Water Stable Zr-Benzenedicarboxylate Metal-Organic Frameworks as Photocatalysts for Hydrogen Generation

Composite MOF foams: the example of UiO-66/polyurethane

Composite MOF foams were prepared using a direct synthesis of UiO-66 over a polyurethane foam template. Under optimized conditions, the composite materials maintained the macrostructure and flexibility of the polyurethane foam, and exhibited the microporosity, high surface area, and adsorption properties of the UiO-66. The composite MOF foam has hierarchical porosity and high adsorption capacity for benzene and n-hexane, maintaining more than 70% of the adsorption capacity of the UiO-66.

Interactions of NO2 with Zr-based MOF: effects of the size of organic linkers on NO2 adsorption at ambient conditions

Zirconium-based metal organic framework (Zr-MOF), UiO-66 and UiO-67, were synthesized and used as adsorbents of NO(2) at ambient temperatures in either dry or moist conditions. The samples were characterized before and after exposure to NO(2) by X-ray diffraction, scanning electron microscopy, N(2)-adsorption at 77 K, thermal analysis, and infrared spectroscopy. The results indicate the important effect of a ligand size on the adsorption of NO(2) on Zr-MOF materials. While the large size of the 4,4-benzenebiphenyldicarboxylic acid (BDPC) ligand has a positive impact on the adsorption of NO(2) on UiO-67 in moist conditions, the opposite effect is found in dry conditions. The large pore volume of UiO-67 enhances the adsorption of moisture and formation of nitric and nitrous acids. The small pore sizes of UiO-66 favor the NO(2) removal in dry conditions via dispersive forces. Upon interaction of NO(2) molecules with the Zr-MOF in dry conditions, the bond between the organic linker and metallic oxide center is broken, leading to the formation of nitrate and nitrite species. Moreover, organic ligands also contribute to the NO(2) reactive adsorption via nitration reaction.

Effects of ammonium hydroxide on the structure and gas adsorption of nanosized Zr-MOFs (UiO-66)

Several zirconium-based metal-organic frameworks (Zr-MOFs) have been synthesized using ammonium hydroxide as an additive in the synthesis process. Their physicochemical properties have been characterized by N(2) adsorption/desorption, XRD, SEM, FTIR, and TGA, and their application in CO(2) adsorption was evaluated. It was found that addition of ammonium hydroxide produced some effects on the structure and adsorption behavior of Zr-MOFs. The pore size and pore volume of Zr-MOFs were enhanced with the additive, however, specific surface area of Zr-MOFs was reduced. Using an ammonium hydroxide additive, the crystal size of Zr-MOF was reduced with increasing amount of the additive. All the samples presented strong thermal stability. Adsorption tests showed that capacity of CO(2) adsorption on the Zr-MOFs under standard conditions was reduced due to decreased micropore fractions. However, modified Zr-MOFs had significantly lower adsorption heat. The adsorption capacity of carbon dioxide was increased at high pressure, reaching 8.63 mmol g(-1) at 987 kPa for Zr-MOF-NH(4)-2.