Synthesis, Characterization, and Electrospinning of Calcium-Containing Polyurethane Urea

Electrospun Poly(carbonate-urea-urethane)s Nonwovens with Shape-Memory Properties as a Potential Biomaterial

Poly(carbonate-urea-urethane) (PCUU)-based scaffolds exhibit various desirable properties for tissue engineering applications. This study thus aimed to investigate the suitability of PCUU as polymers for the manufacturing of nonwoven mats by electrospinning, able to closely mimic the fibrous structure of the extracellular matrix. PCUU nonwovens of fiber diameters ranging from 0.28 ± 0.07 to 0.82 ± 0.12 μm were obtained with an average surface porosity of around 50-60%. Depending on the collector type and solution concentration, a broad range of tensile strengths (in the range of 0.3-9.6 MPa), elongation at break (90-290%), and Young's modulus (5.7-26.7 MPa) at room temperature of the nonwovens could be obtained. Furthermore, samples collected on the plate collector showed a shape-memory effect with a shape-recovery ratio (Rr) of around 99% and a shape-fixity ratio (Rf) of around 96%. Biological evaluation validated the inertness, stability, and lack of cytotoxicity of PCUU nonwovens obtained on the plate collector. The ability of mesenchymal stem cells (MSCs) and endothelial cells (HUVECs) to attach, elongate, and grow on the surface of the nonwovens suggests that the manufactured nonwovens are suitable scaffolds for tissue engineering applications.

Solvent system effects on the physical and mechanical properties of electrospun Poly(ε-caprolactone) scaffolds for in vitro lung models

Mechanical properties are among the key considerations for the design and fabrication of complex tissue models and implants. In addition to the choice of material and the processing technique, the solvent system can significantly influence the mechanical properties of scaffolds. Poly(ε-caprolactone) (PCL) has been abundantly used to develop constructs, fibrous in particular, for pharmaceutical and biomedical research due to the flexibility offered by PCL-based fibrous matrices. The effect of solvent type on the morphological features of electrospun fibres has been extensively studied. Nevertheless, comprehensive studies on the impact of the solvent system on the mechanical properties of electrospun PCL fibres are lacking. This study elucidates the relationship between topographical, physical and mechanical properties of electrospun PCL fibrous meshes upon using various solvent systems. The results of the mechanical investigation highlight the significance of inter-fibre bonds on the mechanical properties of the bulk membranes and that the option of altering the solvent system composition could be considered for tuning the mechanical properties of the PCL scaffolds to serve specific biomedical application requirements. The applicability of the developed membranes as artificial ECM (Extracellular matrix) in the lung will then be investigated and compared to the commercial Polycarbonate (PC) membranes that are often used for in vitro lung models.