Evaluation of the Bonding Strength between Various Dental Zirconia Models and Human Teeth for Dental Posts through In Vitro Aging Tests

Comparative analysis of bonding strength between enamel and overlay of varying thicknesses following an aging test

Abstract

Background/purpose: Overlay restorations can be used clinically as a treatment option to preserve natural dentine. However, whether the residual enamel thickness and overlay thickness affect the adhesion between the restoration and tooth is still unknown. This study was to investigate effects of the overlay thickness and residual enamel thickness on bonding strength.

Materials and methods

Overlays of different thicknesses were prepared with natural teeth which had 2, 4, and 6 mm of occlusal reduction (n = 10). Specimens were subjected to 10,000 cycles in water at 5-55 °C, and finally compressive strength tests were used to evaluate the bonding strength.

Results

All groups showed good bond strength (P > 0.05). The overlay restorations of different thicknesses reduced the preparation amount by 30.3%-7.2% and significantly preserved more of the tooth structure (P < 0.005). Compared to the control group, the overlay restoration increased the marginal fitness by about 0.67-0.88 times. The thermal cycling indicated that the decrease in the maximum bearing stress was due to the aging of the ceramic itself. Therefore, the thickness of the overlay had a greater influence on the compressive strength than the bond strength.

Conclusion

Based on the above this study recommends an overlay thickness of at least 2 mm in clinical practice. The aging test confirmed that adhesion between the overlay and teeth was quite firm and stable. This shows that a stable adhesive effect of the overlay can be used as a treatment option for preserving a greater amount of a tooth's structure.

Calcium Phosphate Nanoclusters for the Repair of Tooth Enamel Erosion

The artificial repair of tooth enamel is still an urgent requirement because it has a complicated and well-arranged structure. Herein, calcium phosphate nanoclusters (CaP NCs) were synthesized, via a facile approach, for application in the repair of tooth enamel erosion. Structural and optical characterizations validated the successful preparation of spherical CaP NCs, with an average size of 2.1 ± 0.11 nm. By evaporating the ethanol and triethylamine (TEA) solvents, pure CaP was produced, which was further used to repair the tooth enamel. Simulated caries lesions were achieved via phosphoric acid etching to cause damage to enamel rods. After repair, the damaged enamel rods were directly covered with CaP. According to microhardness testing, after repair with CaP NCs, the hardness value of the tooth enamel with acid etching increased to a similar level to that of normal tooth enamel. The results of the microhardness test indicated that CaP NCs revealed great potential for repairing tooth enamel erosion. Our work demonstrates a promising potential for treating the early stage of tooth erosion with CaP NCs. Based on these findings, we believe that stable CaP NCs can be employed as a precursor for the tunable, effective repair of tooth enamel in the near future.