Effect of pretreatment with calcium-containing desensitizer on the dentine bonding of mild self-etch adhesives

Enhancing the inhibition of dental erosion and abrasion with quercetin-encapsulated hollow mesoporous silica nanocomposites

Introduction: Dental erosion and abrasion pose significant clinical challenges, often leading to exposed dentinal tubules and dentine demineralization. The aim of this study was to analyse the efficacy of quercetin-encapsulated hollow mesoporous silica nanocomposites (Q@HMSNs) on the prevention of dentine erosion and abrasion. Method: Q@HMSNs were synthesized, characterized, and evaluated for their biocompatibility. A total of 130 dentine specimens (2 mm × 2 mm × 2 mm) were prepared and randomly distributed into 5 treatment groups (n = 26): DW (deionized water, negative control), NaF (12.3 mg/mL sodium fluoride, positive control), Q (300 μg/mL quercetin), HMSN (5.0 mg/mL HMSNs), and Q@HMSN (5.0 mg/mL Q@HMSNs). All groups were submitted to in vitro erosive (4 cycles/d) and abrasive (2 cycles/d) challenges for 7 days. The specimens in the DW, NaF, and Q groups were immersed in the respective solutions for 2 min, while treatment was performed for 30 s in the HMSN and Q@HMSN groups. Subsequently, the specimens were subjected to additional daily erosion/abrasion cycles for another 7 days. The effects of the materials on dentinal tubule occlusion and demineralized organic matrix (DOM) preservation were examined by scanning electron microscopy (SEM). The penetration depth of rhodamine B fluorescein into the etched dentine was assessed using confocal laser scanning microscopy (CLSM). The erosive dentine loss (EDL) and release of type I collagen telopeptide (ICTP) were measured. The data were analysed by one-way analysis of variance (ANOVA) with post hoc Tukey's test (α = 0.05). Results: Q@HMSNs were successfully synthesized and showed minimal toxicity to human dental pulp stem cells (HDPSCs) and gingival fibroblasts (HGFs). Q@HMSNs effectively occluded the dentinal tubules, resulting in a thicker DOM in the Q@HMSN group. The CLSM images showed more superficial penetration in the HMSN and Q@HMSN groups than in the quercetin, NaF, and DW groups. The Q@HMSN group exhibited a significantly lower EDL and reduced ICTP levels compared to the other groups (p < 0.05). Conclusion: Q@HMSNs hold promise for inhibiting dentine erosion and abrasion by promoting tubule occlusion and DOM preservation.

The Effect of Biomimetic Remineralization of Calcium Phosphate Ion Clusters-Treated Enamel Surfaces on Bracket Shear Bond Strength

Purpose

To evaluate the remineralization effect of calcium phosphate ion clusters (CPICs) on demineralized enamel surfaces and their effects on bracket shear bond strength.

Patients and Methods

Extracted premolars were prepared in resin blocks. The samples in the form of resin blocks were divided into five experimental groups: control group, demineralized group, and groups of CPIC solution treatment for 30, 60, and 90s. The specimens were examined using scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDX), microhardness testing, micro-computed tomography (micro-CT) assessment, shear bond strength (SBS) test, and adhesive remnant index (ARI) score.

Results

The SEM images revealed epitaxial growth of enamel and a decrease in the thickness of the demineralized enamel layer when treated with CPIC solution. The EDX analysis revealed an increase in the Ca/P ratio in the CPIC-treated groups. The microhardness value significantly increased when treated with CPICs; however, it showed a lower value than that of the sound enamel groups. As a result of the micro-CT test, radiolucency decreased gradually as the CPIC treatment time increased. The SBS test and ARI score results showed an improvement in bonding stability after treatment with CPICs.

Conclusion

We demonstrated an enamel biomodification approach using CPIC solution treatment, which is a promising strategy for enamel remineralization. Specifically, remineralization of demineralized enamel improves the orthodontic bracket SBS.

