Room‐Temperature Formation Pathway for CdTeSe Alloy Magic‐Size Clusters

A Real-Time In Situ Demonstration of Direct and Indirect Transformation Pathways in CdTe Magic-Size Clusters at Room Temperature

The transformations of colloidal semiconductor magic-size clusters (MSCs) are expected to occur with only discrete, step-wise redshifts in optical absorption. Here, we challenge this assumption presenting a novel, conceptually different transformation, for which the redshift is continuous. In the room-temperature transformation from CdTe MSC-448 to MSC-488 (designated by the peak wavelengths in nanometer), the redshift of absorption monitored in situ displays distinctly continuous and/or step-wise behavior. Based on conclusive evidence provided by real-time experiments, the former transformation is apparently direct and intra-cluster with a relatively large energy barrier. The latter transformation is indirect and assisted by MSC precursor compounds (PCs). The former transformation follows the latter often, being predominant at a relatively high temperature. The present findings encourage a reconsideration of the absorption redshift reported previously for transformations of binary II-VI MSCs, together with the pathway associated without the increase of cluster mass.

Transformation Pathways in Colloidal CdTeSe Magic-Size Clusters

A rarely studied transformation in colloidal ternary magic-size clusters (MSCs) is addressed. We report the first observation of the transformation from ternary CdTeSe MSC-399 to MSC-422, which occurs at room temperature. These two MSC types display sharp optical absorption resonances at 399 and 422 nm, respectively, and are related in that they are quasi isomers, together with their counterpart precursor compounds (PCs). Binary CdTe and CdSe samples were prepared in the prenucleation stage also called the induction period (IP). After they were mixed and placed in a mixture of toluene and octylamine, the transformation was found to take place and to be assisted by the addition of the CdSe IP sample. A binary IP sample contains corresponding binary PCs and monomers (Mo) and fragments (Fr). We argue that the transformation pathway is enabled by the corresponding ternary PCs, involving the substitution reaction, namely CdTeSe PC-399 + CdSe (Mo/Fr)-1 ⇒ CdTeSe PC-422 + CdSe (Mo/Fr)-2. The present study provides an in-depth understanding of the formation characteristics of the MSCs.

Transformation Pathway from CdSe Magic-Size Clusters with Absorption Doublets at 373/393 nm to Clusters at 434/460 nm

Divergent interpretations have appeared in the literature regarding the structural nature and evolutionary behavior for photoluminescent CdSe nanospecies with sharp doublets in optical absorption. We report a comprehensive description of the transformation pathway from one CdSe nanospecies displaying an absorption doublet at 373/393 nm to another species with a doublet at 433/460 nm. These two nanospecies are zero-dimensional (0D) magic-size clusters (MSCs) with 3D quantum confinement, and are labeled dMSC-393 and dMSC-460, respectively. Synchrotron-based small-angle X-ray scattering (SAXS) returns a radius of gyration of 0.92 nm for dMSC-393 and 1.14 nm for dMSC-460, and indicates that both types are disc shaped with the exponent of the SAXS form factor equal to 2.1. The MSCs develop from their unique counterpart precursor compounds (PCs), which are labeled PC-393 and PC-460, respectively. For the dMSC-393 to dMSC-460 transformation, the proposed PC-enabled pathway is comprised of three key steps, dMSC-393 to PC-393 (Step 1), PC-393 to PC-460 (Step 2 involving monomer addition), and PC-460 to dMSC-460 (Step 3). The present study provides a framework for understanding the PC-based evolution of MSCs and how PCs enable transformations between MSCs.