted of fibers ranging from 0.5 to 12 microm in diameter. To evaluate the feasibility of three-dimensional fabric as scaffold matrices, the plain weave, which is the simplest of the weaves and the most common, was prepared with porous PCL filament. The growth characteristics of MCF-7 mammary carcinoma cells in the woven fabrics showed the important role of matrix microstructure in proliferation. This study has shown that woven fabrics, consisting of porous filaments via electrospinning, may be suitable candidates as tissue engineering scaffolds.