Evaluation of the osteoconductive potential of poly(propylene carbonate)/nano-hydroxyapatite composites mimicking the osteogenic niche for bone augmentation

Nano-hydroxyapatite (n-HA) reinforced poly(propylene carbonate) (PPC) composites were prepared for bone repair and reconstruction. The effects of reinforcement on the morphology, mechanical properties and biological performance of n-HA/PPC composites were investigated. The surface morphology and mechanical properties of the composites were characterized by scanning electron microscopy (SEM) and universal material testing machine. The analytical data showed that good incorporation and dispersion of n-HA crystals could be obtained in the PPC matrix at a 30:70 weight ratio. With the increase of n-HA content, the tensile strength increased and the fracture elongation rate decreased. In vitro cell culture revealed that the composite was favorable template for cell attachment and growth. In vivo implantation in femoral condyle defects of rabbits confirmed that the n-HA/PPC composite had good biocompatibility and gradual biodegradability, exhibiting good performance in guided bone regeneration. The results demonstrates that the incorporation of n-HA crystals into PPC matrix provides a practical way to produce biodegradable and cost-competitive composites mimicking the osteogenic niche for bone augmentation.

Fabrication and characterization of a collagen coated electrospun poly(3-hydroxybutyric acid)–gelatin nanofibrous scaffold as a soft bio-mimetic material for skin tissue engineering applications

The collagen coated nanofibrous scaffold mimics the function of the extra cellular matrix with good biocompatibility, cell adhesion, cell proliferation and aids to provide as a promising tool in skin tissue engineering application.

Synthesis, characterization and biological evaluation of chromen and pyrano chromen-5-one derivatives impregnated into a novel collagen based scaffold for tissue engineering applications

The synthesis of novel chromen and pyrano chromen-5-one derivatives (CCN) has obtained in simple experimental method. The CCN and collagen based scaffold showed excellent biological properties to act as biomaterial in tissue engineering application.

Toughening of amorphous poly(propylene carbonate) by rubbery CO2-based polyurethane: transition from brittle to ductile

CO₂-based polyurethane was synthesized to toughen poly(propylene carbonate) (PPC), leading to a transition in the fracture behavior of PPC from brittle to ductile.