Nanoleakage expression and microshear bond strength in the resin cement/dentin interface

PURPOSE

The aim of this study was to evaluate dentin sealing ability and microshear bond strength of two different resin cements.

MATERIALS AND METHODS

Resin composite overlays (Estenia C&B) were fabricated and cemented to mid-dentin surfaces with either a self-adhesive resin cement (RelyX Unicem) or a resin cement with a self-etching primer (Panavia F2.0). After 24 h storage in water, the specimens were sectioned, placed into 50% (w/v) ammoniacal silver nitrate solution for 24 h, exposed to photodeveloping solution and observed using FE-SEM and EDS. Percentage distribution of metallic silver particles in the resin cement/dentin interface was calculated using digital image analysis software. In addition, small resin overlay cylinders were also bonded to dentin using either of the resin cements, and their bonding performance was evaluated with the microshear bond strength test. The statistical significance was defined as p ≤ 0.05.

RESULTS

No statistically significant difference was detected in the microshear bond strength between RelyX Unicem and Panavia F2.0 (24.9 ± 4.8 and 26.1 ± 5.3 MPa, respectively, p > 0.05). However, a significant difference was detected in silver particle penetration percentage between RelyX Unicem and Panavia F2.0 (7.4 ± 4.6 and 18.7 ± 8.7 MPa, respectively). The Kruskal-Wallis mean ranks for nanoleakage were 6.8 and 14.2, respectively (p < 0.05).

CONCLUSION

While the bond strengths of the two materials were comparable, the self-adhesive resin cement may provide better dentin sealing compared to the self-etching primer resin cement.

Effect of bonded area and/or fiber post placement on the fracture strengths of resin-core reconstructions for pulpless teeth

PURPOSE

To compare the fracture strengths of pulpless teeth restored using resin cores with and without fiber posts, and with and without bonding adhesive in the post cavity.

METHODS

Human extracted roots were prepared with post cavities and divided into four experimental groups: Groups 1 and 2--after application of adhesive to both the top surface of the root and the inner surface of the post cavity, DC core Automix was injected into the post space with or without fiber-post placement; Groups 3 and 4--adhesive was applied to the top surface of the root only, with or without post placement. Resin-cores were then built-up. Teeth prepared for full crowns served as controls. After water storage at 37 degrees C for 24 hours, the all specimens were embedded in acrylic resin at 2 mm below CEJ, and loaded at 45 degrees to the long axis of the tooth using a universal testing machine until fracture. The data were analyzed by one-way ANOVA (alpha = 0.05).

RESULTS

The fracture loads were, Group 1: 1832 +/- 240 N, Group 2: 1815 +/- 347 N, Group 3: 1626 +/- 396 N, Group 4: 1810 +/- 332 N, Control Group: 1622 +/- 274 N. There were no significant differences among all the groups (P > 0.05).

Effects of water-storage on the physical and ultramorphological features of adhesives and primer/adhesive mixtures

The aims of this study were to evaluate the ultimate tensile strength (UTS) and elastic modulus (E) of adhesives, and primer/adhesive mixtures after aging for 6 months in water or oil; and to compare silver uptake patterns under the TEM. A one-step self-etching adhesive (One-up Bond F: OB), two two-step self-etching primers (SE Bond: SE and Protect Bond: CP), and two etch-and-rinse systems (Single Bond: SB and Prime&Bond NT: PB) were used. Bonding and primer solutions of self-etching systems were also mixed (SE+P and CP+P). Most adhesives presented decreased UTS after water-storage. Similar or increased UTS was observed after oil storage. Except for SB, E values did not change after water-storage, but they increased after storage in oil. OB, CP+P and SE+P presented more silver uptake. The effects of water-storage were material-dependent, and significantly affected the mechanical properties and silver uptake patterns of adhesives.

CO2 Laser Improves 45S5 Bioglass Interaction with Dentin

Bioglass 45S5 is a bioactive glass that can create a layer of calcium-phosphate crystals on mineralized hard tissues. In this study, 45S5 bioglass was mixed with phosphoric acid and irradiated with CO2 laser and examined as a possible aid in the treatment of dentin hypersensitivity. The dentinal surface modified by the aforementioned technique was chemically and micro-morphologically examined with a field emission scanning electron microscope (FE-SEM) equipped with an energy-dispersive x-ray spectroscope (EDS), and the crystalline structures of the examined dentinal surfaces were examined by x-ray diffraction (XRD). Moreover, the mechanical properties of the newly formed layer were examined by nanoindentation. The results showed that 45S5 bioglass could occlude the dentinal tubule orifices with calcium-phosphate crystals. The application of CO2 laser potentially improved the mechanical organization of these crystals.

