Achieving excellent superplasticity of Mg-7Zn-5Gd-0.6Zr alloy at low temperature regime

Ultrafine-Grained Microstructures of Al-Cu Alloys with Hypoeutectic and Hypereutectic Composition Produced by Extrusion Combined with Reversible Torsion

In this study, binary as-cast Al–Cu alloys: Al25Cu (Al–25%Cu) and Al45Cu (Al–45%Cu) (in wt%) were severely plastically deformed by extrusion combined with a reversible torsion (KoBo) method to produce an ultrafine-grained structure (UFG). The binary Al–Cu alloys consist of α-Al and intermetallic Al2Cu phases. The morphology and volume fraction of α-Al and Al2Cu phases depend on the Cu content. The KoBo process was carried out using extrusion ratios of λ = 30 and λ = 98. The effect of phase refinement has been studied by means of scanning electron microscopy with electron backscattering diffraction and scanning transmission electron microscopy. The mechanical properties were assessed using compression tests. Detailed microstructural analysis shows that after the KoBo process, a large number fraction of high-angle boundaries (HABs) and a very fine grain structure (~2–4 μm) in both phases are created. An increase of λ ratio during the KoBo processing leads to a decrease in average grain size of α-Al and Al2Cu phases and an increase in fraction of HABs. UFG microstructure and high fraction of HABs provide the grain boundary sliding mechanism during KoBo deformation. UFG microstructure contributes to the enhanced mechanical properties. Compressive strength (Rc) of Al25Cu alloy increases from 172 to 340 MPa with an increase of λ. Compressive strain (Sc) for Al25Cu alloy increased from 35 to 67% with an increase of λ. High fraction of intermetallic phase in Al45Cu alloy was responsible for room temperature strengthening of alloy and low compressive strain. The deformed Al45Cu alloy with λ = 30 showed that Rc is 194 MPa and Sc is equal to 10%.

Research on AZ80 + 0.4%Ce (wt %) Ultra-Thin-Walled Tubes of Magnesium Alloys: The Forming Process, Microstructure Evolution and Mechanical Properties

Ultra-thin-walled tubes of magnesium alloys have received more and more attention in producing precision components for medical devices. Therefore, thin-walled tubes with high quality are desperately needed. In this study, the process of multi-pass variable wall thickness extrusion was carried out on an AZ80 + 0.4%Ce Mg alloy with up to five passes—one-pass backward extrusion and four-pass extension—to fabricate the seamless thin-walled tube with an inside diameter of 6.0 mm and a wall thickness of 0.6 mm. The average grain size decreased from 46.3 μm to 8.9 μm at the appropriate deformation temperature of 350 °C with the punch speed of 0.1 mm/s. X-ray diffraction (XRD), optical microscope (OM), scanning electron microscopy (SEM), and the Vickers hardness (HV) tester were utilized to study the phases, microstructure, and hardness evolution. It can be observed that low deformation temperatures (240 °C and 270 °C) and low strain (1 pass extrusion and 1 pass extension) lead to twins that occupy the grains to coordinate deformation, and a slip system was activated with the accumulation of strain. The results of the Vickers hardness test showed that twinning, precipitation of second phases, twinning dynamic recrystallization (TDRX), and work hardening were combined to change the hardness of tubes at 240 °C and 270 °C. The hardness reached 93 HV after the third pass extension without annealing at 350 °C.