Mechanism of Heterogeneous Bubble Nucleation in Polymer Blend Foaming

Insights into heterogeneous surface induced bubble nucleation mechanisms in cellulose reinforced polylactic acid foams

As the most abundant natural homo-polymer, cellulose has the potential to enhance polymer properties reducing the cost of raw materials. In this work, the carboxylate cellulose nanofiber (CNF-C) was selected to modify polylactic acid (PLA) foams, and the density functional theory was constructed to help analyze the foaming mechanism quantitatively. The theoretical results showed that the ordered structure, the carboxyl and the hydroxyl of CNF-C were more conducive to providing much stronger CO2 adsorption for bubble nucleation, where the predicted critical bubble size decreased and the cell density increased with the addition of CNF-C. The experimental results revealed that the CNF-C promoted the rheological properties and crystallization behaviors of PLA samples, the PLA/CNF-C foams were characterized with uniform structures, the average cell size decreased from 21.39 μm to 0.19 μm, and the cell number density increased from 2.65×1010cell/cm3 to 2.30×1014cell/cm3. Those improvements resulted in an increase of 394.0 % for the compressive strength of the prepared foams. Generally, the high-performance PLA/CNF-C foams were fabricated successfully without compromising the properties of bio-based and biodegradable, the foaming mechanism was analyzed combining theoretical results with experimental data, and it was believed to provide a guide for cellulose reinforcing biodegradable polymer materials.

Foaming of PCL-Based Composites Using scCO2: Structure and Physical Properties

The process of foaming poly(caprolactone)-based composites using supercritical carbon dioxide was analyzed. The impact of the conditions of the solid-foam production process on the process efficiency and properties of porous structures was investigated. The novel application of various types of porogens—hydroxyapatite, nanocellulose, carboxymethylcellulose, and graphene oxide—was tested in order to modify the properties and improve the quality of solid foams, increasing their usefulness in specialized practical applications. The study showed a significant influence of the foaming process conditions on the properties of solid foams. The optimal process parameters were determined to be pressure 18 MPa, temperature 70 °C, and time 1 h in order to obtain structures with appropriate properties for applications in biomedical engineering, and the most promising material for their production was selected: a composite containing 5% hydroxyapatite or 0.2% graphene oxide.