Nanoleakage of current self-etch adhesives bonded to artificial carious dentin

PURPOSE

To evaluate the nanoleakage of one- and two-step self-etch adhesives bonded to artificial carious dentin.

METHODS

Deep dentin of 24 human molars was exposed and divided into four groups. One group served as control while the others were demineralized in artificial demineralization solution for 10 minutes, 6 hours, and 24 hours. Roots were sectioned and the crowns were bonded with one- and two-step self-etch adhesives (Clearfil S3 and Clearfil SE Bond) then restored with flowable composite (Estelite Flow Quick). Specimens were exposed to intrapulpal pressure through a tube connected to a barrel filled with silver nitrate solution in total darkness for 24 hours and then sectioned into two mid-slabs that were photo-developed and prepared for nanoleakage evaluation using FE-SEM and EDX. Penetration of silver into the hybrid and adhesive layers was evaluated and compared between adhesives and dentin condition. Data were statistically analyzed by Kruskal-Wallis test (alpha = .05).

RESULTS

Increasing depths of demineralization were observed with increasing demineralization time. There were statistically significant differences for both adhesives (P < 0.05) and dentin demineralization (P< 0.05) in hybrid and adhesive layers. Normal dentin interfaces revealed no or slight nanoleakage regardless of adhesive. The bonded interface treated with one-step Clearfil S3 showed significant differences between normal and demineralized dentin. Also a trend towards increases in nanoleakage with the increasing of the demineralization time was demonstrated. Different patterns of nanoleakage were observed within adhesives.

Dentin bond durability and water sorption/solubility of one-step self-etch adhesives

The purpose of this study was to evaluate the dentin bonding durability of three HEMA-containing one-step self-etch adhesives after one-year water storage and to measure the amounts of their water sorption/solubility. OptiBond All-In-One (OP), Bond Force (BF) and Clearfil S³Bond (S³) were applied to the dentin surfaces according to manufacturers' instructions. Bond strengths to dentin were determined using µTBS test after water storage for 24 hours, six months, and one year. In addition, water sorption and solubility of the polymerized adhesives were measured. The µTBS of S³ and OP significantly decreased after one year. On the other hand, for BF there were no significant differences in µTBS between all storage periods. There were significant differences in water sorption and solubility among the adhesives (BF>S³>OP). The initial amounts of water sorption and solubility of the three adhesives did not affect their bonding durability to dentin.

Effects of electrodeposited poly(ethylene glycol) on biofilm adherence to titanium

Protein-resistant coatings have been studied for inhibiting biofilm formation on implant devices. In this study, titanium (Ti) surfaces were biofunctionalized with poly(ethylene glycol) (PEG) by electrodeposition and were evaluated as biofilm substrates under an oral simulated environment. Streptococcus gordonii, an early colonizer of oral biofilms, was inoculated on Ti and PEG-electrodeposited Ti (PEG-Ti) surfaces and was analyzed quantitatively and topographically. Streptococcus mutans supplemented with sucrose, a late colonizer mainly found in dental plaque, was also used to form biofilms on the surfaces of Ti and PEG-Ti for 20 h followed by sonication as a means of detaching the biofilms. The results indicated that the attachment of S. gordonii on PEG-Ti surfaces was inhibited compared with Ti, and the S. mutans biofilm was easier to be detached from the surface of PEG-Ti than that of Ti. Moreover, the presence of PEG electrodeposited on Ti surface inhibited salivary protein adsorption. The degree of detachment of biofilms from PEG-Ti was associated with the inhibition of the salivary protein adsorption, suggesting weak basal attachment of the biofilms to the electrodeposited surfaces. Therefore, controlling protein adsorption at the initial stage of biofilm formation may be an effective strategy to protect metal surfaces from bacterial contamination not only in dental manipulations but also in orthopedic applications.

Translucency, opalescence and light transmission characteristics of light-cured resin composites

OBJECTIVES

To evaluate the translucency, opalescence and light transmission characteristics of resin composites with different thicknesses.

METHODS

Disks of three resin composites (Estelite∑, Beautifil II, Clearfil Majesty) of A2 shade were prepared in diameter of 10mm with various thicknesses (0.5mm, 1.0mm and 2.0mm). Color was measured according to CIELAB color scale on a reflection spectrophotometer and a color haze meter, and translucency parameter (TP) and opalescence parameter (OP) were calculated. Using the distribution graphs of transmitted light intensity on a goniophotometer, diffusion factor (DF) as an indicator for a diffuse transmission property and peak gain (G0) for a straight-line transmission property were calculated.

