A Comparative Study on the Mechanical Properties of a Polymer-Infiltrated Ceramic-Network Material Used for the Fabrication of Hybrid Abutment

Polymer-infiltrated ceramic-network (PICN) material is a new type of material used for the hybrid abutments of dental implants. This study aimed to compare flexural strength, bond strengths, and fracture-resistance values of PICN with lithium disilicate ceramic (LDS) and to evaluate the effect of thermocycling on the tested parameters. Twenty specimens were fabricated using computer-aided design and manufacturing (CAD-CAM) technology for each material according to three-point bending (n = 10), microshear bond strength (µSBS), and a fracture-resistance test (hybrid abutment, n = 10). All specimens of each test group were divided into two subgroups, thermocycled or nonthermocycled. Hybrid abutments were cemented on titanium insert bases and then fixed on implants to compare fracture resistance. Failure loads were recorded for each test and data were statistically analyzed. Thermocycling decreased bond strength to the resin luting agent and the fracture-resistance values of both materials (p < 0.001), whereas flexural-strength values were not affected. LDS ceramic showed significantly higher flexural strength, bond strength, and fracture-resistance values than PICN material (p < 0.001). Within the limitations of this study, LDS may be a preferable hybrid-abutment material to PICN in terms of mechanical and bonding properties.

Influence of crown and hybrid abutment ceramic materials on the stress distribution of implant-supported prosthesis

Abstract Introduction A new dental implant-abutment design is available with the possibility of improving aesthetic with no compromise of mechanical strength, using perforated CAD/CAM ceramic blocks. Objective This study evaluated the influence of crown and hybrid abutment ceramic materials combination on the stress distribution of external hexagon implant supported prosthesis. Method Zirconia, lithium disilicate and hybrid ceramic were evaluated, totaling 9 combinations of crown and mesostructure materials. For finite element analysis, a monolithic crown cemented over a hybrid abutment (mesostructure + titanium base) was modeled and screwed onto an external hexagon implant. Models were then exported in STEP format to analysis software, and the materials were considered isotropic, linear, elastic and homogeneous. An oblique load (30°, 300N) was applied to the central fossa bottom and the system’s fixation occurred on the bone’s base. Result For crown structure, flexible materials concentrate less stress than rigid ones. In analyzing the hybrid abutment, it presented higher stress values when it was made with zirconia combined with a hybrid ceramic crown. The stress distribution was similar regarding all combinations for the fixation screw and implant. Conclusion For external hexagon implant, the higher elastic modulus of the ceramic crowns associated with lower elastic modulus of the hybrid abutment shows a better stress distribution on the set, suggesting a promising mechanical behavior.

Fatigue Failure Load of Lithium Disilicate Restorations Cemented on a Chairside Titanium-Base

PURPOSE

To evaluate the fatigue failure load of distinct lithium disilicate restoration designs cemented on a chairside titanium base for maxillary anterior implant-supported restorations.

MATERIALS AND METHODS

A left-maxillary incisor restoration was virtually designed and sorted into 3 groups: (n = 10/group; CTD: lithium disilicate crowns cemented on custom-milled titanium abutments; VMLD: monolithic full-contour lithium disilicate crowns cemented on a chairside titanium-base; VCLD: lithium disilicate crowns bonded to lithium disilicate customized anatomic structures and then cemented onto a chairside titanium base). The chairside titanium base was air-abraded with aluminum oxide particles. Subsequently, the titanium base was steam-cleaned and air-dried. Then a thin coat of a silane agent was applied. The intaglio surface of the ceramic components was treated with 5% hydrofluoric acid (HF) etching gel, followed by silanization, and bonded with a resin cement. The specimens were fatigued at 20 Hz, starting with a 100 N load (5000× load pulses), followed by stepwise loading from 400 N up to 1400 N (200 N increments) at a maximum of 30,000 cycles each. The failure loads, number of cycles, and fracture analysis were recorded. The data were statistically analyzed using one-way ANOVA, followed by pairwise comparisons (p < 0.05). Kaplan-Meier survival plots and Weibull survival analyses were reported.

RESULTS

For catastrophic fatigue failure load and the total number of cycles for failure, VMLD (1260 N, 175,231 cycles) was significantly higher than VCLD (1080 N, 139,965 cycles) and CDT (1000 N, 133,185 cycles). VMLD had a higher Weibull modulus demonstrating greater structural reliability.

CONCLUSION

VMLD had the best fatigue failure resistance when compared with the other two groups.

Effect of Clinically Relevant CAD/CAM Zirconia Polishing on Gingival Fibroblast Proliferation and Focal Adhesions

Mucosal seal formation around dental abutments is critical to the successful integration of dental implants into the human oral cavity. No information exists for how clinically relevant polishing procedures for computer-aided design and computer-aided manufactured (CAD/CAM) zirconia abutments affects cellular responses important to mucosal seal formation. CAD/CAM zirconia was divided into four groups for clinically relevant polishing utilizing commercial polishing heads: control, coarse, coarse plus medium, and coarse plus medium plus fine. Surfaces were analyzed with scanning electron microscopy (SEM), atomic force microscopy (AFM), and optical profilometry (OP). Subsequently, human gingival fibroblasts (HGFs) were seeded onto the zirconia surfaces. Proliferation was measured via a quantitative SEM technique and focal adhesion kinase (FAK) phosphorylation status was measured by an enzyme-linked immunosorbent assay (ELISA). Results showed an increase in proliferation on all polished surfaces as compared to the control. Phosphorylation of FAK at tyrosine 397 (Y397) was up-modulated on the control surfaces. The associated cell adaptation is discussed. In all cases, FAK phosphorylation was greater at 24 h than 48 h. These results suggest that clinicians should be mindful of the effects of abutment polishing methodology, as this may have an impact on early mucosal seal formation.