Controlled Growth of Organosilane Micropatterns on Hydrophilic and Hydrophobic Surfaces Templated by Vacuum Ultraviolet Photolithography

In this report, micropatterns of (3-aminopropyl)trimethoxysilane (APTMS) were developed on hydrophilic and hydrophobic surfaces after patterning using 172 nm vacuum ultraviolet (VUV) photolithography. Self-assembled monolayers (SAMs) formed on Si substrates through UV hydrosilylation of 1-hexadecene (HD) and 10-undecenoic acid (UDA) were used as hydrophilic and hydrophobic surfaces, respectively. For templating the HD- and UDA-SAMs, the VUV light was exposed to HD- and UDA-SAMs from the slits of photomasks in atmospheric and evacuated environments, respectively. Various oxygenated groups were generated at the exposed domains of HD-SAM, while the COOH groups were trimmed from the irradiated domains of UDA-SAM. The APTMS molecules were immobilized on the domains that were terminated by oxygenated groups after chemical vapor deposition (CVD). The thicknesses of the developed APTMS micropatterns increased significantly by raising the CVD temperature and in the presence of ambient air in the CVD Teflon container as well. The increase in thicknesses was ascribed to the formation of APTMS multilayers, which were mediated by H₃N⁺ ions. Also, the developed APTMS micropatterns on the UDA-SAM patterned by VUV light irradiation in a high-vacuum environment (HV-VUV) were thicker than those on the VUV/(O) patterned HD-SAM due to the presence of inactive oxygenated groups at the surface of VUV/(O)-terminated domains of HD-SAM such as COO-C and C-O-C groups. The presence of water or ambient air facilitated the silane coupling between the silyl groups with the oxygenated and amino groups The combination of VUV photolithography and the CVD method with control of the conditions would enable us to control the thicknesses and shapes of the developed APTMS micropatterns. These findings illustrate the applicability of VUV photolithography for templating hydrophobic and hydrophobic surfaces toward the development of organosilane architectures, which can be feasible for several applications.

Immobilizing a π-Conjugated Catecholato Framework on Surfaces of SiO2 Insulator Films via a One-Atom Anchor of a Platinum Metal Center to Modulate Organic Transistor Performance

Chemical modification of insulating material surfaces is an important methodology to improve the performance of organic field-effect transistors (OFETs). However, few redox-active self-assembled monolayers (SAMs) have been constructed on gate insulator film surfaces, in contrast to the numerous SAMs formed on many types of conducting electrodes. In this study, we report a new approach to introduce a π-conjugated organic fragment in close proximity to an insulating material surface via a transition metal center acting as a one-atom anchor. On the basis of the reported coordination chemistry of a catecholato complex of Pt(II) in solution, we demonstrate that ligand exchange can occur on an insulating material surface, affording SAMs on the SiO₂ surface derived from a newly synthesized Pt(II) complex containing a benzothienobenzothiophene (BTBT) framework in the catecholato ligand. The resultant SAMs were characterized in detail by water contact angle measurements, X-ray photoelectron spectroscopy, atomic force microscopy, and cyclic voltammetry. The SAMs served as good scaffolds of π-conjugated pillars for forming thin films of a well-known organic semiconductor C8-BTBT (2,7-dioctyl[1]benzothieno[3,2-b][1]benzothiophene), accompanied by the engagements of the C8-BTBT molecules with the SAMs containing the common BTBT framework at the first layer on SiO₂. OFETs containing the SAMs displayed improved performance in terms of hole mobility and onset voltage, presumably because of the unique interfacial structure between the organic semiconducting and inorganic insulating layers. These findings provide important insight into creating new elaborate interfaces through installing coordination chemistry in solution to solid surfaces, as well as OFET design by considering the compatibility between SAMs and organic semiconductors.

Recent advances in bioelectronics chemistry

Research in bioelectronics is highly interdisciplinary, with many new developments being based on techniques from across the physical and life sciences. Advances in our understanding of the fundamental chemistry underlying the materials used in bioelectronic applications have been a crucial component of many recent discoveries. In this review, we highlight ways in which a chemistry-oriented perspective may facilitate novel and deep insights into both the fundamental scientific understanding and the design of materials, which can in turn tune the functionality and biocompatibility of bioelectronic devices. We provide an in-depth examination of several developments in the field, organized by the chemical properties of the materials. We conclude by surveying how some of the latest major topics of chemical research may be further integrated with bioelectronics.

Ferrocene on Insulator: Silane Coupling to a SiO2 Surface and Influence on Electrical Transport at a Buried Interface with an Organic Semiconductor Layer