RESULTS

The TP and G0 values significantly decreased in the order: 0.5mm>1.0mm>2.0mm thickness (p<0.05). The OP value increased as the thickness of resin composite increased from 1.0mm to 2.0mm (p<0.05), while was similar for the 0.5mm- and 1.0mm-thick groups. The DF value increased from 0.5mm to 1.0mm, but was similar for the 1.0mm- and 2.0mm-thick groups. There was a significant correlation between TP and DF (R(2)=0.96, p<0.001). On the other hand, there was a weak correlation between OP and DF (R(2)=0.21, p<0.005), however within the values of the 0.5mm-thick group, OP was highly correlated with DF (R(2)=0.84, p<0.001).

SIGNIFICANCE

At the 0.5mm thickness, the translucency (TP) and opalescence (OP) of resin composites had a significant correlation with a diffuse transmission property (DF). When more than 1.0mm thickness of resin composites, translucency and opalescence were influenced by the thickness, in which translucency significantly decreased and opalescence significantly increased.

Localization of matrix metalloproteinases (MMPs-2, 8, 9 and 20) in normal and carious dentine

BACKGROUND

Dentine matrix metalloproteinases (MMPs) may participate in the destruction of dentine following demineralization by bacterial acids. This study investigated the localization of MMPs in carious dentine.

METHODS

Frozen sections of dentine caries were prepared without demineralization and immersed in monoclonal antibody against MMP-2, -8, -9 and -20. The sections were labelled by IgG conjugated with gold colloidal particles, and observed under FE-SEM. Labelling indexes (number of gold particles/mum(2)) of outer and inner carious dentine, respectively, with and without bacterial infection, were compared with that of normal dentine.

RESULTS

MMP-2 was distributed in both carious and normal dentine; the level of MMP-2 showed no significant difference among the outer caries, inner caries, and normal dentine. The labelling indexes of MMP-8 and MMP-9 both significantly decreased at the inner carious dentine compared with the level of normal dentine, but intensified again at the outer caries region. The labelling index of MMP-20 was the highest at normal dentine.

CONCLUSIONS

The localization of MMPs was visibly detected using immunogold labelling. The localization of MMP-2 showed no significant difference among the three regions, while MMP-8 and MMP-9 showed significant reduction at the inner caries layer, and MMP-20 reduced toward the outer caries.

Properties of Injectable Apatite-Forming Premixed Cements

Previous studies reported premixed calcium phosphate cements (CPCs) that were stable in the package and form hydroxyapatite (HA) as the product after exposure to an aqueous environment. These cements had setting times of greater than 60 min, which are too long to be useful for some clinical applications. The present study investigated properties of fast-setting HA-forming premixed CPCs that initially consisted of two separate premixed pastes: (1) finely ground (1.0 μm in median size) dicalcium phosphate anhydrous (DCPA) mixed with an aqueous NaH(2)PO(4) solution, 1.5 mol/L or 3.0 mol/L in concentration, and (2) tetracalcium phosphate consisting of combinations of particles of two different size distributions, 5 μm (TTCP5) and 17 μm (TTCP17) in median size, mixed with glycerin. Equal volume of Pastes 1 and 2 were injected with the use of atwo-barrel syringe fitted with a static mixer into sample molds. The molar Ca/P ratio of combined paste was approximately 1.5. Cements were characterized in terms of setting time (Gilmore needle), diametral tensile strength (DTS), and phase composition (powder x-ray diffraction, XRD). Setting times were found to range from (4.3 ± 0.6 to 68 ± 3) min (mean ± sd; n = 3), and 1-d and 7-d DTS values were from (0.89 ± 0.08 to 2.44 ± 0.16) MPa (mean ± sd; n = 5). Both the NaH(2)PO(4) concentration and TTCP particle size distribution had significant (p < 0.01) effects on setting time and DTS. Powder XRD analysis showed that low crystallinity HA and unreacted DCPA were present in the 1-day specimens, and the extent of HA formation increased with increasing amount of TTCP5 in the TTCP paste. CONCLUSION: Injectable HA-forming premixed CPCs with setting times from 4 to 70 min can be prepared by using DCPA and TTCP as the ingredients. Compared to the conventional powder liquid cements, these premixed CPCs have the advantages of being easy to use and having a range of hardening times.

The role of functional monomers in bonding to enamel: acid-base resistant zone and bonding performance

OBJECTIVES

To investigate the effects of two functional monomers on caries-inhibition potential and bond strength of two-step self-etching adhesive systems to enamel.