Oyster shell-derived nano-hydroxyapatite and proanthocyanidin pretreatment on dentinal tubule occlusion and permeability before and after acid challenge-an in vitro study

This in vitro study evaluated the dentinal tubule occlusion (TO), depth of penetration (DoP), and dentin permeability (DP) of oyster shell-derived nanohydroxyapatite (os-nHAp) with and without 15% proanthocyanidin (PA) pretreatment. os-nHAp was synthesized via the precipitation method and it was characterized. The morphology and particle size of os-nHAp were analyzed using a high-resolution transmission electron microscope (HRTEM). Cytotoxicity of os-nHAp, PA/os-nHAp, and casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) was assessed by (3-(4,5-dimethythiazol-2-yl) 2,5-diphenyl tetrazolium bromide (MTT) assay using human osteosarcoma (MG-63) cell line. One hundred and ninety-seven dentin discs of 3 mm thickness were prepared from the crown portion of extracted human teeth. The dentinal surfaces of the discs were etched for 2 min with 6% citric acid to simulate dentin hypersensitivity. Five discs were randomly selected and the patency of dentinal tubules was confirmed using a scanning electron microscope (SEM). The remaining 192 discs were divided into four groups (n = 48) depending on the type of remineralization as follows: group 1: os-nHAp, group 2: PA/os-nHAp, group 3: CPP-ACP, and group 4: no treatment. The remineralization protocol was followed for 21 days. Out of the 48 dentin discs in each group, 32 discs were used to evaluate dentinal tubule occlusion (TO) and depth of penetration (DoP) using SEM. The remaining 16 discs were subjected to an assessment of dentin permeability (DP) using a hydraulic conductance model. TO, DoP and DP were evaluated after remineralization and acid challenge. Characterization studies confirmed the presence of pure phase apatite. HRTEM confirmed the nanometric particle size of os-nHAp. MTT assay results showed that all the tested materials exhibited >80% cell viability when tested up to a concentration of 100 µg/mL. The results demonstrated a significantly higher mean percentage of TO, DoP, and lesser mean DP after remineralization in groups 1, 2, and 3 (p < 0.05). After the acid challenge, group 3 showed a significant reduction in TO and DoP, and increased DP (p < 0.05). However, no such changes were observed in groups 1 and 2. Within the limitations of this study, it can be concluded that os-nHAp and PA/os-nHAp could serve as potential and durable therapeutic agents in the treatment of dentin hypersensitivity.

The effect of desensitizing agents on the bond strength of dentin bonding agents: A systematic review

Background

Dentinal hypersensitivity (DH) is a common dental problem and is treated non-invasively using topical application of various desensitizing agents. When there is loss of tooth structure or tooth preparation is to be followed by a bonded restoration, it requires application of dentin bonding agent. However, the effect of desensitizers on bond strength is still controversial.

Aim and Objective

To evaluate the influence of different desensitizing agents on the bond strength of the dentin bonding agents.

Methods and Materials

PICO strategy was used to formulate the research question. In-vitro studies conducted on human teeth to evaluate the bond strength of dentin bonding agent following the application of desensitizing agent were included. Electronic databases PubMed and Cochrane and google scholar were searched using search terms alone or in combination from the year 2010 till 2020. Search was conducted using the key words and MeSH terms (hypersensitivity, bond strength, dental adhesives, dentin bonding agents). The title and abstract were read to verify the inclusion and exclusion criteria and if further any details required, full article was accessed to check the criteria and then included or excluded. Data extraction was done using a customized data extraction form. The risk of bias was evaluated using modified Cochrane Collaboration Quality Assessment tool.

Results

Total no of studies identified in the search were 146, after scrutiny 23 articles were eligible to be included in this study. Out of 23 articles, 17 articles were of medium bias and 6 articles were of high risk after risk of bias assessment.

Conclusion

According to the various articles included in this study, GLUMA and 8.0%Arginine and CaCO3 when used as desensitizing agents along with different bonding agents, were found to be highly compatible without interfering with the bond strength of the dentin adhesives.

