Nanoscale adhesion forces of glucosyltransferase B and C genes regulated Streptococcal mutans probed by AFM

Effects of immunoglobulin Y-loaded amorphous calcium phosphate on dentinal tubules occlusion and antibacterial activity

Aim: This study aimed to evaluate the effects of immunoglobulin Y (IgY)-loaded amorphous calcium phosphate (ACP) (IgY@ACP) on dentinal tubule occlusion and antibacterial activity.

Methodology: IgY@ACP was synthesized based on a biomimetic mineralization strategy. The structure was examined by transmission electron microscopy and Fourier transform infrared spectroscopy. The IgY release property was assessed in vitro. The cell biocompatibility of IgY@ACP was evaluated by CCK-8. The dentin disks were prepared using healthy human molars, and their dentinal tubules were exposed to EDTA. Subsequently, they were randomly selected and treated with or without IgY@ACP for 7 days. The tubule occlusion morphologies and newly formed layers were observed by scanning electron microscopy (SEM) and x-ray diffraction, respectively. To evaluate the acid resistance and abrasion resistance of IgY@ACP, dentin disks that were treated for 1 day were immersed in acid solution or subjected to a toothbrush. The antibacterial effects against Streptococcus mutans (S. mutans) were evaluated by colony-forming unit (CFU) counting, adhesion property assessment, and crystal violet and live/dead bacterial staining. Finally, the occlusion effect was evaluated in rat incisors in vivo. One-way analysis of variance (ANOVA) was performed for statistical analysis. The level of significance was set at 0.05.

Results: IgY@ACP presented an amorphous phase with a nanosize (60–80 nm) and sustained release of protein within 48 h. The CCK-8 results showed that IgY@ACP had good biocompatibility. After treatment with IgY@ACP for 1 day, the majority of dentinal tubules were occluded by a 0.3-μm-thick mineralized layer. Seven days later, all dentinal tubules were occluded by mineralization with a thickness of 1.4 μm and a depth of 16 μm. The newly mineralized layer showed hydroxyapatite-like diffraction peaks. In addition, IgY@ACP had good acid and abrasion resistance. After treatment with IgY@ACP, the CFU counting and adhesion rate of S. mutans were significantly reduced, the crystal violet staining was lighter, and the S. mutans staining revealed more dead cells. Most importantly, IgY@ACP had a certain occluding property in rat incisors in vivo.

Conclusion: IgY@ACP can effectively occlude dentinal tubules with acid-resistant stability and has prominent anti-S. mutans effects, rendering it a potentially suitable desensitization material in the clinic.

Glucosyltransferase modulated Streptococcus mutans adhesion to different surfaces involved in biofilm formation by atomic force microscope

Biofilm on dental restorative materials is an important determinant in the aetiology of secondary caries development. Formation of biofilm involving adhesion of bacteria onto substrate, bacterial cell and biofilm surfaces. Glucosyltransferase B and C (GtfB and GtfC) are essential factors for regulation of Streptococcus mutans biofilm formation, but the mechanisms involving different kind of bacterial adhesion still lack detailed description. In this study, nanoscale adhesion force measurement was performed using atomic force microscopy (AFM). Bacteria-coated cantilevers were used to probe S. mutans adhesion to substrates, bacterial cells and early biofilms. Two representative dental materials, Glass ionomer cement (GIC) and composite resin, served as substrates. It was found that deletion of gtfB and gtfC genes both reduced adhesion forces of S. mutans towards substrate and bacterial cell surfaces (P<0.05). Notably, reduction of gtfB gene remarkably decreased bacterial adhesion to biofilm surfaces(P<0.05), while gtfC showed no obvious effect during this stage. Biofilms cultured on GIG further decreased cell-biofilm adhesion, compared with that on resin (P<0.05). Confocal fluorescence images and scanning electron microscopy images showed that deletion of gtfB lead to reduced microcolony formation and less production of exopolysaccharides (EPS) in the biofilm, and after bacteria culturing on GIC, the EPS content was further decreased. Our findings suggest that EPS mainly mediate bacterial adhesion to early biofilm surface. Deletion of gtfB and co-culture with GIC could significantly reduce the cell-biofilm adhesion, which is probably through decreasing of EPS production. gtfB exerts a critical role in the bacterial adhesion for the whole process of biofilm development, while gtfC possibly works only in the early stages. This article is protected by copyright. All rights reserved.

Implication of Surface Properties, Bacterial Motility, and Hydrodynamic Conditions on Bacterial Surface Sensing and Their Initial Adhesion

Biofilms are structured microbial communities attached to surfaces, which play a significant role in the persistence of biofoulings in both medical and industrial settings. Bacteria in biofilms are mostly embedded in a complex matrix comprised of extracellular polymeric substances that provide mechanical stability and protection against environmental adversities. Once the biofilm is matured, it becomes extremely difficult to kill bacteria or mechanically remove biofilms from solid surfaces. Therefore, interrupting the bacterial surface sensing mechanism and subsequent initial binding process of bacteria to surfaces is essential to effectively prevent biofilm-associated problems. Noting that the process of bacterial adhesion is influenced by many factors, including material surface properties, this review summarizes recent works dedicated to understanding the influences of surface charge, surface wettability, roughness, topography, stiffness, and combination of properties on bacterial adhesion. This review also highlights other factors that are often neglected in bacterial adhesion studies such as bacterial motility and the effect of hydrodynamic flow. Lastly, the present review features recent innovations in nanotechnology-based antifouling systems to engineer new concepts of antibiofilm surfaces.