METHODS

Clearfil SE Bond and similar experimental formulations different in the functional monomer were used. Four combinations of primer and bonding agents were evaluated: (1) Clearfil SE Bond which contains MDP in both primer and bonding (M-M); (2) Clearfil SE Bond primer and Phenyl-P in bonding (M-P); (3) Phenyl-P in primer and Clearfil SE Bond bonding (P-M); (4) Phenyl-P in primer and bonding (P-P). Ground buccal enamel surfaces of human sound premolars were treated with one of the systems and the bonded interface was exposed to an artificial demineralising solution (pH 4.5) for 4.5 h, and then 5% NaOCl with ultrasonication for 30 min. After argon-ion etching, the interfacial ultrastructure was observed using SEM. Micro-shear bond strength to enamel was measured for all groups and results were analysed using one-way ANOVA and Turkey's HSD, while failure modes were analysed by chi-square test.

RESULTS

An acid-base resistant zone (ABRZ) was found with all adhesive systems containing MDP either in primer or bond; however, ultramorphology and crystallite arrangement in the ABRZ were different among groups. P-P was the only group devoid of this protective zone. Micro-shear bond strength in M-M was significantly higher than those in M-P, P-M and P-P, while the latter three were not different from each other. Failure modes were significantly different (p<0.05).

CONCLUSIONS

Functional monomers in two-step self-etching systems influence both the bonding performance and the formation of ABRZ on enamel.

Antimicrobial efficacy of 3.8% silver diamine fluoride and its effect on root dentin

INTRODUCTION

This study investigated the use of 3.8% silver diamine fluoride (Ag[NH3]2F) as an antibacterial agent against Enterococcus faecalis biofilms and its ability to penetrate dentinal tubules by the formation of silver salts.

METHODS

Biofilms were generated on membrane filter discs and subjected to 15-minute and 60-minute exposure times with 3.8% Ag(NH3)2F, saturated Ca(OH)2, 5.25% NaOCl (negative control), and 0.9% NaCl (positive control). Cleaned and shaped radicular dentin were applied with Ag(NH3)2F for 24, 48, and 72 hours. The presence of silver salts on the dentin surface was examined using low-pressure scanning electron microscopy.

RESULTS

Both NaOCl and Ag(NH3)2F were effective against E. faecalis biofilms, with no significant difference in reduction of microorganisms for both exposure times. Silver deposits were present on 66.5% of the radicular dentin surfaces after 72-hour application of Ag(NH3)2F as simulated interappointment dressings. Penetration of the silver deposits was observed at most 40 microm into dentinal tubules after smear layer removal.

CONCLUSION

Ag(NH3)2F has potential to be used as an antimicrobial root canal irrigant or interappointment dressing, especially in locations in which potential browning/blackening of dentin by metallic silver is not a major concern.

Effect of filler content of flowable composites on resin-cavity interface

The purpose of this in vitro study was to evaluate marginal integrity and wall adaptation in 1- and 2-mm-deep cavities restored with a high filler-loaded flowable composite in comparison to a flowable composite with lower filler content and a conventional hybrid composite. 1-mm-deep dentin and 2-mm-deep enamel-dentin Class I cavities were prepared and restored with a self-etch adhesive and with one of the composites. Samples were crosscut and evaluated for marginal integrity and gap formation using a digital microscope. Selected samples were also observed using a scanning electron microscope. For 1-mm-deep cavities, no differences in marginal integrity and wall adaptation were observed among the three composites. For 2-mm-deep cavities, those restored with the bulk technique and with the higher filler-loaded flowable composite demonstrated a similar outcome as that of the conventional hybrid composite. On the effect of restorative techniques, cohesive enamel defects were observed in bulk-filled 2-mm-deep cavities. However, when the incremental technique was used in conjunction with the higher filler-loaded flowable composite and the conventional hybrid composite for 2-mm-deep cavities, superior results were obtained.

