Effect of Pore Structures on 1,4-Butynediol Hydrogenation over Mesoporous Ni/Al2O3-SiO2 Catalysts

Investigation of Ni-Cu-acid multifunctional synergism in NiCu-phyllosilicate catalysts toward the 1,4-butynediol hydrogenation to 1,4-butanediol

We studied the Ni-Cu-acid multifunctional synergism in NiCu-phyllosilicate catalysts toward 1,4-butynediol hydrogenation to 1,4-butanediol by varying the reduction temperature, which can activate different bimetal and support interactions. Compared with a monometallic Ni phyllosilicate (phy), which only showed one type of metal species when reduced at ∼750 °C, there are three types of metal species for the bimetallic Ni-Cu-phyllosilicate derived catalysts, namely Cuphy, differentiated Ni, and Niphy. Thorough structure-activity/selectivity correlation investigations showed that, although the Ni9Cu1-P catalyst matrix can produce tiny amounts of differentiated Ni0 species under the induction of reduced Cu0 at R250 condition, it could not form Ni-Cu bimetallic interactions for the collaborative hydrogenation of 1,4-butynediol, and the product stays in the semi hydrogenated state. When the reduction temperature is raised to 500 °C, stable Ni-Cu alloy active sites exist, accompanied by the strong metal support interaction and metal acid effect derived from the intimate contact between the extracted metal sites and the surviving functional phyllosilicate support; these functionalities yield a supreme hydrogenation performance of the R500 sample with a 1,4-butanediol yield larger than 91.2%.

Unveiling the mechanism of methylcellulose-templated synthesis of Al2O3 microspheres with organic solvents as swelling agents in microchannel

Herein, we report a systematic investigation of the preparation of large-pore-volume Al₂O₃ microspheres using a complex synthesis system with methylcellulose (MC) as the template and gelation initiator and organic solvents as the swelling agent and carrier medium under the flow characteristics of a coaxial microchannel. The adsorption of MC micelles on boehmite colloidal nanoparticles (NPs) was proven and determined by interfacial tension measurements, dynamic light scattering, and cryogenic transmission electron microscopy. Isothermal titration calorimetry demonstrated that the adsorption process was caused by nonspecific hydrophobicity; one binding site was involved, and the affinity constant was 1060 M^-1. When the MC:NPs mass ratio exceeded 0.1, the template-NP bridged each other to form large aggregates, thereby forming large mesopores and enhancing the gelation speed. Alkanes, alcohols, and amines were applied to further enhance the porosity, and the swelling capacities were investigated experimentally and theoretically. Amines were efficient swelling agents owing to their excellent ability to swell MC micelles and insert into the acid colloid network. The coaxial microchannel was subjected to molding; this process significantly influenced the morphology and textural properties owing to the internal circulation during droplet formation. When trihexylamine with suitable steric hindrance, alkalinity, and polarity was used as the swelling agent, the microspheres exhibited an optimal specific surface area of 403 m²/g and a pore volume of 1.85 cm³/g.