Ce-Doped Ni-S nanosheets on Ni foam supported NiMoO4 micropillars: fast electrodeposition, improved electrocatalytic activity and ultralong durability for the oxygen evolution reaction in various electrolytes

Ce Hydroxide-Interfaced NiFe Sulfide Electrocatalyst with Improved Performance for the Oxygen Evolution Reaction

The development of electrochemically inexpensive, durable, and active electrocatalysts for the oxygen evolution reaction (OER) is attracting considerable attention. The heterogeneous interfacing might regulate the electronic structure and further improve the electrochemical activity. Herein, a Ce(OH)3 nanoparticle-interfaced Fe-doped nickel sulfide (Ce(OH)3@Fe-Ni3S2) electrocatalyst was prepared to improve the OER performance. The fabricated electrocatalyst displayed excellent intrinsic activity and long-term stability in 1 M KOH for the OER. The catalyst shows an ultralow overpotential of 195 mV at a current density of 10 mA cm-2 and a Tafel slope of 52 mV dec-1, which are remarkably smaller than those of the control samples. This excellent electrocatalytic activity is attributed to the incorporation of Ce(OH)3 nanoparticles on the surface of the Fe-Ni3S2 nanosheet, which increases the electrochemical activity and enlarges the active surface area of the catalyst. In comparison to previous nonprecious OER electrocatalysts, the prepared Ce(OH)3@Fe-Ni3S2 exhibits greater electrocatalytic activity and longer durability, allowing for the selection of new electrocatalysts for practical applications.

In Situ Fabrication of Mn-Doped NiMoO4 Rod-like Arrays as High Performance OER Electrocatalyst

The slow kinetics of the oxygen evolution reaction (OER) is one of the significant reasons limiting the development of electrochemical hydrolysis. Doping metallic elements and building layered structures have been considered effective strategies for improving the electrocatalytic performance of the materials. Herein, we report flower-like nanosheet arrays of Mn-doped-NiMoO₄/NF (where NF is nickel foam) on nickel foam by a two-step hydrothermal method and a one-step calcination method. The doping manganese metal ion not only modulated the morphologies of the nickel nanosheet but also altered the electronic structure of the nickel center, which could be the result of superior electrocatalytic performance. The Mn-doped-NiMoO₄/NF electrocatalysts obtained at the optimum reaction time and the optimum Mn doping showed excellent OER activity, requiring overpotentials of 236 mV and 309 mV to drive 10 mA cm^-2 (62 mV lower than the pure NiMoO₄/NF) and 50 mA cm^-2 current densities, respectively. Furthermore, the high catalytic activity was maintained after continuous operation at a current density of 10 mA cm^-2 of 76 h in 1 M KOH. This work provides a new method to construct a high-efficiency, low-cost, stable transition metal electrocatalyst for OER electrocatalysts by using a heteroatom doping strategy.

Anchoring Ce-modified Ni(OH)2 nanoparticles on Ni-MOF nanosheets to enhances the oxygen evolution performance

Constructing a heterostructure is an efficient strategy to enhance the catalytic activity toward the oxygen evolution reaction (OER). Herein, Ce-modified Ni(OH)₂ nanoparticles are anchored on Ni-MOF nanosheets by the electrodeposition strategy, forming a self-supporting electrode of Ce-m-Ni(OH)₂@Ni-MOF. The Raman spectrum proves that both Ce(OH)₃ and Ce doping exist in Ce-modified Ni(OH)₂ nanoparticles. The heterostructure possesses an open nanosheet structure, with a good interaction between Ni-MOF and Ce-m-Ni(OH)₂, which enables efficient mass/charge transfer and the synergetic effect between Ni and Ce, leading to a high-performance electrocatalyst. Specifically, Ce-m-Ni(OH)₂@Ni-MOF achieves current densities of 50 and 100 mA cm^-2 at low overpotentials of 219 and 272 mV, respectively, and retains high activity for at least 30 h.