Namomechanical Imaging and Nanoscale Elastic Modulus Measurements of SnO2 Nanobelts

Environmentally Friendly Synthesis of Poly(3,4-Ethylenedioxythiophene): Poly(Styrene Sulfonate)/SnO2 Nanocomposites

Conductive poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (PEDOT:PSS) is widely used for practical applications such as energy conversion and storage devices owing to its good flexibility, processability, high electrical conductivity, and superior optical transparency, among others. However, its hygroscopic character, short durability, and poor thermoelectric performance compared to inorganic counterparts has greatly limited its high-tech applications. In this work, PEDOT:PSS/SnO2 nanocomposites have been prepared via a simple, low cost, environmentally friendly method without the use of organic solvents or compatibilizing agents. Their morphology, thermal, thermoelectrical, optical, and mechanical properties have been characterized. Electron microscopy analysis revealed a uniform dispersion of the SnO2 nanoparticles, and the Raman spectra revealed the existence of very strong SnO2-PEDOT:PSS interactions. The stiffness and strength of the matrix gradually increased with increasing SnO2 content, up to 120% and 65%, respectively. Moreover, the nanocomposites showed superior thermal stability (as far as 70 °C), improved electrical conductivity (up to 140%), and higher Seebeck coefficient (about 80% increase) than neat PEDOT:PSS. On the other hand, hardly any change in optical transparency was observed. These sustainable nanocomposites show considerably improved performance compared to commercial PEDOT:PSS, and can be highly useful for applications in energy storage, flexible electronics, thermoelectric devices, and related fields.

Thermally driven interfacial dynamics of metal/oxide bilayer nanoribbons

Solid-solid interfacial processes greatly affect the performance of electronic and composite materials, but probing the dynamics of buried interfaces is challenging and often involves lengthy or invasive sample preparation. We show that bilayer nanoribbons-made here of tin dioxide and copper-are convenient structures for observing as-made interfaces as they respond to changing temperature in a transmission electron microscope (TEM). At low temperatures (<200 degrees C), differential thermal expansion causes the bilayers to bend when heated or cooled, with the motion determined by the extent of Cu-SnO(2) epitaxy. At higher temperatures, we are able to watch-in real time and with nanometer resolution-a progression of grain growth, interdiffusion, island formation, solid-state chemical reactions, and melting. This novel TEM geometry is readily applicable to other nanoribbon/coating combinations and is well suited to observing interfacial phenomena driven thermally or by the application of mechanical, electrical, or magnetic forces.