Hierarchical Porous Carbon Electrodes with Sponge-Like Edge Structures for the Sensitive Electrochemical Detection of Heavy Metals

Microspherical Titanium-Phosphorus Double Oxide: Hierarchical Structure Development for Sensing Applications

Stable, water-soluble titanium complexed with mandelic acid was used as a precursor for titanium phosphorus double oxide obtained in hydrothermal conditions in the presence of phosphoric acid. Surprisingly, hydrolysis of organic complexes provided a microstructured sphere with narrow size distribution, low aggregation and a small fraction of morphological irregularities. Obtained microspheres had a complex structure comprised of flakes, whose size could be manipulated with temperature conditions. Samples were found to be electrochemically active against sulcotrione, a well-recognized herbicide. Electrochemical sensors based on the synthesized microspheres were successfully adapted for natural water reservoir analysis and exhibited low levels of detection of 0.61 µM, limit of quantification of 1.86 µM, wide dynamic linear range from 2 to 200 µM, good selectivity, excellent reproducibility and in-time stability.

Batch Nanofabrication of Suspended Single 1D Nanoheaters for Ultralow-Power Metal Oxide Semiconductor-Based Gas Sensors

The demand for power-efficient micro-and nanodevices is increasing rapidly. In this regard, electrothermal nanowire-based heaters are promising solutions for the ultralow-power devices required in IoT applications. Herein, a method is demonstrated for producing a 1D nanoheater by selectively coating a suspended pyrolyzed carbon nanowire backbone with a thin Au resistive heater layer and utilizing it in a portable gas sensor system. This sophisticated nanostructure is developed without complex nanofabrication and nanoscale alignment processes, owing to the suspended architecture and built-in shadow mask. The suspended carbon nanowires, which are batch-fabricated using carbon-microelectromechanical systems technology, maintain their structural and functional integrity in subsequent nanopatterning processes because of their excellent mechanical robustness. The developed nanoheater is used in gas sensors via user-designable localization of the metal oxide semiconductor nanomaterials onto the central region of the nanoheater at the desired temperature. This allows the sensing site to be uniformly heated, enabling reliable and sensitive gas detection. The 1D nanoheater embedded gas sensor can be heated immediately to 250 °C at a remarkably low power of 1.6 mW, surpassing the performance of state-of-the-art microheater-based gas sensors. The presented technology offers facile 1D nanoheater production and promising pathways for applications in various electrothermal devices.

MOF-derived nanoporous carbons with diverse tunable nanoarchitectures

Metal-organic frameworks (MOFs), or porous coordination polymers, are crystalline porous materials formed by coordination bonding between inorganic and organic species on the basis of the self-assembly of the reacting units. The typical characteristics of MOFs, including their large specific surface areas, ultrahigh porosities and excellent thermal and chemical stabilities, as well as their great potential for chemical and structural modifications, make them excellent candidates for versatile applications. Their poor electrical conductivity, however, has meant that they have not been useful for electrochemical applications. Fortuitously, the direct carbonization of MOFs results in a rearrangement of the carbon atoms of the organic units into a network of carbon atoms, which means that the products have useful levels of conductivity. The direct carbonization of zeolitic imidazolate framework (ZIF)-type MOFs, particularly ZIF-8, has successfully widened the scope of possible applications of MOFs to include electrochemical reactions that could be used in, for example, energy storage, energy conversion, electrochemical biosensors and capacitive deionization of saline water. Here, we present the first detailed protocols for synthesizing high-quality ZIF-8 and its modified forms of hollow ZIF-8, core-shell ZIF-8@ZIF-67 and ZIF-8@mesostuctured polydopamine. Typically, ZIF-8 synthesis takes 27 h to complete, and subsequent nanoarchitecturing procedures leading to hollow ZIF-8, ZIF-8@ZIF-67 and ZIF-8@mPDA take 6, 14 and 30 h, respectively. The direct-carbonization procedure takes 12 h. The resulting nanoporous carbons are suitable for electrochemical applications, in particular as materials for supercapacitors.