Highly Porous Carbons Synthesized from Tannic Acid via a Combined Mechanochemical Salt-Templating and Mild Activation Strategy

Scale-Up of Solvent-Free, Mechanochemical Precursor Synthesis for Nanoporous Carbon Materials via Extrusion

The mechanochemical synthesis of nitrogen-rich nanoporous carbon materials has been scaled up using an extruder. Lignin, urea, and K₂ CO₃ were extruded under heat and pressure to yield nanoporous carbons with up to 3500 m²  g^-1 specific surface area after pyrolysis. The route was further broadened by applying different nitrogen sources as well as sawdust as a low-cost renewable feedstock to receive carbons with a C/N ratio of up to 15 depending on nitrogen source and extrusion parameters. The texture of obtained carbons was investigated by scanning electron microscopy as well as argon and nitrogen physisorption, while the chemical structure was analyzed by X-ray photoelectron spectroscopy. The received carbon was tested as a supercapacitor electrode, showing comparable performance to similar ball-mill-synthesized materials. Lastly, the space-time yield was applied to justify the use of a continuous reactor versus the ball mill.

Chemical Activation of Lignocellulosic Precursors and Residues: What Else to Consider?

This paper provides the basis for understanding the preparation and properties of an old, but advanced material: activated carbon. The activated carbons discussed herein are obtained from "green" precursors: biomass residues. Accordingly, the present study starts analyzing the components of biomass residues, such as cellulose, hemicellulose, and lignin, and the features that make them suitable raw materials for preparing activated carbons. The physicochemical transformations of these components during their heat treatment that lead to the development of a carbonized material, a biochar, are also considered. The influence of the chemical activation experimental conditions on the yield and porosity development of the final activated carbons are revised as well, and compared with those for physical activation, highlighting the physicochemical interactions between the activating agents and the lignocellulosic components. This review incorporates a comprehensive discussion about the surface chemistry that can be developed as a result of chemical activation and compiles some results related to the mechanical properties and conformation of activated carbons, scarcely analyzed in most published papers. Finally, economic, and environmental issues involved in the large-scale preparation of activated carbons by chemical activation of lignocellulosic precursors are commented on as well.