Corrosion of the Welded Aluminium Alloy in 0.5 M NaCl Solution. Part 1: Specificity of Development

A Superior Corrosion Protection of Mg Alloy via Smart Nontoxic Hybrid Inhibitor-Containing Coatings

The increase of corrosion resistance of magnesium and its alloys by forming the smart self-healing hybrid coatings was achieved in this work in two steps. In the first step, using the plasma electrolytic oxidation (PEO) treatment, a ceramic-like bioactive coating was synthesized on the surface of biodegradable MA8 magnesium alloy. During the second step, the formed porous PEO layer was impregnated with a corrosion inhibitor 8-hydroxyquinoline (8-HQ) and bioresorbable polymer polycaprolactone (PCL) in different variations to enhance the protective properties of the coating. The composition, anticorrosion, and antifriction properties of the formed coatings were studied. 8-HQ allows controlling the rate of material degradation due to the self-healing effect of the smart coating. PCL treatment of the inhibitor-containing layer significantly improves the corrosion and wear resistance and retains an inhibitor in the pores of the PEO layer. It was revealed that the corrosion inhibitor incorporation method (including the number of steps, impregnation, and the type of solvent) significantly matters to the self-healing mechanism. The hybrid coatings obtained by a 1-step treatment in a dichloromethane solution containing 6 wt.% polycaprolactone and 15 g/L of 8-HQ are characterized by the best corrosion resistance. This coating demonstrates the lowest value of corrosion current density (3.02 × 10−7 A cm−2). The formation of the hybrid coating results in the corrosion rate decrease by 18 times (0.007 mm year−1) as compared to the blank PEO layer (0.128 mm year−1). An inhibitor efficiency was established to be 83.9%. The mechanism of corrosion protection of Mg alloy via smart hybrid coating was revealed.

The Effect of Smart PEO-Coatings Impregnated with Corrosion Inhibitors on the Protective Properties of AlMg3 Aluminum Alloy

The protective coating with a self-organized microtubular structure was formed using plasma electrolytic oxidation (PEO) on AlMg3 aluminum alloy in the tartrate-fluoride electrolyte. This protective layer was further modified using corrosion inhibitors of the azole group (1,2,4-triazole, benzotriazole) and polymer material (polyvinilidene fluoride, PVDF). X-ray diffraction analysis and scanning electron microscopy with energy dispersive spectroscopy were used to study the morphology and composition of the obtained oxide coatings. The presence of the inhibitor in the PEO-layer was confirmed using micro-Raman spectroscopy and X-ray photoelectron spectroscopy. The level of corrosion protection of formed coatings as well as the effect of loaded inhibitors on the anticorrosion efficiency was evaluated using electrochemical impedance spectroscopy (EIS) and localized scanning techniques (SVET/SIET). The coating impregnation with corrosion inhibitors of the azole group significantly improves the corrosion characteristics of the material. Impregnation of the base PEO-layer with 1,2,4-triazole during 24 h results in a 36 times increase in the impedance modulus measured at the lowest frequency (|Z|_f=0.1Hz). Additional sealing of impregnated coating with polymer improves the corrosion stability of the treated material. On the base of the obtained data, the optimal way of protective inhibitor- and polymer-containing formation using surface treatment was suggested. The best barrier properties were established for hybrid coatings obtained by the immersion of a PEO-coated sample in 1,2,4-triazole solution for 24 h and following spraying the PVDF solution. The value of |Z|_f=0.1Hz for this protective layer increased by more than two orders of magnitude in comparison with the base PEO-layer. The three-stage mechanism of corrosion inhibition of the sample with smart inhibitor-containing coating was established.

Optimization of Physicochemical Parameters during the Electrocoagulation Cadmium Elimination

The increased use of fertilizers from phosphates in agriculture generates water pollution by heavy metals contained in these phosphates at levels higher than the standards. In our study, we used a cadmium nitrate Cd(NO3)2 solution to simulate artificially polluted water, whose decontamination efficiency will be evaluated by an electrocoagulation/flotation process. During this work, we aimed to optimize the electrocoagulation process according to the following factors: initial pH of the solution, density of the electrolysis current, cell time, and nature of the supporting electrolyte and its concentration. The criteria adopted during the optimization of the process are relatively different from those used in similar studies. Indeed, we have tried to achieve maximum efficiency and also seeking to minimize costs and facilitate implementation. We achieved a 98% Cd removal efficiency from the solution at pH = 7, J = 6.25 A/m2, t = 10 min, and [K2SO4] = 0.01 M. In addition, during the characterization of the flocs obtained as a supernatant, we first highlighted the presence of Cd in this gelatinous body and then the relatively easy volatility of Cd as well as that of aluminum oxide (Al2O3).

Effect of Microstructure on the Corrosion Resistance of TIG Welded 1579 Alloy

The paper studies microstructure, chemical composition and corrosion activity of the tungsten inert gas welded joint of the Al-Mg-Sc alloy. An intensive corrosion attack of the heat affected zone (HAZ) was found due to precipitation of secondary phases at recrystallized grain boundaries. The ccorrosion process initiated along the boundary of α-Al grains, where a high concentration of anodic (Mg₂Si and Mg₂Al₃) and cathodic phases ((MnFe)Al₆) was observed. Increased temperatures during welding led to coalescence of the anodic phases in HAZ. Additionally, HAZ was found to be enriched with hard intermetallic compounds (Mg₂Si and (MnFe)Al₆). This area had a higher microhardness (930 MPa) compared to base metal (BM, 895 MPa) and fusion zone (FZ, 810 MPa). The volume fraction of secondary phases was 26% in BM, 28% in FZ and 38% in HAZ. The average grain size increased in the following order: (9 ± 3) µm (BM) < (16 ± 3) µm (HAZ) < (21 ± 5) µm (FZ). A plasma electrolytic oxidation (PEO) coating of aluminum-based material was applied to protect the weld from oxidation. The PEO-coating provided a high corrosion protection in the aggressive Cl⁻-containing environment.

Corrosion of the Welded Aluminium Alloy in 0.5 M NaCl Solution. Part 2: Coating Protection

The high electrochemical activity of the aircraft 1579 aluminium alloy with a welded joint and the necessity of the coating formation to protect this material against corrosion as well as to increase the stability of the weld interface in the corrosive medium has been previously established. In this work, two suggested methods of protective coating formation based on plasma electrolytic oxidation (PEO) in tartrate-fluoride electrolyte significantly increased the protective properties of the welded joint area of the 1579 Al alloy. The electrochemical properties of the formed surface layers have been investigated using SVET (scanning vibrating electrode technique) and SIET (scanning ion-selective electrode technique), EIS (electrochemical impedance spectroscopy), OCP (open circuit potential), and PDP (potentiodynamic polarization) in 0.5 M NaCl. The less expressed character of the local electrochemical processes on the welded 1579 Al alloy with the composite coating in comparison with the base PEO-layer has been established. Polymer-containing coatings obtained using superdispersed polytetrafluoroethylene (SPTFE) treatment are characterized by the best possible protective properties and prevent the material from corrosion destruction. Single SPTFE treatment enables one to increase PEO-layer protection by 5.5 times. The results of this study indicate that SVET and SIET are promising to characterize and to compare corrosion behaviour of coated and uncoated samples with a welded joint in chloride-containing media.