Apatite growth on calcium adsorbed surface of wet flocculated silica particles immersed in a modified simulated body fluid

How Surface Properties of Silica Nanoparticles Influence Structural, Microstructural and Biological Properties of Polymer Nanocomposites

The aim of this work was to study effect of the type of silica nanoparticles on the properties of nanocomposites for application in the guided bone regeneration (GBR). Two types of nanometric silica particles with different size, morphology and specific surface area (SSA) i.e., high specific surface silica (hss-SiO₂) and low specific surface silica (lss-SiO₂), were used as nano-fillers for a resorbable polymer matrix: poly(L-lactide-co-D,L-lactide), called PLDLA. It was shown that higher surface specific area and morphology (including pore size distribution) recorded for hss-SiO₂ influences chemical activity of the nanoparticle; in addition, hydroxyl groups appeared on the surface. The nanoparticle with 10 times lower specific surface area (lss-SiO₂) characterized lower chemical action. In addition, a lack of hydroxyl groups on the surface obstructed apatite nucleation (reduced zeta potential in comparison to hss-SiO₂), where an apatite layer appeared already after 48 h of incubation in the simulated body fluid (SBF), and no significant changes in crystallinity of PLDLA/lss-SiO₂ nanocomposite material in comparison to neat PLDLA foil were observed. The presence and type of inorganic particles in the PLDLA matrix influenced various physicochemical properties such as the wettability, and the roughness parameter note for PLDLA/lss-SiO₂ increased. The results of biological investigation show that the bioactive nanocomposites with hss-SiO₂ may stimulate osteoblast and fibroblast cells’proliferation and secretion of collagen type I. Additionally, both nanocomposites with the nanometric silica inducted differentiation of mesenchymal cells into osteoblasts at a proliferation stage in in vitro conditions. A higher concentration of alkaline phosphatase (ALP) was observed on the material modified with hss-SiO₂ silica.

Apatite nucleation on silica surface: a zeta potential approach

Zeta potential measurements on pure silica, prepared by the sol-gel method from tetraethoxysilane under acidic conditions, are reported in different suspensions. Water suspensions and suspensions containing calcium or phosphate ions with and without NaCl were tested. zeta potential measurements were carried out as a function of the pH and ion concentration. Also, calcium and phosphate adsorption on silica was determined experimentally. The results of zeta potential and adsorption measurements suggest that both calcium and phosphate ions can be adsorbed on the silica surface; however, calcium adsorption is stronger than phosphate adsorption. When calcium and sodium ions are present in the suspension, calcium adsorption decreases. It seems that certain sites on the silica surface are specific for calcium adsorption.

Sandbed Consolidation with Mineral Precipitation

A new method has been developed to prevent sand reentrainment during oil production from unconsolidated or poorly consolidated reservoir formations. Consolidation of the zformation around the well is achieved through in situ precipitation of a sparingly soluble salt, namely, calcium phosphate. Control of the depth of salt formation is achieved by alternating injection, mixing, and reaction of two aqueous solutions of calcium chloride and potassium phosphate. Calcium phosphate crystals precipitate and grow on the grain surfaces, forming sufficiently uniform coatings. The formation of relatively uniform coatings on the grains causes an acceptably small decrease of the permeability, which is a feature of primary importance for oil production. The grains are gradually "cemented" with bridges of calcium phosphate crystallites and form a consolidated and still porous structure. As a result, the rate of hydrocarbon production for the problematic reservoir can be increased considerably without undesirable reentrainment of sand. The proposed method for consolidation has been successfully tested in sandbeds. Several series of experiments have been carried out under diverse conditions to establish the optimum parameter values for the implementation of this method. A set of optimum conditions at 25 degrees C were determined and these conditions gave satisfactory consolidation with permeability loss of ca. 60% of the initial value. The conditions of precipitation were chosen so that the precipitated phase was octacalcium phosphate [Ca(4)H(PO(4))(3).2.5H(2)O], along with its byproduct hydroxyapatite [Ca(5)(PO(4))(3)OH]. Experiments were also carried out at 70 degrees C and have shown that it is feasible to consolidate loose sandpacks at oil reservoir conditions. Copyright 2000 Academic Press.