Hydrogen-Bonded CdS Nanoparticle Assemblies on Electrodes for Photoelectrochemical Applications

Reversible control over molecular recognition in surface-bound photoswitchable hydrogen-bonding receptors: towards read-write-erase molecular printboards

The synthesis of an anthracene-bearing photoactive barbituric acid receptor and its subsequent grafting onto azide-terminated alkanethiol/Au self-assembled monolayers by using an Cu(I) -catalyzed azide-alkyne reaction is reported. Monolayer characterization using contact-angle measurements, electrochemistry, and spectroscopic ellipsometry indicate that the monolayer conversion is fast and complete. Irradiation of the receptor leads to photodimerization of the anthracenes, which induces the open-to-closed gating of the receptor by blocking access to the binding site. The process is thermally reversible, and polarization-modulated IR reflection-absorption spectroscopy indicates that photochemical closure and thermal opening of the surface-bound receptors occur in 70 and 100 % conversion, respectively. Affinity of the open and closed surface-bound receptor was characterized by using force spectroscopy with a barbituric-acid-modified atomic force microscope tip.

Tunable wetting of nanoparticle-decorated polymer films

In this paper, amine-modified silica nanoparticles (NPs) with diameters (d) from 15 to 230 nm are covalently linked to poly(styrene-random-acrylic acid) (P(S-ran-AA)) films, and wettability is studied as a function of diameter and NP surface coverage. During attachment, films swell and exhibit long and short scale roughness, consisting of a ridged, honeycomb structure, approximately 1 mum wide and 45-50 nm deep, which encircles nanoscale features 10-15 nm high and approximately 50 nm apart. A maximum NP coverage of approximately 70% was achieved for d less than or nearly equal to the nanoscale roughness induced by surface swelling. For d several times greater than this nanoscale roughness, the maximum coverage was limited by interparticle repulsion and reached only approximately 30%. For NPs with diameters of 15-106 nm, the water contact angle increased from 75 degrees to 120 degrees as NP coverage increased from 0 to 70%. At low and high NP coverage, the Wenzel and Cassie models, respectively, accurately describe the data. However, at intermediate NP coverage, neither model is satisfactory. An increase in surface roughness alone cannot account for this discrepancy. Atomic force microscopy (AFM) studies show that the NPs partially embed into the swollen P(S-ran-AA) surface, suggesting that the amine-coated NPs are wet by the copolymer, exposing low surface energy styrene. These studies demonstrate that control over surface properties of coatings, such as wetting, can be achieved by selecting NP sizes that complement film roughness.

Controlled arrangement of nanoparticle arrays in block-copolymer domains

This Review describes recent results on the precise spatial distribution control of metal and semiconductor nanoparticles into domains of microphase-separated block copolymers. Specific focus is directed towards selective incorporation into a specific microphase of a block copolymer. Details on theoretical aspects concerning nanoparticle incorporation as well as practical examples are given. Furthermore, examples on applications and technological aspects of the resulting nanoparticle/polymer nanocomposites are provided.