Application of Amorphous Calcium Phosphate Agents in the Prevention and Treatment of Enamel Demineralization

Enamel demineralization, as a type of frequently-occurring dental problem that affects both the health and aesthetics of patients, is a concern for both dental professionals and patients. The main chemical composition of the enamel, hydroxyapatite, is easy to be dissolved under acid attack, resulting in the occurrence of enamel demineralization. Among agents for the preventing or treatment of enamel demineralization, amorphous calcium phosphate (ACP) has gradually become a focus of research. Based on the nonclassical crystallization theory, ACP can induce the formation of enamel-like hydroxyapatite and thereby achieve enamel remineralization. However, ACP has poor stability and tends to turn into hydroxyapatite in an aqueous solution resulting in the loss of remineralization ability. Therefore, ACP needs to be stabilized in an amorphous state before application. Herein, ACP stabilizers, including amelogenin and its analogs, casein phosphopeptides, polymers like chitosan derivatives, carboxymethylated PAMAM and polyelectrolytes, together with their mechanisms for stabilizing ACP are briefly reviewed. Scientific evidence supporting the remineralization ability of these ACP agents are introduced. Limitations of existing research and further prospects of ACP agents for clinical translation are also discussed.

Effect of photodynamic therapy on resin-dentin bonding interface using different illumination time

OBJECTIVES

The aim of the present study was to evaluate the effect of photodynamic therapy(PDT) on the resin-dentin bonding interface using different illumination time.

METHODS

Seventy completed, isolated molar teeth were collected for this study, sixty of them were used in microtensile bond strength tests. These teeth were initially divided randomly in two main groups(n=30) by the random number table method upon the type of using illumination or not respectively. Then these groups followed by dividing each category in five subgroups(n=6): group A, group B1,group B2, group B3, group B4, group a, group b1, group b2, group b3, group b4. After different treatment, the remaining teeth were made specimens which were observed the fracture modes and interfaces under a stereomicroscope and a scanning electron microscope(SEM). The dentin permeability of the specimens were evaluated by a laser scanning confocal microscope(LSCM). To detect significance difference between means of different groups analysis of variance(ANOVA) was performed followed by LSD-t tests.

RESULTS

There was a significant statistical difference in the microtensile bond strength of the different illumination time of PDT between four experimental groups and the control (P<0.05).

CONCLUSION

With the increase of the illumination time in PDT, the bonding strength between resin and dentin decreased gradually.

Influences of desensitizing agents on bond strength of etch-and-rinse and self-etch adhesive system to dentin

Background:

Cervical lesions requiring adhesive restoration may present with dentin hypersensitivity, but the effect of desensitizer treatment on microtensile bond strength (MBS) is inconclusive.

Aim:

The aim of the present study was to assess the influence of two types of dentin desensitizing treatment on bond strength to dentin.

Materials and Methods:

Thirty-six extracted human mandibular first premolars were used to obtain superficial buccal cervical dentin. The samples were assigned to two groups (18/group): etch-and-rinse (ERS) (Optibond^® Solo) and self-etch (Palfique) adhesive systems. Eighteen teeth in each group were randomly assigned to three desensitizer treatments (6/treatment); control (no desensitization), Gluma™ desensitizerand Novamin-containing toothpaste (Sensodyne repair and protect™). Bonded dentin-composite specimens were stored in artificial saliva for 2 weeks prior to scanning electron microscope (SEM) evaluation and MBS testing. Univariate analysis of variance and Tukey tests were performed (α = 0.05) for the data analysis.

Results:

The mean MBS with self-etch system (SES) was significantly higher than ERS system, irrespective of the dentin desensitizer regimen. SEM showed no hybrid layer or resin tag formation in the SES group. Tubular occlusion was observed in all specimens treated with desensitizer.

Conclusion:

Mild self-etch adhesive can be used on dentin treated with Gluma or bioglass-containing desensitizer without compromising the bond strength.

Clinical Relevance:

Dentin desensitizer such as in-office Gluma or at-home Novamin-containing toothpaste could be used without compromising the bond strength of mild self-etch adhesive systems.

Effects of calcium-phosphate, laser and adhesive on dentin permeability and bond strength

Objectives

The present study examined a technique for reducing dentin permeability through the application of a calcium phosphate (CaP)-based desensitiser with a laser-assisted process and evaluated adhesive-dentin bond strength. Methods: Thirty dentin discs were divided into two groups according to whether the selected desensitiser (TeethMate; Kuraray Noritake) was used prior to dentin bonding. Each group was subdivided into three subgroups (n = 5): A- Adhesive (Single Bond Universal, 3M ESPE), AL- Adhesive + Laser (Nd:YAG 60 mJ) and LAL- Laser + Adhesive + Laser. Dentin permeability values (%) were recorded before and after desensitiser application. Resin composites were placed over the bonded specimens; the latter were aged prior to microtensile bond strength evaluation. Gelatinolytic activity within the hybrid layers was examined with in-situ zymography using confocal laser scanning microscopy. Data were analysed with ANOVA and Tukey test (α = 0.05).

