Research of Wood Waste as a Potential Filler for Loose-Fill Building Insulation: Appropriate Selection and Incorporation into Polyurethane Biocomposite Foams

Fire-Retardant Flexible Foamed Polyurethane (PU)-Based Composites: Armed and Charmed Ground Tire Rubber (GTR) Particles

Inadequate fire resistance of polymers raises questions about their advanced applications. Flexible polyurethane (PU) foams have myriad applications but inherently suffer from very high flammability. Because of the dependency of the ultimate properties (mechanical and damping performance) of PU foams on their cellular structure, reinforcement of PU with additives brings about further concerns. Though they are highly flammable and known for their environmental consequences, rubber wastes are desired from a circularity standpoint, which can also improve the mechanical properties of PU foams. In this work, melamine cyanurate (MC), melamine polyphosphate (MPP), and ammonium polyphosphate (APP) are used as well-known flame retardants (FRs) to develop highly fire-retardant ground tire rubber (GTR) particles for flexible PU foams. Analysis of the burning behavior of the resulting PU/GTR composites revealed that the armed GTR particles endowed PU with reduced flammability expressed by over 30% increase in limiting oxygen index, 50% drop in peak heat release rate, as well as reduced smoke generation. The Flame Retardancy Index (FRI) was used to classify and label PU/GTR composites such that the amount of GTR was found to be more important than that of FR type. The wide range of FRI (0.94-7.56), taking Poor to Good performance labels, was indicative of the sensitivity of flame retardancy to the hybridization of FR with GTR components, a feature of practicality. The results are promising for fire protection requirements in buildings; however, the flammability reduction was achieved at the expense of mechanical and thermal insulation performance.

Recycled Waste as Polyurethane Additives or Fillers: Mini-Review

The intensive development of the polyurethanes industry and limited resources (also due to the current geopolitical situation) of the raw materials used so far force the search for new solutions to maintain high economic development. Implementing the principles of a circular economy is an approach aimed at reducing the consumption of natural resources in PU production. This is understood as a method of recovery, including recycling, in which waste is processed into PU, and then re-used and placed on the market in the form of finished sustainable products. The effective use of waste is one of the attributes of the modern economy. Around the world, new ways to process or use recycled materials for polyurethane production are investigated. That is why innovative research is so important, in which development may change the existing thinking about the form of waste recovery. The paper presents the possibilities of recycling waste (such as biochar, bagasse, waste lignin, residual algal cellulose, residual pineapple cellulose, walnut shells, silanized walnut shells, basalt waste, eggshells, chicken feathers, turkey feathers, fiber, fly ash, wood flour, buffing dust, thermoplastic elastomers, thermoplastic polyurethane, ground corncake, Tetra Pak®, coffee grounds, pine seed shells, yerba mate, the bark of Western Red Cedar, coconut husk ash, cuttlebone, glass fibers and mussel shell) as additives or fillers in the formulation of polyurethanes, which can partially or completely replace petrochemical raw materials. Numerous examples of waste applications of one-component polyurethanes have been given. A new unexplored niche for the research on waste recycling for the production of two components has been identified.

Sapropel as a Binding Material for Wood Processing Waste in the Development of Thermal Insulation Biocomposite

When developing new innovative building materials, their performance characteristics as well as their environmental friendliness are important. It is difficult to produce a fully ecological material for building envelopes, because there is a lack of ecological binding materials on the market, good binding materials are very expensive, and cheaper ones have poorer adhesive properties and performance characteristics. In this work, natural organic sapropel was used as an ecological binder. Before use, an organic sapropel was additionally mechanically activated. Its activation efficiency was evaluated on the basis of consistency and tensile strength. Sapropel activation increased its consistency from 112 to 168 mm and its tensile strength from 466 to 958 kPa. Wood processing waste was used as a filler for the thermal insulation biocomposite. Additionally, the wood waste was chopped to regulate the density and main performance properties of the biocomposite. The density of the biocomposite was also regulated using different amounts of sapropel and the degree of compaction of the composite mixture. In this work, the influence of the amount of sapropel, the level of compression of the biocomposite mixture, and the size of the wood waste particles on the thermal conductivity and compressive stress of the biocomposite was analyzed. It was found that the compression level had the greatest influence on both the compressive stress and thermal conductivity, up to 12 times and 43.3%, respectively.

