Improving Dispersion and Barrier Properties of Polyketone/Graphene Nanoplatelet Composites via Noncovalent Functionalization Using Aminopyrene

A series of polyketone (PK) nanocomposite films with varying content of noncovalently functionalized graphene nanoplatelet with 1-aminopyrene (GNP/APy) is prepared by solution blending with a solvent of hexafluoro-2-propanol. GNP/APy, prepared by a facile method, can effectively induce specific interaction such as hydrogen bonding between the amine functional group of GNP/APy and the carbonyl functional group of the PK matrix. With comparison of GNP and GNP/Py as reference materials, intensive investigation on filler-matrix interaction is achieved. In addition, the dispersion state of the functionalized GNP (f-GNPs; GNP/Py and GNP/APy) in the PK matrix is analyzed by three-dimensional nondestructive X-ray microcomputed tomography, and the increased dispersion state of those fillers results in significant improvement in the water vapor transmission rate (WVTR). The enhancement in WVTR of the PK/GNP/APy nanocomposite film at 1 wt % loading of filler leads to a barrier performance approximately 2 times larger compared to that of PK/GNP nanocomposite film and an approximately 92% reduction in WVTR compared to the case of pristine PK film. We expect that this facile method of graphene functionalization to enhance graphene dispersibility as well as interfacial interaction with the polymer matrix will be widely utilized to expand the potential of graphene materials to barrier film applications.

Enhanced molecular level dispersion and interface bonding at low loading of modified graphene oxide to fabricate super nylon 12 composites

Development of advanced graphene based polymer composites is still confronted with severe challenges due to its poor dispersion caused by restacking, weak interface bonding, and incompatibility with polymer matrices which suppress exertion of the actual potential of graphene sheets in composites. Here, we have demonstrated an efficient chemical modification process with polyethylenimine (PEI) to functionalize graphene oxide which can overcome the above-mentioned drawbacks and also can remarkably increase the overall strength of the nylon 12 composites even at very low graphene loading. Chemical modification was analyzed by various surface characterizations including X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, and X-ray diffraction. Addition of only 0.25 and 0.35 wt % modified GO showed 37% and 54% improvement in tensile strength and 65% and 74% in Young's modulus, respectively, compared with that of the neat polymer. The dynamic mechanical analysis showed ∼39% and 63% increment in storage modulus of the nanocomposites. Moreover, the nanocomposites exhibited significantly high thermal stability (∼15 °C increment by only 0.35 wt %) as compared to neat polymer. Furthermore, the composites rendered outstanding resistance against various chemicals.

Facile preparation of highly electrically conductive films of silver nanoparticles finely dispersed in polyisobutylene-b-poly(oxyethylene)-b-polyisobutylene triblock copolymers and graphene oxide hybrid surfactants

The melted morphologies revealed that the AgNPs possessed mobility, and melted on the film surface, giving a high electrical conductivity of 5.2 × 10⁻² Ω sq⁻¹ when heat-treated at 350 °C.