Results

Significant differences in dentin permeability were identified for all groups (p = 0.00). Both laser treatment (p = 0.182) and desensitiser application (p = 0.687) did not significantly improve dentin bond strength. Ultrastructure of the resin-dentin interface identified presence of calcium phosphate within dentinal tubules. Laser treatment did not affect hybrid layer ultrastructure. Both treatment modalities (intratubular CaP occlusion and laser) had no influence on gelatinolytic activity within hybrid layers.

Conclusion

Although intratubular CaP occlusion and laser treatment were effective in reducing dentin permeability, they did not affect bond strength, interfacial ultrastructure and gelatinolytic activity within hybrid layers.

Clinical relevance

Treatment of etched dentin with Nd:YAG Laser at 60 mJ does not adversely affect collagen ultrastructure and gelatinolytic activity within the hybrid layer. The application of a calcium phosphate-based desensitiser to etch dentin does not affect dentin bond strength.

Effect of Dentin Pretreatment with Arginine on Microshear Bond Strength of Etch-and-Rinse or Self-Etch Adhesive Systems

Objective The main purpose of this study was to evaluate the effect of dentin pretreatment with 8% arginine on the immediate and 6-month bond strength (BS) of adhesive systems and surface morphology of dentin.

Materials and Methods Dentin bovine specimens (5 × 5 mm) were allocated into following pretreatments: without pretreatment (conventional technique, C) or exposure to arginine solution (A) for 5 minutes prior to tooth restoration. The adhesive procedure was performed using ( n = 12): 3-step etch-and-rinse adhesive (Scotchbond Multipurpose—SBMP [C+SBMP and A+SBMP]); 2-step etch-and-rinse adhesive (Single Bond 2 - SB [C+SB and A+SB]); or 2-step self-etch adhesive (Clearfil SE Bond - CSEB [C+CSEB and A+CSEB]). After 24 hours, the composite resin restorations were evaluated immediately and after 6 months of water storage using a microshear test and fracture pattern. The dentin surface exposed to A was assessed by scanning electron microscopy (SEM). The immediate BS data were submitted to a two-way analysis of variance and Tukey's test, and the long-term BS results were analyzed using Kruskal–Wallis and Dunn tests (α = 0.05).

Results There was a significant decrease in immediate and 6-month BS for the A+SB and A+CSEB groups, which differed statistically from the C group. The fracture pattern was predominantly adhesive for SB and CSEB adhesive for C and A. The SEM images presented a different conditioning pattern of the dentin exposed to A.

Conclusion The dentin pretreatment with arginine interfered negatively in the immediate and long-term BS of the simplified adhesive system. However, the SBMP adhesive was not affected by arginine pretreatment presenting the most satisfactory results.

Inhibitory effect of zinc-containing desensitizer on bacterial biofilm formation and root dentin demineralization

This study compared the effect of a novel zinc containing, Caredyne Shield (CS), and a fluoroaluminocalciumsilicate-based, Nanoseal (NS) desensitizers on dentin tubule occlusion, inhibition of Streptococcus mutans (S. mutans) biofilm growth, and resistance to bacterial demineralization. Desensitizers were applied to simulated hypersensitive bovine dentin, with distilled water used as a control. S. mutans biofilms were grown on the surface of each specimen in an oral biofilm simulator. CS showed the least bacterial count and water insoluble glucan amount followed by NS. Transverse micro radiography revealed that both CS and NS showed significant reduction in mineral loss and lesion depth of the associated lesion. Scanning electron micrographs showed that the two desensitizers formed obvious depositions on the dentin surfaces, occlusion of tubules and mineral tag formation.

The Effect of the Application Sequence of Casein Phosphopeptide-Amorphous Calcium Phosphate Paste on the Shear Bond Strength of Etch-and-Rinse Resin Cements to Dentin

PURPOSE

To evaluate the effect of the application sequence of casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) paste (MI paste) on shear bond strength (SBS) of 2 etch-and-rinse resin cements to dentin.

