Evaluation of post-treatment solutions for clinical use with the calcium phosphate precipitation method

Duration of dentin tubule occlusion by the calcium phosphate precipitation method: An in vivo study in beagle dogs

The aim of the present study was to assess the duration of dentin tubule occlusion by the calcium phosphate precipitation (CPP) method in the vital teeth of beagle dogs. Vital teeth were treated using the CPP method, potassium oxalate, or a bonding agent (Liner bond II) after cavity preparation and acid etching. The dentin tubules of all groups, except for the bonding agent, opened more widely with time in the absence of plaque control. Dentin tubules treated with the CPP method were open and no precipitate remained in the absence of plaque control. Differences were observed in dentin tubule occlusion when plaque control was achieved by daily tooth brushing. The majority of dentin tubules were occluded with an apatitic precipitate seven days after the CPP method with plaque control. The present results demonstrated that the CPP method is useful with proper plaque control.

Effects of calcium phosphate precipitation method on acid resistance to apatite powder and bovine tooth

The aims of this study were to evaluate the effects of CPP method on the crystallinity of apatite powder and on the acid resistance of bovine enamel. Crystallinity degrees of apatite powder before and after CPP treatment were measured by powder X-ray diffraction analysis. Polished bovine enamel specimens treated with CPP method or NaF were immersed in a lactic acid solution for up to five days. The demineralized depth of enamel was measured with a surface roughness analyzer. XRD peaks became sharper after the CPP treatment, indicating an increased crystallinity of the apatite powder. The demineralized depth of bovine enamel treated with CPP method was shallower than that of enamel treated with NaF. Results of this study revealed that the CPP method increased the crystallinity of apatite powder and the acid resistance of enamel. Therefore, the CPP method would be useful not only for treating dentin hypersensitivity, but also for the prevention of dental caries.

In Vitro Study of Dentinal Tubule Occlusion with Sol-gel DP-bioglass for Treatment of Dentin Hypersensitivity

DP-bioglass paste has been demonstrated to produce 60 microm of sealing depth on exposed dentinal tubules. However, the occlusive effect depended on a continuous placement of DP-bioglass paste on dentinal surface for three days. In a bid to fabricate highly reactive DP-bioglass particles, a sol-gel method was used together with HNO3, NaOH, and H3PO4 as catalysts. As a result, the application time of DP-bioglass paste was significantly reduced to 10 minutes. Percentage of tubular occlusion with DP-bioglass was 53.2-65.4%, while One Coat Bond and Seal & Protect yielded 51.3% and 41.2% respectively. Further, the average depth of tubular occlusion with DP-bioglass was 55.8-62.7 microm, while One Coat Bond and Seal & Protect produced 40.8 microm and 32.5 microm respectively. In conclusion, the best sealing performance of tubular occlusion was rendered by DP-bioglass catalyzed with HNO3. Its performance was significantly better than Seal & Protect, and was considered to exhibit the greatest potential in treating dentin hypersensitivity.