Role of hemp fiber addition on thermal stability, heat insulation, air permeability and cellular structural features of rigid polyurethane foam

In this current study, rigid polyurethane foams (RPUFs) composites were prepared using different percentage (3, 6, 9 and 12%) of the hemp fibers via one-shut one-step polymerization method. The influences of the hemp fiber addition on the RPUFs were investigated meticulously by means of Fourier-transform infrared spectroscopy (FTIR), thermo gravimetric analysis (TGA), thermal conductivity measurement and scanning electron microscopy (SEM) techniques by evaluating the alternations in the chemical structures of the component, thermal stability, apparent density, insulation performance and cellular topology of the produced samples. The structural analysis revealed that there existed the strong secondary chemical bonds between the functional groups belonging to the components and, depending on that, the improvement in the thermal stability of the foam samples was recorded accompanied by the formation of the better interfacial adhesion. Furthermore, thermal conductivity values of the hemp fiber-loaded RPUFs were observed to increase regularly with the increasing of the content level of the hemp fibers. This was explained by enhancement in the bulk phase conduction level depending of the apparent density rising, reduction in CO2 concentration inside cells as well as the formation of the distorted cellular structures. The obtained air permeability results displayed that the hemp fibers incorporated successfully with RPUF structure, which provides the occurrence of the novel micro barriers and pathways limiting the passage of the air throughout the matrix. The taken scanning electron microscopy images also indicated that the cellular morphology and dimensional stability of the produced foams affected negatively by the hemp fiber addition. At high contents, the wrinkled, non-uniform and irregular cellular structures were observed with ruptured and collapsed walls and struts.

One More Step towards a Circular Economy for Thermal Insulation Materials-Development of Composites Highly Filled with Waste Polyurethane (PU) Foam for Potential Use in the Building Industry

The rapid development of the building sector has created increased demand for novel materials and technologies, while on the other hand resulting in the generation of a severe amount of waste materials. Among these are polyurethane (PU) foams, which are commonly applied as thermal insulation materials. Their management is a serious industrial problem, due to, for example, their complex chemical composition. Although some chemical and thermochemical methods of PU foam recycling are known, their broader use is limited due to requirements related to the complexity and safety of their installation, thus implicating high costs. Therefore, material recycling poses a promising alternative. The incorporation of waste PU foams as fillers for polymer composites could make it possible to take advantage of their structure and performance. Herein, polypropylene-based composites that were highly filled with waste PU foam and modified using foaming agents were prepared and analyzed. Depending on the foam loading and the foaming agent applied, the apparent density of material was reduced by as much as 68%. The efficient development of a porous structure, confirmed by scanning electron microscopy and high-resolution computed micro-tomography, enabled a 64% decrease in the thermal conductivity coefficient. The foaming of the structure affected the mechanical performance of composites, resulting in a deterioration of their tensile and compressive performance. Therefore, developing samples of the analyzed composites with the desired performance would require identifying the proper balance between mechanical strength and economic, as well as ecological (share of waste material in composite, apparent density of material), considerations.

Multifunctional Polyurethane Composites with Coffee Grounds and Wood Sawdust

Currently, the fundamental activity that will allow for the development of an economy with closed circulation is the management of food waste and production waste for the preparation of biocomposites. The use of waste materials of natural origin allows for the creation of innovative composites with improved physicochemical and functional properties. The present investigation concerns the use of coffee grounds (2.5-20 wt.%) and oak sawdust (2.5-20 wt.%) as effective fillers of rigid polyurethane foam. Innovative composite materials, previously indebted in the literature, were subjected to the necessary analyses to determine the application abilities: processing times, free density, water absorption, dimensional stability, mechanical properties (compressive strength), thermal conductivity, morphology, and flame resistance. The results with respect to the mechanical tests turned out to be the key. Increasing the number of coffee additives has a positive effect on the compressive strength. The addition of this filler in the range of 5-15 wt.% increased the compressive strength of the composites, 136-139 kPa, compared to the reference sample, 127 kPa. The key parameter analysed was thermal conductivity. The results obtained were in range of the requirements, that is, 0.022-0.024 W/m·K for all used amounts of fillers 2.5-20 wt.%. This is extremely important since these materials are used for insulation purposes. The results of the burning-behaviour test have confirmed that the addition of renewable materials does not negatively affect the fire resistance of the received foams; the results were obtained analogously to those obtained from the reference sample without the addition of fillers. The height of the flame did not exceed 17 cm, while the flame decay time was 17 s for the reference sample and the composite with coffee grounds and 18 s for the composite with oak sawdust. In this work, the practical application of bioorganic waste as an innovative filler for the insulation of flooded polyurethane foam is described for the first time. The introduction of fillers of natural origin into the polymer matrix is a promising method to improve the physicochemical and functional properties of rigid polyurethane foams. Composites modified with coffee grounds and sawdust are interesting from a technological, ecological, and economic point of view, significantly increasing the range of use of foam in various industries.

