Pit and fissure nanocomposite sealants reinforced with organically modified montmorillonite: A study of their mechanical properties, surface roughness and color stability

Influence of incorporation of nanostructured silver vanadate decorated with silver nanoparticles on roughness, microhardness, and color change of pit and fissure sealants

Objective

The aim of this study was to evaluate the roughness, hardness, and color change of pit and fissure sealants of two commercial brands (Fluroshield ™ and Ultraseal XT ™) incorporated with nanostructured silver vanadate nanomaterial decorated with silver nanoparticles (β-AgVO3) in concentrations (0% - control, 2.5% and 5%).

Material and methods

Two commercial brands Fluroshield TM and Ultraseal XT ™ were used to make the samples with dimensions of 6 × 6 × 4 mm. The control group was made according to the manufacturer's instructions and in the groups with the addition of β-AgVO3, the nanomaterial was added proportionally by mass at percentages of 2.5% and 5%. Roughness properties were evaluated using a 3D Laser Confocal Microscope (n = 10), Knoop microhardness by Microdurometer (n = 10), and color change by Portable Color Spectrophotometer on the CIEDE2000 system (n = 10). Data were evaluated by one-way ANOVA with Bonferroni adjustment and Tukey's mean comparison test at a 5% significance level.

Results

Ultraseal XT ™ sealant roughness showed a significant difference between concentrations with the highest mean for the 5% group (P = 0.010). Regarding the hardness, both sealants showed no significant difference between the groups. Fluroshield ™ sealant showed a significant difference in ΔE00 between the control-2.5% 24.93 (3.49) and control-5% 28.41 (2.58).

Conclusion

It may be concluded that the incorporation of β-AgVO3 influenced the increase in roughness for Ultraseal XT ™ pit and fissure sealant, did not interfere with the microhardness of both sealants, and promoted a change in the color of Fluroshield ™ sealant within clinically acceptable limits.

Do nanofillers provide better physicomechanical properties to resin-based pit and fissure sealants? A systematic review

The purpose of this study was to systematically review the impact of nanofillers on the physicomechanical properties of resin-based pit and fissure sealants (RBS). This review included in vitro studies with full-length English-language articles reporting on the physicomechanical properties of nanofilled RBS until February 2023. PubMed, Web of Sciences, Scopus, and LILACS databases were accessed for literature searches. The review was formulated based on the Preferred Reporting Items for Systematic Review and Meta-Analyses (PRISMA) guidelines and used the Consolidated Standards of Reporting Trials (CONSORT) guidelines and risk of bias Cochrane tool for quality assessment. The search resulted in 539 papers, of which 22 were eligible to be included in the review. Inorganic, polymeric, core-shell, and composite nanomaterials were used to reinforce the studied RBS. The inherent nature of the nanomaterial used, its morphology, concentration, and volume used were the primary parameters that determined the nanomaterial's success as a filler in RBS. These parameters also influenced their interaction with the resin matrix, which influenced the final physicomechanical properties of RBS. The use of nanofillers that were non-agglomerated and well dispersed in the resin matrix enhanced the physicomechanical properties of RBS.

Preparation and characterization of dental pit and fissure sealant based on calcium sodium silicate bioactive glasses.. [DOI: 10.21203/rs.3.rs-2453592/v1] [Citation(s) in RCA: 0] [Impact Index Per Article: 0]

This study aimed to prepare a resin based dental sealant loaded with novel bioactive glass formulated from (50 wt% calcium silicate and 50 wt% sodium silicate) with different percentages of fluorapatite. Four glass batches were formulated then characterized using Fourier Transform Infrared Spectroscopy analysis, X-ray powder diffraction analysis and Transmission electron microscopy. Density, microhardness and bioactivity testing after insertion in artificial saliva were done. Four Bisphenol-A glycerolate dimethacrylate based sealant loaded with the glass batch that showed the preeminent properties and silica fillers were prepared. The prepared sealants were compared to commercial sealants regarding flow, curing depth, compressive strength and microhardness. Sealant composition that showed comparable properties to that of the commercial sealant was selected for pH changes, ion release testing after immersion in artificial saliva for different time intervals. Results indicated the structural stability, amorphous nature, and bioactive behavior with apatite forming ability of the tested glass batches. Experimental sealant revealed comparable tested properties with lower compressive strength compared to the commercial sealants at P < 0.001. The mean pH values of the tested sealants ranged from 6.75 to 6.35 with extended calcium and phosphorus ion release up to 90 days. It was concluded that the 85 wt% calcium silicate and sodium silicate with 15 wt% fluoroapatite had the best trend regarding ion release and appetite forming ability. Sealant loaded with 65 wt% bioactive glass, 10 wt% sintered nanosilica and 10 wt% nanosilica had the best acceptable mechanical properties. The novel pit and fissure sealant is a promising bioactive and ion releasing material.