Binary Oxides Prepared by Microwave-Assisted Solution Combustion: Synthesis, Characterization and Catalytic Activity

Synthesis, Characterization and Catalytic Activity of Ternary Oxide Catalysts Using the Microwave-Assisted Solution Combustion Method

Ni-Co-Al, Ni-Cu-Al and Co-Cu-Al ternary oxide catalysts, with a fixed 5 wt% transition metal loading, were prepared by the microwave-assisted solution combustion method and tested in CO oxidation. The bulk and surface properties of the catalysts were investigated, using XRD, N2 adsorption-desorption, SEM, XPS and TEM techniques. XRD, XPS and TEM results revealed that nickel and cobalt were present as spinels on the surface and in the bulk. Differently, copper was preferentially present in "bulk-like" CuO-segregated phases. No interaction between the couples of transition metal species was detected, and the introduction of Cu-containing precursors into the Ni-Al or Co-Al combustion systems was not effective in preventing the formation of NiAl2O4 and CoAl2O4 spinels in the Ni- or Co-containing catalysts. Copper-containing catalysts were the most active, indicating that copper oxides are the effective active species for improving the CO oxidation activity.

Influence of the Fuel/Oxidant Ratio on the Elaboration of Binary Oxide Catalyst by a Microwave-Assisted Solution Combustion Method

Three series of binary metal oxide catalysts containing Ni, Cu, or Co oxides were prepared, fully characterized and tested in CO oxidation. The catalysts, with a constant transition metal loading of 10 wt%, were prepared from metal nitrates and urea mixtures by a microwave-assisted solution combustion method. The RV/OV ratio, corresponding to the stoichiometry of the reactants, calculated from their elemental oxidizing and reducing valences, was varied. In order to modify the redox character of the synthesis medium from the quantity of urea; an excess of urea was used for attaining reducing conditions, while a deficit of urea shifted the medium to oxidizing conditions. Three RV/OV ratios (0.9, 1.0, and 1.1) were selected to elaborate the different binary metal oxide catalysts, nine oxide catalysts were synthesized. Then, the influence of the stoichiometry (RV/OV ratio) on the bulk and surface properties of the binary metal oxide catalysts was investigated. Similarly, the influence of the RV/OV ratio on the CO oxidation activity was discussed and the optimal value of RV/OV ratio was identified. The results show that the increasing of the RV/OV ratio from 0.9 to 1.1, particularly in Ni- and Co-containing catalysts, induces stronger metal-aluminum interactions, in the form of aluminates phases, and that are correlated to the dramatic reduction of the CO oxidation activity. The best physicochemical properties and highest catalytic activities were achieved with the catalysts prepared in redox systems stoichiometrically balanced (RV/OV = 1). The Cu-containing catalysts presented the best catalytic activities in CO oxidation.

Electronic Percolation Threshold of Self-Standing Ag-LaCoO3 Porous Electrodes for Practical Applications

Perovskite LaCoO3 materials have various applications, from selective permeable membranes and gas sensing devices to water splitting applications. However, the intrinsic electrical resistivity of the perovskite limits the applicative potential. To overcome that, Ag powder was used with LaCoO3 to obtain porous composite electrodes with enhanced conductivities. For that, a series of composite Ag-LaCoO3 powders were prepared into pellets and pre-sintered at various temperatures up to 1000 ∘C. Their structural properties and morphology were investigated by X-ray diffraction and scanning electron microscopy. The electronic transport of compacted specimens was studied by impedance spectroscopy. The results indicate that the presence of Ag acts as pre-sintering additive to obtain porous electrodes, with porosity values as high as 40% at 50 vol. % Ag. Moreover, the overall electrical resistivity of the composite electrodes varied well over four orders of magnitude. The results are discussed within the generalized Bruggeman theory for effective media comprising arbitrarily shaped metallic and semiconducting inclusions.