Wood Flour Modified by Poly(furfuryl alcohol) as a Filler in Rigid Polyurethane Foams: Effect on Water Uptake

The use of lignocellulosic fillers in rigid polyurethane foams (RPUFs) has been receiving great attention due to their good mechanical and insulation properties and the high sustainable appeal of the obtained cellular polymers, although high water uptakes are found in most of these systems. To mitigate this detrimental effect, RPUFs filled with wood flour (2.5% wt) were fabricated with the addition of furfuryl alcohol (FA) to create a polymer grafted with the wood filler. Two concentrations of FA (10 wt% and 15 wt%) were investigated in relation to the wood flour, and the RPUFs were characterized for cell morphology, density, compressive properties, thermal stability, and water uptake. The introduction of wood flour as a filler decreased the cell size and increased the anisotropy index of the RPUFs and, in addition to that, the FA grafting increased these effects even more. In general, there were no significant changes in both mechanical and thermal properties ascribed to the incorporation of the fillers. On the other hand, a reduction of up to 200% in water uptake was ascribed to the FA-treated fillers.

Comprehensive Enhancement of Prepolymer-Based Flexible Polyurethane Foams' Performance by Introduction of Cost-Effective Waste-Based Ground Tire Rubber Particles

Material innovations in polyurethane (PU) foams should ideally combine performance enhancement, environmental impact limitation, and cost reduction. These goals can be achieved by applying recycled or waste-based materials without broader industrial applications, implicating their low price. Herein, from 5 to 20 parts by weight of ground tire rubber (GTR) particles originated from the recycling of postconsumer car tires were incorporated into a flexible foamed PU matrix as a cost-effective waste-based filler. A two-step prepolymer method of foams manufacturing was applied to maximize the potential of applied formulation changes. The impact of the GTR content on the foams' processing, chemical, and cellular structure, as well as static and dynamic mechanical properties, thermal stability, sound suppression ability, and thermal insulation performance, was investigated. The introduction of GTR caused a beneficial reduction in the average cell diameter, from 263.1 µm to 144.8-188.5 µm, implicating a 1.0-4.3% decrease in the thermal conductivity coefficient. Moreover, due to the excellent mechanical performance of the car tires-the primary application of GTR-the tensile performance of the foams was enhanced despite the disruption of the cellular structure resulting from the competitiveness between the hydroxyl groups of the applied polyols and on the surface of the GTR particles. The tensile strength and elongation at break were increased by 10 and 8% for 20 parts by weight GTR addition. Generally, the presented work indicates that GTR can be efficiently applied as a filler for flexible PU foams, which could simultaneously enhance their performance, reduce costs, and limit environmental impacts due to the application of waste-based material.

Properties of Rigid Polyurethane Foam Filled with Sawdust from Primary Wood Processing

In this study, the possibility of using sawdust, a by-product of primary wood processing, as a filler (WF) for rigid polyurethane (PUR) foams was investigated. The effects of the addition of 5, 10, 15 and 20% of WF particles to the polyurethane matrix on the foaming process, cell structure and selected physical-mechanical properties such as density, thermal conductivity, dimensional stability, water absorption, brittleness, compressive and bending strengths were evaluated. Based on the results, it was found that the addition of WF in the amount of up to 10% does not significantly affect the kinetics of the foam foaming process, allowing the reduction of their thermal conductivity, significantly reducing brittleness and maintaining high dimensional stability. On the other hand, such an amount of WF causes a slight decrease in the compressive strength of the foam, a decrease in its bending strength and an increase in water absorption. However, it is important that in spite of the observed decrease in the values of these parameters, the obtained results are satisfactory and consistent with the parameters of insulation materials based on rigid PUR foam, currently available on the market.

Synthesis and Characterization of Wood Rigid Polyurethane Composites

Incorporating biodegradable reinforcement, such as wood particles, into rigid polyurethane foams (RPUFs) is among the alternatives to reduce their environmental impact. This study aims to assess the effect of different wood particles as reinforcement in RPUFs. Reinforced rigid polyurethane foams are synthesized with milled wood particles of various forms and sizes and commercial polyol and isocyanate. The effect of fiber treatments and mechanical stirring on foams’ properties is also studied. Additional tests on polyisocyanurate foams (PIR) were undertaken to assess the effect of reinforcement on their properties. Mechanical properties are measured to investigate the impact of wood particle reinforcement on the foam. Confocal microscopy and Fourier-transform infrared spectroscopy (FTIR) showed the interaction between the wood fibers and the matrix. Despite the adhesion observed for some fibers, most of the cell walls of RPUFs were punctured by the rigid wood fibers, which explained the decrease in the compressive strength of the composites for manually mixed foams. Mechanical stirring proved to be an efficient method to enhance the reinforcement power of untreated fibers. RPUF foams’ properties showed similar changes when untreated wood flour was introduced to the formula, increasing compressive strength significantly.