A silane coupling-based procedure for decoration of an insulator surface containing abundant hydroxy groups by constructing redox-active self-assembled monolayers (SAMs) is described. A newly synthesized ferrocene (Fc) derivative containing a triethoxysilyl group designated FcSi was immobilized on SiO₂/Si by a simple operation that involved immersing the substrate in a toluene solution of the Fc silane coupling reagent and then rinsing the resulting substrate. X-ray photoelectron spectroscopy (XPS) measurements confirmed that the Fc group was immobilized on SiO₂/Si in the Fe(II) state. Cyclic voltammetry measurements showed that the Fc groups were electrically insulated from the Si electrode by the SiO₂ layer. The FcSi on SiO₂/Si structures were found to serve as a good scaffold for formation of organic semiconductor thin films by vacuum thermal evaporation of C8-BTBT (2,7-dioctyl[1]benzothieno[3,2-b][1]benzothiophene), which is well-known as an organic field-effect transistor (OFET) material. The X-ray diffraction profile indicated that the conventional standing-up conformation of the C8-BTBT molecules perpendicular to the substrates was maintained in the thin films formed on FcSi@SiO₂/Si. Further vacuum thermal evaporation of Au provided an FcSi-based OFET structure with good transfer characteristics. The FcSi-based OFET showed pronounced source-drain current hysteresis between the forward and backward scans. The degree of this hysteresis was varied reversibly via gate bias manipulation, which was presumably accompanied by trapping and detrapping of hole carriers at the Fc-decorated SiO₂ surface. These findings provide new insights into application of redox-active SAMs to nonvolatile OFET memories while also creating new interfaces through junctions with functional thin films, in which the underlying redox-active SAMs play supporting roles.

Exploiting the versatile alkyne-based chemistry for expanding the applications of a stable triphenylmethyl organic radical on surfaces

The incorporation of terminal alkynes into the chemical structure of persistent organic perchlorotriphenylmethyl (PTM) radicals provides new chemical tools to expand their potential applications. In this work, this is demonstrated by the chemical functionalization of two types of substrates, hydrogenated SiO₂-free silicon (Si-H) and gold, and, by exploiting the click chemistry, scarcely used with organic radicals, to synthesise multifunctional systems. On one hand, the one-step functionalization of Si-H allows a light-triggered capacitance switch to be successfully achieved under electrochemical conditions. On the other hand, the click reaction between the alkyne-terminated PTM radical and a ferrocene azide derivative, used here as a model azide system, leads to a multistate electrochemical switch. The successful post-surface modification makes the self-assembled monolayers reported here an appealing platform to synthesise multifunctional systems grafted on surfaces.

Electrochemistry of Redox-Active Guest Molecules at β-Cyclodextrin-Functionalized Silicon Electrodes

Functionalization of silicon-based sensing devices with self-assembled receptor monolayers offers flexibility and specificity towards the requested analyte as well as the possibility of sensor reuse. As electrical sensor performance is determined by electron transfer, we functionalized H-terminated silicon substrates with β-cyclodextrin (β-CD) molecules to investigate the electronic coupling between these host monolayers and the substrate. A trivalent (one ferrocene and two adamantyl moieties), redox-active guest was bound to the β-CD surface with a coverage of about 10-11 mol/cm2 and an overall binding constant of 1.5⋅109 M-1. This packing density of the host monolayers on silicon is lower than that for similar β-CD monolayers on gold. The monolayers were comparable on low-doped p-type and highly doped p++ substrates regarding their packing density and the extent of oxide formation. Nonetheless, the electron transfer was more favorable on p++ substrates, as shown by the lower values of the peak splitting and peak widths in the cyclic voltammograms. These results show that the electron-transfer rate on the host monolayers is not only determined by the composition of the monolayer, but also by the doping level of the substrate.

Preparation, characterization, and protein-resistance of films derived from a series of α-oligo(ethylene glycol)-ω-alkenes on H–Si(111) surfaces

Films on Si(111) were prepared by photo-activated grafting of CH₂&#xe001;CH(CH₂)m(OCH₂CH₂)nOCH₃ (m = 8, 9; n = 3–7) by using different vacuum conditions. High vacuum produced a higher thickness (40 Å) and <0.8% fibrinogen adsorption (C₁₀EG₇). Films were stable even after 28 days.

Logic gates operated by bipolar photoelectrochemical water splitting

A new approach for the design of electrochemical logic gates, based on the polarization of a light-sensitive interface, is presented here.

Solid nanoarchitecture – Cu(ii) solution: dynamics of the chemical communication

The response of a porphyrin nanoarchitecture, covalently supported on quartz, was investigated upon the external chemical Cu(ii) stimulus. The overall structure behaves as a ternary optical system.

Micropatterned ferrocenyl monolayers covalently bound to hydrogen-terminated silicon surfaces: effects of pattern size on the cyclic voltammetry and capacitance characteristics

The effect of the size of patterns of micropatterned ferrocene (Fc)-functionalized, oxide-free n-type Si(111) surfaces was systematically investigated by electrochemical methods. Microcontact printing with amine-functionalized Fc derivatives was performed on a homogeneous acid fluoride-terminated alkenyl monolayer covalently bound to n-type H-terminated Si surfaces to give Fc patterns of different sizes (5 × 5, 10 × 10, and 20 × 20 μm(2)), followed by backfilling with n-butylamine. These Fc-micropatterned surfaces were characterized by static water contact angle measurements, ellipsometry, X-ray photoelectron spectroscopy (XPS), infrared reflection-absorption spectroscopy (IRRAS), atomic force microscopy (AFM), and scanning electron microscopy (SEM). The charge-transfer process between the Fc-micropatterned and underlying Si interface was subsequently studied by cyclic voltammetry and capacitance. By electrochemical studies, it is evident that the smallest electroactive ferrocenyl patterns (i.e., 5 × 5 μm(2) squares) show ideal surface electrochemistry, which is characterized by narrow, perfectly symmetric, and intense cyclic voltammetry and capacitance peaks. In this respect, strategies are briefly discussed to further improve the development of photoswitchable charge storage microcells using the produced redox-active monolayers.