Effect of electrospun fiber diameter and alignment on macrophage activation and secretion of proinflammatory cytokines and chemokines

NEGATIVE VOLTAGE ELECTROSPINNING AND POSITIVE VOLTAGE ELECTROSPINNING OF TISSUE ENGINEERING SCAFFOLDS: A COMPARATIVE STUDY AND CHARGE RETENTION ON SCAFFOLDS

Positive voltage electrospinning (PVES) has been mainly used for forming fibrous polymer scaffolds for different applications including tissue engineering. There is virtually no report on negative voltage electrospinning (NVES) of tissue engineering scaffolds. In this study, NVES of four biopolymers, namely, gelatin, chitosan, poly(lactic-co-glycolic acid) (PLGA), and polybutylene terephthalate (PBT), to form nanofibrous membranes was systematically investigated. For comparisons, PVES of these polymers was also conducted. It was found that chitosan fibers could not be produced using NVES. Under NVES or PVES, the fiber diameter of electrospun scaffolds generally increased with increasing needle inner diameter and polymer solution concentration but decreased with increasing working distance for all four polymers. Neither NVES nor PVES altered the chemical structure of gelatin, PLGA, and PBT. PVES and NVES resulted in fibrous membranes bearing positive charges and negative charges, respectively. PLGA and PBT fibrous membranes retained around 30% and 50%, respectively, of the initial charge one week after electrospinning. Charges on gelatin and chitosan fibrous membranes were almost completely dissipated within 60 min of electrospinning. For all four polymers, under either PVES or NVES, the retained charges on fibrous membranes increased with increasing applied electrospinning voltage. This study explored a new approach for forming fibrous scaffolds by using NVES and has opened a new area for developing negatively charged fibrous scaffolds for tissue engineering applications.

Preferential cell response to anisotropic electro-spun fibrous scaffolds under tension-free conditions

Anisotropic alignment of collagen fibres in musculoskeletal tissues is responsible for the resistance to mechanical loading, whilst in cornea is responsible for transparency. Herein, we evaluated the response of tenocytes, osteoblasts and corneal fibroblasts to the topographies created through electro-spinning and solvent casting. We also evaluated the influence of topography on mechanical properties. At day 14, human osteoblasts seeded on aligned orientated electro-spun mats exhibited the lowest metabolic activity (P < 0.001). At day 5 and at day 7, no significant difference was observed in metabolic activity of human corneal fibroblasts and bovine tenocytes respectively seeded on different scaffold conformations (P > 0.05). Osteoblasts and corneal fibroblasts aligned parallel to the direction of the aligned orientated electro-spun mats, whilst tenocytes aligned perpendicular to the aligned orientated electro-spun mats. Mechanical evaluation demonstrated that aligned orientated electro-spun fibres exhibited significant higher stress at break values than their random aligned counterparts (P < 0.006) and random orientated electro-spun fibres exhibited significant higher strain at break values than the aligned orientated scaffolds (P < 0.006). While maintaining fibre structure, we also developed a co-deposition method of spraying and electro-spinning, which enables the incorporation of microspheres within the three-dimensional structure of the scaffold.

Effect of the surface topography of electrospun poly(ε-caprolactone)/poly(3-hydroxybuterate-co-3-hydroxyvalerate) fibrous substrates on cultured bone cell behavior

The use of electrospun fibrous matrices as substrates for cell/tissue culture has usually been confined to those consisting of smooth fibers. Here, we demonstrated that in vitro responses of mouse-calvaria-derived preosteoblastic cells (MC3T3-E1) that had been cultured on electrospun fibrous substrates made from blend solutions of 50/50 w/w poly(ε-caprolactone) (PCL) and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) of varying concentrations, ranging from 4 to 14 wt %, depended strongly on the topography of the individual fibers. As the concentration of the blend solutions increased from 4 to 14 wt %, the topography of the individual fibers changed from discrete beads/smooth fibers to beaded fibers/smooth fibers and finally to smooth fibers, and the average diameter of the individual, smooth fibers increased from ∼0.4 to ∼1.8 μm. The results clearly showed that MC3T3-E1 preferred the smooth hydrophilic surface of the fibrous substrate from 10 wt % PCL/PHBV solution because the cells appeared to attach, proliferate, and differentiate on the surface of this substrate particularly well.

Development of a chitosan nanofibrillar scaffold for skin repair and regeneration

The final goal of the present study was the development of a 3-D chitosan dressing that would shorten the healing time of skin wounds by stimulating migration, invasion, and proliferation of the relevant cutaneous resident cells. Three-dimensional chitosan nanofibrillar scaffolds produced by electrospinning were compared with evaporated films and freeze-dried sponges for their biological properties. The nanofibrillar structure strongly improved cell adhesion and proliferation in vitro. When implanted in mice, the nanofibrillar scaffold was colonized by mesenchymal cells and blood vessels. Accumulation of collagen fibrils was also observed. In contrast, sponges induced a foreign body granuloma. When used as a dressing covering full-thickness skin wounds in mice, chitosan nanofibrils induced a faster regeneration of both the epidermis and dermis compartments. Altogether our data illustrate the critical importance of the nanofibrillar structure of chitosan devices for their full biocompatibility and demonstrate the significant beneficial effect of chitosan as a wound-healing biomaterial.