Thermal and Sliding Wear Properties of Wood Waste-Filled Poly(Lactic Acid) Biocomposites

In our study, the effects of wood waste content (0, 2.5, 5, 7.5, and 10 wt.%) on thermal and dry sliding wear properties of poly(lactic acid) (PLA) biocomposites were investigated. The wear of developed composites was examined under dry contact conditions at different operating parameters, such as sliding velocity (1 m/s, 2 m/s, and 3 m/s) and normal load (10 N, 20 N, and 30 N) at a fixed sliding distance of 2000 m. Thermogravimetric analysis demonstrated that the inclusion of wood waste decreased the thermal stability of PLA biocomposites. The experimental results indicate that wear of biocomposites increased with a rise in load and sliding velocity. There was a 26-38% reduction in wear compared with pure PLA when 2.5 wt.% wood waste was added to composites. The Taguchi method with L₂₅ orthogonal array was used to analyze the sliding wear behavior of the developed biocomposites. The results indicate that the wood waste content with 46.82% contribution emerged as the most crucial parameter affecting the wear of PLA biocomposites. The worn surfaces of the biocomposites were examined by scanning electron microscopy to study possible wear mechanisms and correlate them with the obtained wear results.

Cost-Effective Fabrication of Modified Palygorskite-Reinforced Rigid Polyurethane Foam Nanocomposites

Integration of nanoclay minerals into rigid polyurethane foams (RPUFs) is a cost-effective solution to enhance foam’s performance via environmental protection technology. In this work, palygorskite/RPUFs nanocomposites (Pal/RPUFNs) with excellent mechanical properties and thermal stability were prepared via a one-step method, using 4,4’-diphenylmethane diisocyanate and polyether polyol as the starting materials, coupled with Pal modified by silane coupling agent KH570. The effects of the modified Pal on the mechanics, morphology, and thermal properties of the nanocomposites were studied systematically. When the content of the modified Pal was 8 wt% of polyether polyol, the elastic modulus and compressive strength of the Pal/RPUFNs were increased by ca. 131% and 97%, respectively. The scanning electron microscopy images indicated that the addition of the modified Pal significantly decreased the cell diameter of the Pal/RPUFNs. The results of thermogravimetric and derivative thermogravimetry analyses revealed that the addition of the modified Pal increased the thermal weight loss central temperature of the Pal/RPUFNs, showing better thermal stability in comparison with the pure RPUFs. A self-made evaluation device was used to estimate the thermal insulation ability of the Pal/RPUFNs. It was found that the small cell size and uniform cellular structure were keys to improving the thermal insulation performance of the RPUFs. The prepared Pal/RPUFNs are expected to have great potential in the field of building insulation.

Bio-Based Rigid Polyurethane Foam Composites Reinforced with Bleached Curauá Fiber

This study aims to evaluate the influence of using a bleached Curauá fiber (CF) as filler in a novel rigid polyurethane foam (RPUF) composite. The influence of 0.1, 0.5 and 1 wt.% of the reinforcements on the processing characteristics, cellular structure, mechanical, dynamic-mechanical, thermal, and flame behaviors were assessed and discussed for RPUF freely expanded. The results showed that the use of 0.5 wt.% of CF resulted in RPUF with smoother cell structure with low differences on the processing times and viscosity for the filled pre-polyol. These morphological features were responsible for the gains in mechanical properties, in both parallel and perpendicular rise directions, and better viscoelastic characteristics. Despite the gains, higher thermal conductivity and lower flammability were reported for the developed RPUF composites, related to the high content of cellulose and hemicellulose on the bleached CF chemical composition. This work shows the possibility of using a Brazilian vegetable fiber, with low exploration for the manufacturing of composite materials with improved properties. The developed RPUF presents high applicability as enhanced cores for the manufacturing of structural sandwich panels, mainly used in civil, aircraft, and marine industries.

Waste Wood Particles from Primary Wood Processing as a Filler of Insulation PUR Foams

A significant part of the work carried out so far in the field of production of biocomposite polyurethane foams (PUR) with the use of various types of lignocellulosic fillers mainly concerns rigid PUR foams with a closed-cell structure. In this work, the possibility of using waste wood particles (WP) from primary wood processing as a filler for PUR foams with open-cell structure was investigated. For this purpose, a wood particle fraction of 0.315–1.25 mm was added to the foam in concentrations of 0, 5, 10, 15 and 20%. The foaming course of the modified PUR foams (PUR-WP) was characterized on the basis of the duration of the process’ successive stages at the maximum foaming temperature. In order to explain the observed phenomena, a cellular structure was characterized using microscopic analysis such as SEM and light microscope. Computed tomography was also applied to determine the distribution of wood particles in PUR-WP materials. It was observed that the addition of WP to the open-cell PUR foam influences the kinetics of the foaming process of the PUR-WP composition and their morphology, density, compressive strength and thermal properties. The performed tests showed that the addition of WP at an the amount of 10% leads to the increase in the PUR foam’s compressive strength by 30% (parallel to foam’s growth direction) and reduce the thermal conductivity coefficient by 10%.