Bismuth oxyiodide coupled with bismuth nanodots for enhanced photocatalytic bisphenol A degradation: synergistic effects and mechanistic insight

Bismuth based semiconductor photocatalysts are being generated as promising materials for photocatalysis. In this work, hydrothermal methods have been utilized to synthesize a bismuth oxyiodide semiconductor with deposited Bi nanodots (Bi-BiOI), which could create oxygen defects and accelerate photoinduced charge migration simultaneously. The resulting Bi-BiOI strongly demonstrates the high photocatalytic performance for bisphenol A and methylene blue degradation under visible light. 86% of BPA was degraded after an irradiation time of 4 hours. Electrospray ionization mass spectrometry was employed to detect the evolution of intermediates formed during the decomposition process of bisphenol A, and the following results suggested complete bisphenol A mineralization. Additionally, electron paramagnetic resonance results revealed the production of free radicals and the presence of oxygen vacancies. Furthermore, a distinctively increased photocurrent response and photoluminescence decay dynamics demonstrate that the interface between the Bi nanodots and BiOI semiconductor promotes the separation and migration of photoinduced electron-hole pairs. The lower valence band value (2.57 eV) of Bi-BiOI presented a higher oxidation potential, thus the production of hydroxyl radicals could be promoted considerably. Based on the experimental results, factors such as oxygen vacancies, effective charge migration, suppressed photoinduced electron-hole pair recombination and a high Bi-BiOI oxidation potential would result in advanced free radical production capacity, thereby enhancing the photocatalytic efficiency. The findings of our work will contribute to the fabrication of metal nanodot deposited semiconductor photocatalysts and pave the way for the utilization of advanced oxidation technology.

Synthesis of Bi₂S₃/BiVO₄ Heterojunction with a One-Step Hydrothermal Method Based on pH Control and the Evaluation of Visible-Light Photocatalytic Performance

The band gaps of bismuth vanadate (BiVO₄) and bismuth sulfide (Bi₂S₃) are about 2.40 eV and 1.30 eV, respectively. Although both BiVO₄ and Bi₂S₃ are capable of strong visible light absorption, electron–hole recombination occurs easily. To solve this problem, we designed a one-step hydrothermal method for synthesizing a Bismuth sulfide (Bi₂S₃)/Bismuth vanadate (BiVO₄) heterojunction using polyvinylpyrrolidone K-30 (PVP) as a structure-directing agent, and 2-Amino-3-mercaptopropanoic acid (l-cysteine) as a sulfur source. The pH of the reaction solution was regulated to yield different products: when the pH was 7.5, only monoclinic BiVO₄ was produced (sample 7.5); when the pH was 8.0 or 8.5, both Bi₂S₃ and BiVO₄ were produced (samples 8.0 and 8.5); and when the pH was 9.0, only Bi₂S₃ was produced (sample 9.0). In sample 8.0, Bi₂S₃ and BiVO₄ were closely integrated with each other, with Bi₂S₃ particles formed on the surface of concentric BiVO₄ layers, but the two compounds grew separately in a pH solution of 8.5. Visible-light photocatalytic degradation experiments demonstrated that the degradation efficiency of the Bi₂S₃/BiVO₄ heterojunction was highest when prepared under a pH of 8.0. The initial rhodamine B in the solution (5 mg/L) was completely degraded within three hours. Recycling experiments verified the high stability of Bi₂S₃/BiVO₄. The synthesis method proposed in this paper is expected to enable large-scale and practical use of Bi₂S₃/BiVO₄.

Additive dependent synthesis of bismuth oxybromide composites for photocatalytic removal of the antibacterial agent ciprofloxacin and mechanism insight

Bismuth oxybromide composites obtained with TEOA as additive exhibit the highest photocatalytic degradation for CIP under visible light irradiation.

Promotion of phenol photodegradation based on novel self-assembled magnetic bismuth oxyiodide core–shell microspheres

A novel visible-light driven “plates-over-nanospheres” (PONs) photocatalyst with BiOI nanoplates grown on the surface of Fe₃O₄ nanospheres was prepared using a facile method.