Empirical NOx Removal Analysis of Photocatalytic Construction Materials at Real-Scale

Preparation and Real World Applications of Titania Composite Materials for Photocatalytic Surface, Air, and Water Purification: State of the Art

The semiconducting transition metal oxide TiO2 is a rather cheap and non-toxic material with superior photocatalytic properties. TiO2 thin films and nanoparticles are known to have antibacterial, antiviral, antifungal, antialgal, self, water, and air-cleaning properties under UV or sun light irradiation. Based on these excellent qualities, titania holds great promises in various fields of applications. The vast majority of published field and pilot scale studies are dealing with the modification of building materials or generally focus on air purification. Based on the reviewed papers, for the coating of glass, walls, ceilings, streets, tunnels, and other large surfaces, titania is usually applied by spray-coating due to the scalibility and cost-efficiency of this method compared to alternative coating procedures. In contrast, commercialized applications of titania in medical fields or in water purification are rarely found. Moreover, in many realistic test scenarios it becomes evident that the photocatalytic activity is often significantly lower than in laboratory settings. In this review, we will give an overview on the most relevant real world applications and commonly applied preparation methods for these purposes. We will also look at the relevant bottlenecks such as visible light photocatalytic activity and long-term stability and will make suggestions to overcome these hurdles for a widespread usage of titania as photocalyst.

Ozone Formation during Photocatalytic Oxidation of Nitric Oxides under UV Irradiation with the Use of Commercial TiO2 Photocatalytic Powders

The application of photocatalytic materials has been intensively researched in recent decades. The process of nitric oxide (NO) oxidation during photocatalysis has been observed to result in the formation of nitric dioxide (NO₂). This is a significant factor of the photocatalysis process, as NO₂ is more toxic than NO. However, it has been reported that ozone (O₃) is also formed during the photocatalytic reaction. This study analyzed the formation and oxidationof O₃ during the photocatalytic oxidation of NO under ultraviolet irradiation using commercial photocatalytic powders: AEROXIDE^® TiO₂ P25 by Evonik, KRONOClean^® 7050 by KRONOS^®, and KRONOClean^® 7000 by KRONOS^®. An NO concentration of 100 ppb was assumed in laboratory tests based on the average nitric oxide concentrations recorded by the monitoring station in Warsaw. A mix flow-type reactor was applied in the study, and the appropriateness of its application was verified using a numerical model. The developed model assumed an empty reactor without a photocatalytic material, as well as a reactor with a photocatalytic material at its bottom to verify the gas flow in the chamber. The analysis of the air purification performance of photocatalytic powders indicated a significant reduction of NO and NO_x and typical NO₂ formation. However, no significant formation of O₃ was observed. This observation was verified by the oxidation of pure ozone in the process of photocatalysis. The results indicated the oxidation of ozone concentration during the photocatalytic reaction, but self-decomposition of a significant amount of the gas.

A Study on the Evaluation Methods of Nitrogen Oxide Removal Performance of Photocatalytic Concrete for Outdoor Applications

In Korea, the issue of particulate matter pollution is growing, and many solutions are being developed to deal with it. Photocatalytic technology has been found to be helpful in removing precursors such as nitrogen oxides that cause particulate matter. In a microcosm setup, ISO 22197-1 has been successfully used to quantify the removal of nitrogen oxides from the specimen to which the photocatalyst is applied. However, owing to a lack of suitable tools, on-site measurement of real-scale efficacy is difficult. Depending on the substrate and surrounding circumstances at the application location, the photocatalyst may function at varying levels. Additionally, the expected photocatalytic effect may differ depending on the ambient air quality and sunlight irradiation intensity. This article describes two approaches for studying outdoor concrete photocatalysis. Standard gas measurement and dual-reactor measurement are the recommended evaluation approaches. The standard gas measurement method was found useful for assessing the applied photocatalyst itself as an outcome of field assessment. The performance of photocatalysts at different sites was found to be mutually exclusive and comparable. Over 180 min, on a building roof deck, the NO removal by the standard gas method was 0.68 ppm, whereas, at two shaded locations, the removal amount was 0.51 ppm (side wall) and 0.24 ppm (underpass) for 300 min. The dual reactor measurement approach, on the other hand, was discovered to be one of the most suitable methods for assessing how much of an improvement there has been in the air quality in areas where photocatalysts have been placed.