Production of hollow polymer particles by suspension polymerization

Enzymes in the cavity of hollow silica nanoparticles

Due to limitations of the existing preparative methods of hollow nanoparticles by either heating at high temperature (>600 degrees C) or by using strong acid, alkali, or an organic solvent, it was not possible up till now to encapsulate any sensitive organic molecule like enzyme or others inside the cavity of hollow nanoparticles. We have demonstrated a much softer method of preparing hollow silica nanoparticles with horseradish peroxidase (HRP) inside the cavity by synthesizing HRP-doped core-shell silica-coated silver chloride nanoparticles and finally leaching out silver chloride with dilute ammonia at low temperatures. TEM pictures showed the hollow cavity inside the nanoparticles. The enzyme entrapped in these particles was active. The turnover number of HRP entrapped into these hollow particles and dispersed in aqueous buffer (pH 7.2) (k(cat) = 2.56 x 10(6) s(-1)) was found to be less than that of free enzyme in aqueous buffer (k(cat) = 6.133 x 10(7) s(-1)) but higher than that of HRP entrapped in solid-core silica nanoparticles and dispersed in aqueous buffer (k(cat) = 1.05 x 10(5) s(-1)). The result showed that hollow nanoparticles could be prepared using soft chemical methods and sensitive chemicals like active enzyme could be entrapped in the cavities and it retains its activity.

pH-responsive core-shell particles and hollow spheres attained by macromolecular self-assembly

According to our "block-copolymer-free" strategy for self-assembly of polymers, noncovalently connected micelles (NCCM) with poly(epsilon-caprolactone) (PCL) as the core and poly(acrylic acid) (PAA) as the shell in aqueous solutions were attained due to specific interactions between the component polymers. The micellar structure was then locked in by the reaction of PAA with diamine. Afterward, hollow spheres based on PAA network were obtained by either core degradation with lipase or core dissolution with dimethylformamide of the cross-linked micelles. The cavitation process was monitored by dynamic light scattering, which indicated a mass decrease and size expansion. The hollow structure is confirmed by transmission electron microscopy observations. The resultant hollow spheres are pH- and salt-responsive: there is a substantial volume increase when pH changes from acid to base, and vice versa. The volume change takes place dramatically over the pH-range from 5.8 to 7.5. Furthermore, this volume-pH-dependence is found to be completely reversible provided the effect of ionic strength is excluded. The volume change can be adjusted by changing the shell thickness and the cross-linking degree of the hollow spheres. The salt effect on the hollow sphere size depends on pH: with increasing salt concentration the size shows an increase, a decrease, and a little change in acidic, basic, and neutral media, respectively.

Preparation of hollow silica microspheres in W/O emulsions with polymers

Micrometer-sized hollow silica particles were synthesized by sol-gel reaction in water-in-oil emulsion. To obtain hollow structures in silica particles, the viscosity of water droplets in W/O emulsion was controlled with polyethylene glycol (PEG) or polyvinylpyrrolidone (PVP). To stabilize the emulsion structure, hydroxypropyl cellulose (HPC) was added to the oil phase. Without HPC, the particles have an irregular shape and hardly have a particulate form. As the concentration of HPC increased from 0.8 to 1.4 wt%, the size of silica particles decreased from 10 to 1 microm. But above 1.4 wt%, the solution was very viscous, so that it was difficult to handle. Especially, the role of PEG or PVP in the water phase was very important, not only because it stabilized the W/O emulsion structure, but also because it influenced the formation of hollow structure. Interestingly, the hollow silica particles were formed when the molar ratio of water to TEOS (Rw) was 4 and the concentrations of PEG and HPC were 6 and 1.4 wt%, respectively. Also, when PEG was replaced with polyvinylpyrrolidone (PVP), hollow silica particles ranging from 3 to 7 microm were formed.

Decomposable hollow biopolymer-based capsules

Decomposable hollow capsules based on deoxyribonucleic acid (DNA) and a low molecular weight organic molecule, a naturally occurring polyamine, spermidine (SP), were formed by applying the layer-by-layer adsorption strategy to colloid particles, viz., assembling DNA/SP multilayers on colloids and subsequently removing the templated core. For comparison, hollow capsules from the higher molecular weight biopolymers, alginate (ALG) and poly(lysine) (PL), were also prepared. The multilayers were first formed on polystyrene spheres, and their growth was followed by microelectrophoresis. The preparation of hollow capsules, derived from multilayer coating melamine formaldehyde core particles and then decomposing the core by acid treatment, was verified by atomic force microscopy and transmission electron microscopy. In contrast to the hollow ALG/PL capsules, the hollow DNA/SP capsules displayed a high sensitivity to salt solutions: Decomposition of the DNA/SP multilayers occurred after exposure to sodium chloride solutions. The hollow capsules prepared are attractive for the encapsulation and release of various substances; for example, the release of encapsulated compounds, such as dyes or drugs, can occur when loaded DNA/SP capsules are exposed to environmental (salt) conditions that decompose them, e.g., in the bloodstream.