Textile ageing due to atmospheric gases and particles in indoor cultural heritage

Textile fibre degradation can be due to many factors. The most common cause is light exposure, but upon the lifespan of a textile, many other environmental factors are to be taken into account. This study focuses on the role of atmospheric compounds-both particulate and gaseous species-on natural textiles ageing, more specifically cotton, silk and wool. To achieve this, reference samples of textiles were exposed to contrasted environments (marine, urban and semi-rural museums and historical buildings) for natural ageing. These conditions were also reproduced in an experimental chamber dedicated to the study of the impact of airborne pollutants on heritage materials. Experimental ageing allowed to highlight degradation mechanisms for each fibre: SO₂ and HCOOH cause the cleavage of cotton's glyosidic links and silk's peptide bonds, while NO₂ promotes the oxidation of the fibres. The most harmful pollutant towards cotton is NO₂ since it causes both its oxidation and hydrolysis. The case of wool is more complicated: HCOOH provokes peptide link cleavage (similarly to silk) but this fibre is less sensitive to SO₂ attacks than silk and even seems to be protected against future alterations after having been firstly exposed to this pollutant. In any case, this experimental study evidences that damages caused by gaseous pollutants are fostered by the presence of particles, regardless of the chemical composition of the particle coating.

Wet and dry atmospheric deposition on TiO(2) coated glass

To prevent the soiling of glass window used in the built environment, the use TiO(2) coated products appears an important application matter. To test the cleaning efficiency and the sustainability of self-cleaning glass, a field experiment was conducted under real life condition, on a site representative of the background urban pollution. Samples of float glass, used as reference, and commercialized TiO(2) coated glasses were exposed to dry and wet atmospheric deposition during two years. The crossed optical, chemical and microscopic evaluations performed, after withdrawal, allowed highlighting a sensible difference between the reference and the self-cleaning substrate in terms of accumulation, nature, abundance and geometry of the deposit. This experiment conducted in real site emphasized on the efficacy of self-cleaning glass to reduce the maintenance cost.

Modeling of soiling based on silica-soda-lime glass exposure at six European sites

Samples of silica-soda-lime float glass, a material selected as a pertinent soiling sensor, were exposed for up to 28 months at four urban sites (Athens, Krakow, London and Prague) and at a semi-urban one (Monte Libretti, near Rome), sheltered from rain. This exhaustive experience permitted to complete and to test the generalisation ability of the results previously obtained on the same material, exposed according to the same protocol, during 24 months, at a single site (Paris). The model previously fitted for the Paris experiment, the Hill equation, could be successfully generalised for four other sites of exposure (Athens, Krakow, Prague and Rome). The analytical form of this model was interpreted in terms of a physical description of the soiling phenomenon. Some of the model coefficients were different from one site to another, depending on the specific environment of exposure (air pollution levels, meteorological factors), while the other ones were rather equivalent. The analysis of the model coefficients, on the one hand, led to an estimation of the period after which soiling is close to its saturation level, and on the other hand, it will permit to correlate these coefficients to the environmental factors, in order to select the most appropriate ones for building dose-response functions for soiling, with broad geographical application.