3D printed porous sulfonated polyetheretherketone scaffold for cartilage repair: Potential and limitation

Objective

The treatment of cartilage lesions has always been a difficult problem. Although cartilage tissue engineering provides alternative treatment options for cartilage lesions, biodegradable tissue engineering scaffolds have limitations.

Methods

In this study, we constructed a porous PEEK scaffold via 3D printing, surface-engineered with concentrated sulfuric acid for 15 s (SPK-15), 30 s (SPK-30), and 60 s (SPK-60). We systematically evaluated the physical and chemical characteristics and biofunctionalities of the scaffolds, and then evaluated the macrophage polarization modulating ability and anti-inflammatory effects of the sulfonated PEEK, and observed the cartilage-protective effect of SPK using a co-culture study. We further evaluated the repair effect of PEEK and SPK by implanting the prosthetic scaffold into a cartilage defect in a rabbit model.

Results

Compared to the PEEK, SPK-15 and SPK-60 scaffolds, SPK-30 has a good micro/nanostructure, appropriate biomechanical properties (compressive modulus, 43 ± 5 MPa; Shaw hardness, 20.6 ± 1.3 HD; close to native cartilage, 30 ± 8 MPa, 17.8 ± 0.8 HD), and superior biofunctionalities. Compared to PEEK, sulfonated PEEK can favor macrophage polarization to the M2 phenotype, which increases anti-inflammatory cytokine secretion. Furthermore, SPK can also prevent macrophage-induced cartilage degeneration. The in-vivo animal experiment demonstrates that SPK can favor new tissue ingrowth and integration, prevent peri-scaffold cartilage degeneration and patellar cartilage degeneration, inhibit inflammatory cytokine secretion, and promote cartilage function restoration.

Conclusion

The present study confirmed that the 3D printed porous sulfonated PEEK scaffold could promote cartilage functional repair, and suggests a new promising strategy for treating cartilage defects with a functional prosthesis that spontaneously inhibits nearby cartilage degeneration.

Translational potential of this article

In the present study, we propose a new cartilage repair strategy based on a porous, non-biodegradable polyetheretherketone (PEEK) scaffold, which may bring up a new treatment route for elderly patients with cartilage lesions in the future.

Hyaline Articular Matrix Formed by Dynamic Self-Regenerating Cartilage and Hydrogels

Injuries to the articular cartilage surface are challenging to repair because cartilage possesses a limited capacity for self-repair. The outcomes of current clinical procedures aimed to address these injuries are inconsistent and unsatisfactory. We have developed a novel method for generating hyaline articular cartilage to improve the outcome of joint surface repair. A suspension of 10(7) swine chondrocytes was cultured under reciprocating motion for 14 days. The resulting dynamic self-regenerating cartilage (dSRC) was placed in a cartilage ring and capped with fibrin and collagen gel. A control group consisted of chondrocytes encapsulated in fibrin gel. Constructs were implanted subcutaneously in nude mice and harvested after 6 weeks. Gross, histological, immunohistochemical, biochemical, and biomechanical analyses were performed. In swine patellar groove, dSRC was implanted into osteochondral defects capped with collagen gel and compared to defects filled with osteochondral plugs, collagen gel, or left empty after 6 weeks. In mice, the fibrin- and collagen-capped dSRC constructs showed enhanced contiguous cartilage matrix formation over the control of cells encapsulated in fibrin gel. Biochemically, the fibrin and collagen gel dSRC groups were statistically improved in glycosaminoglycan and hydroxyproline content compared to the control. There was no statistical difference in the biomechanical data between the dSRC groups and the control. The swine model also showed contiguous cartilage matrix in the dSRC group but not in the collagen gel and empty defects. These data demonstrate the survivability and successful matrix formation of dSRC under the mechanical forces experienced by normal hyaline cartilage in the knee joint. The results from this study demonstrate that dSRC capped with hydrogels successfully engineers contiguous articular cartilage matrix in both nonload-bearing and load-bearing environments.

High seeding density of human chondrocytes in agarose produces tissue-engineered cartilage approaching native mechanical and biochemical properties

Animal cells have served as highly controllable model systems for furthering cartilage tissue engineering practices in pursuit of treating osteoarthritis. Although successful strategies for animal cells must ultimately be adapted to human cells to be clinically relevant, human chondrocytes are rarely employed in such studies. In this study, we evaluated the applicability of culture techniques established for juvenile bovine and adult canine chondrocytes to human chondrocytes obtained from fresh or expired osteochondral allografts. Human chondrocytes were expanded and encapsulated in 2% agarose scaffolds measuring ∅3-4mm×2.3mm, with cell seeding densities ranging from 15 to 90×10(6)cells/mL. Subsets of constructs were subjected to transient or sustained TGF-β treatment, or provided channels to enhance nutrient transport. Human cartilaginous constructs physically resembled native human cartilage, and reached compressive Young's moduli of up to ~250kPa (corresponding to the low end of ranges reported for native knee cartilage), dynamic moduli of ~950kPa (0.01Hz), and contained 5.7% wet weight (%/ww) of glycosaminoglycans (≥ native levels) and 1.5%/ww collagen. We found that the initial seeding density had pronounced effects on tissue outcomes, with high cell seeding densities significantly increasing nearly all measured properties. Transient TGF-β treatment was ineffective for adult human cells, and tissue construct properties plateaued or declined beyond 28 days of culture. Finally, nutrient channels improved construct mechanical properties, presumably due to enhanced rates of mass transport. These results demonstrate that our previously established culture system can be successfully translated to human chondrocytes.