MATERIALS AND METHODS

Sixty extracted human maxillary premolars were cut to expose the mid-coronal dentin surfaces. The teeth were randomly divided into 6 groups (n = 10), based on the resin cement used and CPP-ACP application. In groups 1-3, Excite DSC/Variolink II and in groups 2-4, One-Step Plus/Duolink was bonded to dentin. There were 3 groups for each cement as follows: with no treatment as a control; 3-minute application of CPP-ACP before acid etching (CPP-ACP/Etching); 3-minute application of CPP-ACP after acid etching (Etching/CPP-ACP). After storage in distilled water at 37°C for 24 hours, SBS test was performed. Data were analyzed with 2-way ANOVA and post-hoc Tukey test (α = 0.05).

RESULTS

CPP-ACP application on the dentin before and after acid etching significantly decreased the SBS of OS/Duolink (13.60 and 14.71 MPa, respectively vs. control; 21.21 MPa, p < 0.001); however, it did not influence the SBS of Excite DSC/Variolink II (25.14 MPa) before acid etching (27.37 MPa) or after acid etching (26.41 MPa, p > 0.388). The application sequence of CPP-ACP did not influence the SBS of etch-and-rinse resin cements evaluated.

CONCLUSION

CPP-ACP applications may lower the SBS in some etch-and-rinse resin cements, and timing of applications makes no difference.

Effect of Preetching on Microleakage with All-In-One Adhesives Using Calcium-Based Desensitizers: An In vitro Study

Objectives

The aim of this study was to evaluate the effect of calcium-based desensitizers on the microleakage with and without preetching enamel in Class V cavities restored with all-in-one adhesives.

Materials and Methods

Class V cavities were prepared on the buccal surfaces of 100 extracted human premolars. A total of 100 box-shaped cavities were divided into five groups (n = 20). Group 1 - no desensitizer was applied and Groups 2 and 4 - desensitizer (CCP-ACP and Novamin) was applied, respectively, followed by the application of G-Bond and restored with composite restoration. Groups 3 and 5 are same as Group 2 and 4, but preetching of enamel was done for 3 s after desensitizers application. The teeth were thermocycled and the specimens were examined for microleakage using methylene blue as a marker. The teeth were sectioned buccolingually and evaluated for microleakage under stereomicroscope and the scores obtained were analyzed with Kruskal-Wallis and Mann-Whitney tests.

Results

Statistically significant difference existed between Groups 2 and 3 (P < 0.05). There was also statistically significant difference between Groups 4 and 5 (P < 0.05). Groups 3 and 5 showed significantly less microleakage (P < 0.05). No statistically significant difference in microleakage values was observed between the two desensitizers CCP-ACP and Novamin.

Conclusion

The application of calcium-containing desensitizers with selective etch enamel technique in all-in-one adhesives could be considered an advisable procedure to minimize microleakage.

Dentin sealing and antibacterial effects of silver-doped bioactive glass/mesoporous silica nanocomposite: an in vitro study

OBJECTIVES

To synthesize a silver-doped bioactive glass/mesoporous silica nanoparticle (Ag-BGN@MSN), as well as to investigate its effects on dentinal tubule occlusion, microtensile bond strength (MTBS), and antibacterial activity.

MATERIALS AND METHODS

Ag-BGN@MSN was synthesized using a modified "quick alkali-mediated sol-gel" method. Demineralized tooth disc models were made and divided into four groups; the following treatments were then applied: group 1-no treatment, group 2-bioglass, group 3-MSN, group 4-Ag-BGN@MSN. Next, four discs were selected from each group and soaked into 6 wt% citric acid to test acid-resistant stability. Dentinal tubule occlusion, as well as the occlusion ratio, was observed using field-emission scanning electron microscopy. The MTBS was also measured to evaluate the desensitizing effect of the treatments. Cytotoxicity was examined using the MTT assay. Antibacterial activity was detected against Lactobacillus casei, and ion dissolution was evaluated using inductively coupled plasma optical emission spectrometry.

RESULTS

Ag-BGN@MSN effectively occluded the dentinal tubule and formed a membrane-like layer. After the acid challenge, Ag-BGN@MSN had the highest rate of dentinal tubule occlusion. There were no significant differences in MTBS among the four groups (P > 0.05). All concentrations of Ag-BGN@MSN used had a relative cell viability above 72%.

