Low-Temperature Electrocatalytic Conversion of CO2 to Liquid Fuels: Effect of the Cu Particle Size

Nanostructured Copper-Based Electrodes Electrochemically Synthesized on a Carbonaceous Gas Diffusion Membrane with Catalytic Activity for the Electroreduction of CO2

In this work, four different 4 cm2-sized nanostructured Cu-based electrocatalysts have been designed by a one-step electrodeposition process of Cu metal on a three-dimensional carbonaceous membrane. One consisted of Cu0, and the other three were obtained by further simple oxidative treatments. Morphological, structural, and electrochemical investigations on the four materials were carried out by scanning electron microscopy, Raman spectroscopy, X-ray diffraction, linear sweep voltammetry, and potential-controlled electrolysis. All the electrocatalysts showed promising catalytic activities toward CO2 electroreduction in liquid phase, with a remarkable selectivity toward acetic acid achieved when using the oxidized materials. In particular, the best electrocatalytic activity was observed for the Cu2O-Cu0 catalyst, working at a relatively low potential (-0.4 V vs RHE), which exhibited a stable and low current density of 0.46 mA cm-2 and a productivity of 308 μmol gcat-1 h-1. These results were attributed to the nanostructured morphology that is characterized by many void spaces and by a high surface area, which should guarantee a large number of CuI and Cu0 catalytic active sites. Moreover, kinetic analyses and preliminary studies about catalyst regeneration highlighted the stability of the best-performing catalyst.

Tuning the Catalytic Performance of Cobalt Nanoparticles by Tungsten Doping for Efficient and Selective Hydrogenation of Quinolines under Mild Conditions

Non-noble bimetallic CoW nanoparticles (NPs) partially embedded in a carbon matrix (CoW@C) have been prepared by a facile hydrothermal carbon-coating methodology followed by pyrolysis under an inert atmosphere. The bimetallic NPs, constituted by a multishell core-shell structure with a metallic Co core, a W-enriched shell involving Co7W6 alloyed structures, and small WO3 patches partially covering the surface of these NPs, have been established as excellent catalysts for the selective hydrogenation of quinolines to their corresponding 1,2,3,4-tetrahydroquinolines under mild conditions of pressure and temperature. It has been found that this bimetallic catalyst displays superior catalytic performance toward the formation of the target products than the monometallic Co@C, which can be attributed to the presence of the CoW alloyed structures.

Electrochemical reduction of CO2 using Germanium-Sulfide-Indium amorphous glass structures

The research in electrochemical reduction of CO₂ is shifting towards the discovery of new and novel materials. This study shows a new class of material, that of Ge-S-In chalcogenide glass, to be active for reduction of CO₂ in aqueous solutions. Experiments were conducted with bulk and particle form of the material, yielding different product for each structural form. Faradaic efficiency of upto 15% was observed in bulk form for CO production while formic acid with up to 26.1 % faradaic efficiency was measured in powder form. Chalcogenide studies have focused primarily on the photoelectrochemical reduction however these results provide a strong merit for introducing metal in chalcogenide glass structures for electrochemical reduction of CO₂. The activity for CO₂ reduction and the change in product selectivity reflects that further efforts to improve the glass structures can be undertaken in order to increase the faradaic efficiency and selectivity of the products.

Emissions Control Catalysis

Important advances have been achieved over the past years in agriculture, industrial technology, energy, and health, which have contributed to human well-being [...]