Synthesis and properties of a benzoxazine monomer containing maleimide and biphenyl groups

Benzoxazine resin exhibits excellent properties and is widely used in many fields. Herein, the synthesis of a novel compound, the bis(2,4-dihydro-2 H-3-(4- N-maleimido)phenyl-1,3-benzoxazinyl)biphenyl (BMIPBB), has been reported, which was synthesized by reacting N-(4-aminophenyl)maleimide (APMI), formaldehyde, and 4,4’-dihydroxybiphenyl. 1,3,5-three(4-(maleimido)phenyl)-1,3,5-triazine (TMIPT) was formed as an intermediate during the reaction. The proton nuclear magnetic resonance (1H-NMR) and Fourier transform-infrared (FTIR) spectroscopy experiments were conducted to determine the structure of BMIPBB. BMIPBB was obtained as a reddish-brown solid in 40.1% yield. The thermal properties of BMIPBB were investigated using differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA) techniques. Analysis of the DSC curves revealed that the broad peak representing the release of curing reaction heat appeared in the temperature range of 140–330°C. The peak temperature was 242.59°C and the heat of the reaction was 393.82 J/g, indicating that the rate of the curing reaction was low and the heat of the reaction was high. Analysis of the TGA results revealed that the weight loss rate was 5% at 110°C. The monomer exhibited a significant weight loss in the range of 320–500°C. The compound lost 50% of its weight at a temperature of 427°C.

Electronic effects of asymmetric and meta-alkoxy substituents on the polymerization behavior of bis-benzoxazines

Three isomers of benzoxazine monomers based on m-alkoxyphenol and 4,4′-methylenedianiline were synthesized and successfully isolated by column chromatography.