CONCLUSIONS

Ag-BGN@MSN was successfully fabricated using a modified sol-gel method. The Ag-BGN@MSN biocomposite effectively occluded dentinal with acid-resistant stability, did not decrease bond strength in self-etch adhesive system, had low cytotoxicity, and antibacterial effect.

CLININAL RELEVANCE

Dentinal tubule sealing induced by Ag-BGN@MSN biocomposite with antibacterial effect is likely to increase long-term stability in DH.

Effects of calcium-containing desensitizers on the bonding stability of an etch-and-rinse adhesive against long-term water storage and pH cycling

This study aimed to evaluate the effects of two calcium-containing desensitizing pastes on the bonding stability of an etch-and-rinse (E&R) adhesive to dentine. After dentine hypersensitivity model established, dentine surfaces were assigned one of the following pretreatment: Group 1, no desensitizer; Group 2, CPP-ACP; and Group 3, Novamin. Specimens were then bonded with an E&R adhesive. Beams from each tooth were randomly divided into three subgroups and then subjected to microtensile bond strength (MTBS) test after 24 h; 12 months of water storage; or 15 runs of pH cycling. Failure modes, nanoleakage, and tubule-occluding effectiveness were analyzed. Results showed that CPP-ACP- or Novamin-pretreated specimens mainly preserved the bonding strength after 12 months of water storage, while effective tubule occlusion could be observed. The results suggested that the calcium-containing desensitizers were compatible pretreatment for bonding with E&R adhesives to obtain reliable long-term bonding strength and prevention of post-operative sensitivity.

Development of Epigallocatechin-3-gallate-Encapsulated Nanohydroxyapatite/Mesoporous Silica for Therapeutic Management of Dentin Surface

In dental clinic, unsatisfactory management of the dentin surface after dentin exposure often leads to the occurrence of dentin hypersensitivity and caries. Current approaches can occlude the tubules on the dentin surface to relieve dentin hypersensitivity; however, the blocked tubules are generally weak in combating daily tooth erosion and abrasion. Moreover, cariogenic bacteria, such as Streptococcus mutans, produce biofilm on the dentin surface, causing caries and compromising the tubules' sealing efficacy. To overcome this problem, the present study focused on establishing a versatile biomaterial, epigallocatechin-3-gallate-encapsulated nanohydroxyapatite/mesoporous silica nanoparticle (EGCG@nHAp@MSN), for therapeutic management of the dentin surface. The effectiveness of the biomaterial on dentinal tubule occlusion, including resistances against acid and abrasion, was evaluated by field-emission scanning electron microscopy (FESEM) and dentin permeability measurement. The inhibitory capability of the biomaterial on S. mutans biofilm formation was investigated by confocal laser scanning microscopy (CLSM), 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyltetrazolium bromide (MTT) assay, colony forming units (CFU) counts, and FESEM. Results demonstrated for the first time that the use of EGCG@nHAp@MSN on the dentin surface was capable of effectively occluding dentinal tubules, reducing dentin permeability, and achieving favorable acid- and abrasion-resistant stability. Furthermore, EGCG@nHAp@MSN held the capability to continuously release EGCG, Ca, and P, and significantly inhibit the formation and growth of S. mutans biofilm on the dentin surface. Thus, the development of EGCG@nHAp@MSN bridges the gap between multifunctional concept and dental clinical practice and is promising in providing dentists a therapeutic strategy for the management of the dentin surface to counter dentin hypersensitivity and caries.

Influence of dentin pretreatment with synthetic hydroxyapatite application on the bond strength of fiber posts luted with 10-methacryloyloxydecyl dihydrogen phosphate-containing luting systems

