Modification of aqueous polyurethane dispersions via tetraphenylethane iniferters

Functionalization of Polylactide with Multiple Tetraphenyethane Inifer Groups to Form PLA Block Copolymers with Vinyl Monomers

In the present contribution, a new strategy for preparing block copolymers of polylactide (PLA), a bio-derived polymer of increasing importance, is described. The method should lead to multiblock copolymers of lactide with vinyl monomers (VM), i.e., monomers that polymerize according to different mechanisms, and is based on the introduction of multiple "inifer" (INItiator/transFER agent) groups into PLA's structure. As an "inifer" group, tetraphenylethane (TPE, known to easily thermally dissociate to radicals) was incorporated into PLA chains using diisocyanate. PLA that contained TPE groups (PLA-PU) was characterized, and its ability to form initiating radicals was demonstrated by ESR measurements. PLA-PU was used as a "macroinifer" for the polymerization of acrylonitrile and styrene upon moderate heating (85 °C) of the PLA-PU in the presence of monomers. The formation of block copolymers PLA/PVM was confirmed by ¹H NMR, DOSY NMR, and FTIR spectroscopies and the SEC method. The prepared copolymers showed only one glass transition in DSC curves with T_g values higher than those of PLA-PU.

Structure–Properties Relationship in Waterborne Poly(Urethane-Urea)s Synthesized with Dimethylolpropionic Acid (DMPA) Internal Emulsifier Added before, during and after Prepolymer Formation

Dimethylolpropionic acid (DMPA) internal emulsifier has been added before, during and after prepolymer formation in the synthesis of waterborne poly(urethane-urea)s (PUDs) and their structure–properties relationships have been assessed. PUDs were characterized by pH, viscosity and particle size measurements, and the structure of the poly(urethane-urea) (PU) films was assessed by infra-red spectroscopy, differential scanning calorimetry, X-ray diffraction, thermal gravimetric analysis, plate–plate rheology and dynamic mechanical thermal analysis. The adhesion properties of the PUDs were measured by cross-hatch adhesion and T-peel test. The lowest pH value and the highest mean particle size were found in the PUD made by adding DMPA after prepolymer formation, all PUDs showed relatively ample mono-modal particle size distributions. The highest viscosity and noticeable shear thinning were obtained in the PUD made by adding DMPA during prepolymer formation. Depending on the stage of addition of DMPA, the length of the prepolymer varied and the PU films showed different degree of micro-phase separation. Because the shortest prepolymer was formed in the PU made with DMPA added before prepolymer, this PU film showed the lowest storage moduli and early melting indicating higher degree of micro-phase separation. The highest storage modulus, later melting, higher temperature and lower modulus at the cross between the storage and loss moduli corresponded to the PU made by adding DMPA after prepolymer formation, because the longer prepolymer produced during synthesis. The lowest thermal stability corresponded to the PU made by adding DMPA during prepolymer formation and the structures of all PU films were dominated by the soft domains, the main structural differences derived from the hard domains. Whereas DMPA-isophorone diisocyanate (IPDI) urethane and urea hard domains were created in the PU film made by adding DMPA during prepolymer formation, the other PU films showed DMPA-IPDI, polyester-IPDI and two different DMPA-IPDI-polyester hard domains. Finally, the adhesion properties of the PUDs and PU coatings were excellent and they were not influenced by the structural differences caused by adding DMPA in different stages of the synthesis.

Preparation and Properties of Bio-Based Waterborne Polyurethane Modified by Zinc Oxide

In the present study, a kind of bio-based waterborne polyurethane (BWPU) /ZnO was prepared with BWPU and different concentrations of nanometer ZnO emulsion by incorporated into the BWPU matrix. The prepared BWPU/ZnO hybrid dispersions were casted in a Teflon petridish and the dried films were used for XRD, SEM, FT-IR and antibacterial tests. The results suggest that the BWPU/ZnO hold the potential applications as new materials.