Effects of light sources and visible light-activated titanium dioxide photocatalyst on bleaching

The objective of this study was to evaluate, using methylene blue (MB), the effects of various light sources on the bleaching action of hydrogen peroxide (H(2)O(2)) with two titanium dioxide (TiO(2)) photocatalysts - an ultraviolet light-activated TiO(2) photocatalyst (UVTiO(2)) versus a visible light-activated TiO(2) photocatalyst (VL-TiO(2)). Five experimental solutions (VL-TiO(2)+H(2)O(2), UV-TiO(2)+H(2)O(2), H(2)O(2), VL-TiO(2), UV-TiO(2)) were prepared by mixing varying concentrations of H(2)O(2 )and/or TiO(2 )photocatalyst with MB solution. For H(2)O(2)-containing solutions (VL-TiO(2)+H(2)O(2), UV-TiO(2)+H(2)O(2), and H(2)O(2)), the concentration of H(2)O(2) was adjusted to 3.5%. For the four different light sources, low- and high-intensity halogen lamps and blue LED LCUs were used. All the experimental solutions were irradiated by each of the light sources for 7 minutes, and the absorbance at 660 nm was measured every 30 seconds to determine the concentration of MB as an indicator of the bleaching effect. On the interaction between the effects of light source and bleaching treatment, the high-intensity halogen with VL-TiO(2)+H(2)O(2) caused the most significant reduction in MB concentration. On the effect of light sources, the halogen lamps resulted in a greater bleaching effect than the blue LED LCUs.

Why does fluorosed dentine show a higher susceptibility for caries: an ultra-morphological explanation

BACKGROUND

Chronic endemic dental fluorosis is a malformation of teeth caused by excessive ingestion of fluoride during period of tooth development. Apatite crystallites and collagen fibrils determine the caries susceptibility related properties of dentine. Information relating the effect of dental fluorosis with dentine crystallite and collagen structure is currently unavailable. This study examined structural aberrations of apatite crystallites and collagen fibrils in human fluorosed dentine.

METHOD

Superficial dentine of thirty six normal (Thylstrup-Fejerskov index - 0) and thirty six severely fluorosed (Thylstrup-Fejerskov index - 7 to 9) extracted human molars from individuals living in an area which is endemic for dental fluorosis were morphologically analyzed using transmission electron microscopy with selected area electron diffraction and dynamic force microscopy.

RESULTS

A statistically significant enlargement in the size of crystallites was found in fluorosed dentine (p<0.05). These crystallites were not homogenously arranged. Selected area electron diffraction revealed a lower density of crystallites in fluorosed dentine. Randomly distributed collagen fibrils showed a less complex lay out in contrast to normal dentine tissue.

CONCLUSION

Ultrastructure aberrations of the dentine explain the caries susceptibility of the tissue and suggest the necessity of special approach in dental caries treatment for patients with chronic severe endemic dental fluorosis.

Relationship between mechanical properties of one-step self-etch adhesives and water sorption

OBJECTIVES

The purpose of this study was to evaluate the relationship between changes in the modulus of elasticity and ultimate tensile strength of one-step self-etch adhesives, and their degree of water sorption.

METHODS

Five one-step self-etch adhesives, Xeno IV (Dentsply Caulk), G Bond (GC Corp.), Clearfil S3 Bond (Kuraray Medical Inc.), Bond Force (Tokuyama Dental Corp.), and One-Up Bond F Plus (Tokuyama Dental Corp.) were used. Ten dumbelled-shaped polymers of each adhesive were used to obtain the modulus of elasticity by the three-point flexural bending test and the ultimate tensile strength by microtensile testing. The modulus of elasticity and the ultimate tensile strength were measured in both dry and wet conditions before/after immersion in water for 24h. Water sorption was measured, using a modification of the ISO-4049 standard. Each result of the modulus of elasticity and ultimate tensile strength was statistically analyzed using a two-way ANOVA and the result of water sorption was statistically analyzed using a one-way ANOVA. Regression analyses were used to determine the correlations between the modulus of elasticity and the ultimate tensile strength in dry or wet states, and also the percent decrease in these properties before/after immersion of water vs. water sorption.

RESULTS

In the dry state, the moduli of elasticity of the five adhesive polymers varied from 948 to 1530 MPa, while the ultimate tensile strengths varied from 24.4 to 61.5 MPa. The wet specimens gave much lower moduli of elasticity (from 584 to 1073 MPa) and ultimate tensile strengths (from 16.5 to 35.0 MPa). Water sorption varied from 32.1 to 105.8 g mm(-3).

SIGNIFICANCE

The moduli of elasticity and ultimate tensile strengths of the adhesives fell significantly after water-storage. Water sorption depended on the constituents of the adhesive systems. The percent decreases in the ultimate tensile strengths of the adhesives were related to water sorption, while the percent reductions in the moduli of elasticity of the adhesives were not related to water sorption.

Effect of Double-application of Three Single-step Self-etch Adhesives on Dentin Bonding and Mechanical Properties of Resin-dentin Area

Double-application enhanced the hardness of bonding layer and resin-dentin interface for all the adhesives used; however, it only improved the bond strength to dentin for some of the single-step self-etch adhesives.