The aim of this in vitro study was evaluate the effect of application of synthetic hydroxyapatite on fiber post bond strength to radicular dentine. Forty, single-root teeth were endodontically treated and an 8 mm post space was prepared. Specimens were randomly placed in four groups (n = 10 in each) and treated using the following fiber post luting procedures: group 1, 17% EDTA + Panavia SA; group 2, 17% EDTA + Teethmate Desensitizer + Panavia SA; group 3, All-Bond Universal + Duo-Link Universal; and group 4, All-Bond Universal + Teethmate Desensitizer + Duo-Link Universal. Fiber posts were luted in the post space and light-cured for 120 s using a light-emitting diode (LED) lamp. After 7 d of storage at 37°C, the teeth were cut into 1-mm-thick slices, which were subjected to a push-out test until failure using a universal testing machine. Two specimens per group were prepared for scanning electron microscopy analysis. An energy-dispersive X-ray spectroscopy detector was used for elemental analysis of the specimen surface. The results were statistically analyzed using one-way anova. The fiber post bond strength was statistically significantly increased after the application of Teethmate Desensitizer to post space walls, either with a 10-MDP-containing self-adhesive cement or with a universal adhesive. Scanning electron microscopy and EDAX analysis showed that Teethmate Desensitizer created a calcium phosphate precipitate over post space dentinal tubules, which significantly improved the bond strength of the fiber post luted with 10-methacryloyloxydecyl dihydrogen phosphate (10-MDP)-containing adhesive systems.

Effect of desensitizing agents on the microtensile bond strength of two-step etch-and-rinse adhesives to dentin

Desensitizers can be used to control postoperative sensitivity in adhesive restorations. The aim of this study was to evaluate the effect of desensitizing agents on the bond strength of two-step etch-and-rinse adhesive systems to dentin. Forty-two human molars were sectioned to obtain 3-mm-thick dentin discs. The discs were divided into three groups (n = 14 in each) - no-treatment control group (CT), and oxalic acid [BisBlock (BB)] and calcium phosphate [Desensibilize Nano-P (NP)] desensitizers - before the application of two adhesive systems [Adper Single Bond Plus (SB) and One-Step Plus (OSP)]. A nanoparticle composite resin was used to create a 3-mm-thick build-up. The specimens were stored in distilled water for 24 h before a microtensile bond-strength test was performed. The failure modes were determined using a stereomicroscope at 100 × magnification. Specimens were sectioned perpendicular to the interface for scanning electron microscopy analyses. The CT-SB group exhibited the highest bond strength, differing significantly from BB-SB and BB-OSP groups. Mixed failures were prevalent for all groups. Scanning electron microscopy revealed a continuous hybrid layer and resin tags in all groups. Dentin bond strength of etch-and-rinse adhesive systems was reduced by an oxalic acid desensitizer but was not affected by a calcium phosphate-containing desensitizer.

Effects of the application sequence of calcium-containing desensitising pastes during etch-and-rinse adhesive restoration

OBJECTIVES

To evaluate the effects of different application sequence of calcium-containing desensitising pastes on bonding effectiveness and tubule occlusion during etch-and-rinse (E&R) adhesive restoration.

METHODS

Seventy molars were sectioned parallel to the occlusal plane, polished and randomly divided into seven groups (n=10). Group 1 was etched with 35% phosphoric acid for 15s. Groups 2-4 were treated with different calcium-containing desensitisers, including an arginine-calcium carbonate (Arg-CaCO3)-containing paste, a casein phosphopeptide-amorphous calcium phosphate (CPP-ACP)-containing paste and a calcium-sodium phosphosilicate (Novamin)-containing paste, respectively. Afterward, these groups were etched with 35% phosphoric acid for 15s. Groups 5-7 were initially etched and then treated with Arg-CaCO3-, CPP-ACP- and Novamin-containing desensitisers, respectively. In each group, samples were equally distributed into two subgroups (n=5) to bond with either a two-step E&R adhesive Adper SingleBond 2 (SB) or a three-step E&R adhesive Adper ScotchBond Multi-Purpose (SBMP). The microtensile bond strengths (MTBS) were tested and fracture modes were analyzed by stereomicroscopy and field-emission scanning electron microscopy (FESEM). Eight additional dentine disks were prepared to evaluate tubule occlusion prior to bonding using FESEM.

RESULTS

The application sequence of calcium-containing desensitising pastes did not significantly affect MTBS irrespective of two-step SB (P>0.05) or three-step SBMP E&R adhesives (P>0.05). Effective dentinal tubule occlusion was observed in the mode of etching-desensitising.

CONCLUSIONS

Applying calcium-containing desensitisers (particularly Arg-CaCO3- and Novamin-based) after etching during E&R adhesive restoration could achieve effective tubule occlusion without affecting the bonding strength.