Co–Ce Oxides Supported on SBA-15 for VOCs Oxidation

Synthesis, Surface Modification and Magnetic Properties Analysis of Heat-Generating Cobalt-Substituted Magnetite Nanoparticles

Here, we present the results of the synthesis, surface modification, and properties analysis of magnetite-based nanoparticles, specifically Co0.047Fe2.953O4 (S1) and Co0.086Fe2.914O4 (S2). These nanoparticles were synthesized using the co-precipitation method at 80 °C for 2 h. They exhibit a single-phase nature and crystallize in a spinel-type structure (space group Fd3¯m). Transmission electron microscopy analysis reveals that the particles are quasi-spherical in shape and approximately 11 nm in size. An observed increase in saturation magnetization, coercivity, remanence, and blocking temperature in S2 compared to S1 can be attributed to an increase in magnetocrystalline anisotropy due to the incorporation of Co ions in the crystal lattice of the parent compound (Fe3O4). The heating efficiency of the samples was determined by fitting the Box-Lucas equation to the acquired temperature curves. The calculated Specific Loss Power (SLP) values were 46 W/g and 23 W/g (under HAC = 200 Oe and f = 252 kHz) for S1 and S2, respectively. Additionally, sample S1 was coated with citric acid (Co0.047Fe2.953O4@CA) and poly(acrylic acid) (Co0.047Fe2.953O4@PAA) to obtain stable colloids for further tests for magnetic hyperthermia applications in cancer therapy. Fits of the Box-Lucas equation provided SLP values of 21 W/g and 34 W/g for CA- and PAA-coated samples, respectively. On the other hand, X-ray photoelectron spectroscopy analysis points to the catalytically active centers Fe2+/Fe3+ and Co2+/Co3+ on the particle surface, suggesting possible applications of the samples as heterogeneous self-heating catalysts in advanced oxidation processes under an AC magnetic field.

Coupling effect of reaction conditions on the catalytic activity of Cu-Mn composite oxide catalysts for toluene

Volatile organic compounds (VOCs) are one of the major components of air pollution. Catalytic combustion is a promising technology for the treatment of VOCs and at its center is the preparation of efficient and cheap catalysts. In this study, by loading copper (Cu) and manganese (Mn) on Santa Barbara Amorphous-15 (SBA-15) molecular sieve, the Cux-Mny/SBA-15 (x = 1, 2; y = 1, 2) composite metal oxide catalyst was prepared using the equal volume impregnation method. Their performance in the toluene catalytic combustion reaction was investigated by adjusting the molar ratio (x : y), and the loading of Cu and Mn. The results of the Brunner-Emmett-Teller (BET), X-ray diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS) analyses show that the CuMnO spinel phase can be detected in the Cu-Mn composite metal oxide catalyst doped with a low concentration of Cu. The overall rod-like structure of the fibrous network structure provides a large specific surface area, and the particle crystallinity is low and the dispersion is good. Due to the synergistic effect of Cu and Mn, the greater the amount of Mn3+ and adsorbed oxygen species (Oads) that are available, and the higher the turnover frequency (TOF) value, the better and more superior catalytic performance and excellent stability is obtained, when compared with the single-component oxides used in toluene catalytic combustion. After a continuous catalytic reaction for 12 h, the toluene conversion rate remained above 95%. The coupling effect of the catalytic reaction temperature and concentration of oxygen on the catalytic combustion of toluene was also studied. At a low reaction temperature (<250 °C), the increase of the concentration of oxygen played a superior role in promoting the conversion of toluene. The kinetic analysis of the toluene catalytic combustion process showed that the catalytic combustion of toluene by Cu-Mn/SBA-15 followed both the Mars-Van Krevelen (MVK) and Langmuir-Hinshelwood (L-H) reaction mechanisms. With the increase of the Oads amount caused by the decrease of the Cu ratio, the proportion of the L-H reaction mechanism increases.

Reaction Kinetics and Mechanism of VOCs Combustion on Mn-Ce-SBA-15

A propane combustion catalyst based on Mn and Ce and supported by SBA-15 was prepared by the “two-solvents’’ method aiming at the possible application in catalytic converters for abatement of alkanes in waste (exhaust) gases. The catalyst characterization was carried out by SAXS, N2-physisorption, XRD, TEM, XPS, EPR and H2-TPR methods. The catalysts’ performance was evaluated by tests on the combustion of methane, propane and butane. The reaction kinetics investigation showed that the reaction orders towards propane and oxygen were 0.7 and 0.1, respectively. The negative reaction order towards the water (−0.3) shows an inhibiting effect on the water molecules. Based on the data from the instrumental methods, catalytic experiments and mathematic modeling of the reaction kinetics, one may conclude that the Mars–van Krevelen type of mechanism is the most probable for the reaction of complete propane oxidation over single Mn and bi-component Mn–Ce catalysts. The fine dispersion of manganese and cerium oxide and their strong interaction inside the channels of the SBA-15 molecular sieve leads to the formation of difficult to reduce oxide phases and consequently, to lower catalytic activity compared to the mono-component manganese oxide catalyst. It was confirmed that the meso-structure was not modified during the catalytic reaction, thus it can prevent the agglomeration of the oxide particles.

Mechanochemically Prepared Co3O4-CeO2 Catalysts for Complete Benzene Oxidation

Considerable efforts to reduce the harmful emissions of volatile organic compounds (VOCs) have been directed towards the development of highly active and economically viable catalytic materials for complete hydrocarbon oxidation. The present study is focused on the complete benzene oxidation as a probe reaction for VOCs abatement over Co3O4-CeO2 mixed oxides (20, 30, and 40 wt.% of ceria) synthesized by the more sustainable, in terms of less waste, less energy and less hazard, mechanochemical mixing of cerium hydroxide and cobalt hydroxycarbonate precursors. The catalysts were characterized by BET, powder XRD, H2-TPR, UV resonance Raman spectroscopy, and XPS techniques. The mixed oxides exhibited superior catalytic activity in comparison with Co3O4, thus, confirming the promotional role of ceria. The close interaction between Co3O4 and CeO2 phases, induced by mechanochemical treatment, led to strained Co3O4 and CeO2 surface structures. The most significant surface defectiveness was attained for 70 wt.% Co3O4-30 wt.% CeO2. A trend of the highest surface amount of Co3+, Ce3+ and adsorbed oxygen species was evidenced for the sample with this optimal composition. The catalyst exhibited the best performance and 100% benzene conversion was reached at 200 °C (relatively low temperature for noble metal-free oxide catalysts). The catalytic activity at 200 °C was stable without any products of incomplete benzene oxidation. The results showed promising catalytic properties for effective VOCs elimination over low-cost Co3O4-CeO2 mixed oxides synthesized by simple and eco-friendly mechanochemical mixing.