Novel Blend for Producing Porous Chitosan-Based Films Suitable for Biomedical Applications

In this work, a chitosan–gelatin–ferulic acid blend was used in different ratios for preparing novel films that can be used in biomedical applications. Both acetic and formic acid were tested as solvents for the chitosan–gelatin–ferulic acid blend. Glycerol was tested as a plasticizer. The thickness, mechanical strength, static water contact angle and water uptake of the prepared films were determined. Also, the prepared films were characterized using different analysis techniques such as Fourier transform infrared spectroscopy (FT-IR) analysis, X-ray diffraction (XRD), thermal gravimetric analysis (TGA), differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). Acetic acid produced continuous compact surfaces that are not recommended for testing in biomedical applications. The plasticized chitosan–gelatin–ferulic acid blend, using formic acid solvent, produced novel hexagonal porous films with a pore size of around 10–14 µm. This blend is recommended for preparing films (scaffolds) for testing in biomedical applications as it has the advantage of a decreased thickness.

Graft-modified cellulose nanocrystals as CO2-switchable Pickering emulsifiers

Cellulose nanocrystals (CNC) grafted with <25 wt% PDEAEMA or PDMAPMAm were used as CO₂-switchable Pickering emulsifiers for the reversible emulsification/demulsification of oil and water.

Surface behavior and bulk properties of aqueous chitosan and type-B gelatin solutions for effective emulsion formulation

The behavior of aqueous chitosan (CH), type-B gelatin (GB) and CH-GB coacervate was studied on oil-in-water emulsion formulation at various pH and concentration ratio. The coacervate was formed by phase separation at ratios CH:GB, 1:10 to 1:1 with total biopolymer concentrations of 0.55%-1.0% (w/v) at pH 4.0-5.5. Soluble complexes were formed below pH 5.0 and coacervate formation was confirmed at pH 5.0 and above by zeta potential and UV-spectroscopy measurements. The coacervate formation was found maximum at the CH-GB ratios of 1:10 and 1:5 at pH 5.5. Formulated emulsions (>10μm droplets) using 1% (w/v) chitosan and GB were found stable (+52.5mv and creaming index 86%) and unstable respectively. Emulsion stabilized by mixed CH:GB 1:5 (3%w/v) had no creaming effect. The instability was attributed to the lower surface activity (K=5.0Lg^-1) of pure GB compared to CH (K=14.3Lg^-1). The formulation and methods can successfully tune the stability of the emulsions.